The homogeneously dispersed, less agglomerated (Nd0.01Y0.99)3Al5O12 nano-sized powders were synthesized by the low temperature combustion (LCS), using Nd2O3, Y2O3, Al(NO3)3·9H2O, ammonia water and citric acid as ...The homogeneously dispersed, less agglomerated (Nd0.01Y0.99)3Al5O12 nano-sized powders were synthesized by the low temperature combustion (LCS), using Nd2O3, Y2O3, Al(NO3)3·9H2O, ammonia water and citric acid as starting materials. This method effectively solves the problems caused by solid-state reaction at high temperature and hard agglomerates brought by the chemical precipitation method. The powders were characterized by TG-DTA, XRD, FT-IR, TEM respectively and the photoluminescence (PL) spectra of (Nd0.01Y0.99)3Al5O12 green and sintered ceramic disks were measured. The results show that the forming temperature of YAG crystal phase is 850 ℃ and YAP crystal phase appearing during the calcinations transforms to pure YAG at 1050 ℃. The particle size of the powders synthesized by the LCS is in a range of 20～50 nm depending on the thermal treatment temperatures. The effectively induced cross section (σin) with the value 4.03×10-19 cm2 of (Nd0.01Y0.99)3Al5O12 ceramics is about 44% higher than that of single crystal.展开更多
Pr-CeO2 Nano-crystalline red pigments were prepared by low-temperature combustion with a later hydrothermal treatment using Ce（NO3）3·6H2O and Pr6O11 as raw materials. The phase composition, coloring mechanism a...Pr-CeO2 Nano-crystalline red pigments were prepared by low-temperature combustion with a later hydrothermal treatment using Ce（NO3）3·6H2O and Pr6O11 as raw materials. The phase composition, coloring mechanism and morphology of pigments were analyzed by XRD, SEM, EDS and XPS. Results showed that Pr-CeO2 solid solution with a fluorite structure was obtained by the diffusion of Pr^＋3 into CeO2 crystal lattice during the synthesis process. XPS analysis indicated that Pr^＋3 substitutes Ce^＋4 in CeO2 and is compensated by oxygen vacancies. Compared with low-temperature combustion synthesis, the Pr-CeO2 pigments prepared with a subsequent hydrothermal treatment have an average grain size of about 16.70 nm, and the crystallinity and red tonality are improved.展开更多
An attempt was made to extend mild combustion to forward flow furnace, such as the refinery and petrochemical tube furnace. Three dimensional numerical simulation was carried out to study the performance of this furna...An attempt was made to extend mild combustion to forward flow furnace, such as the refinery and petrochemical tube furnace. Three dimensional numerical simulation was carried out to study the performance of this furnace. The Eddy Dissipation Concept(EDC) model coupled with the reaction mechanism DRM-19 was used. The prediction showed a good agreement with the measurement. The effect of air nozzle circle(D), air nozzle diameter(d), air nozzle number(N), and air preheating temperature(Tair) on the flow, temperature and species fields, and the CO and NO emissions was investigated. The results indicate that there are four zones in the furnace, viz.: a central jet zone, an ignition zone, a combustion reaction zone, and a flue gas zone, according to the distribution profiles of H_2 CO and OH. The central jet entrains more flue gas in the furnace upstream with an increasing D while the effect of D is negligible in the downstream. The air jet momentum increases with a decreasing d or an increasing Tair, and entrains more flue gas. The effect of N is mainly identified near the burner exit. More heat is absorbed in the radiant section and less heat is discharged to the atmosphere with a decreasing d and an increasing N as evidenced by the flue gas temperature. The CO and NO emissions are less than 50 μL/L and 10 μL/L, respectively, in most of conditions.展开更多
YAG:Ce3+ phosphor was prepared by sol-gel low-temperature combustion method. The effects of the precursor properties and calcining temperature on the crystallization process, microscopic morphology and luminescent pro...YAG:Ce3+ phosphor was prepared by sol-gel low-temperature combustion method. The effects of the precursor properties and calcining temperature on the crystallization process, microscopic morphology and luminescent properties of phosphor were studied. The results indicate that the pure phase of YAG can be obtained at 800 ℃ by sol-gel low temperature combustion method, using citric acid as complexing agent. When the molar ratio of metal ion to citric acid is 2.0 and pH value is 2, the crystallinity increases and the phosphor particle size grows up gradually with the increase of the calcining temperature. The powders were characterized through thermal analysis, X-ray diffraction analysis and scanning electron microscope analysis. The excitation spectra of YAG:Ce3+ phosphor take on a double peak structure, and the peak value of the main excitation spectra occurs at 460 nm and that of the emission spectra is near 530 nm. With the gradual increase of the calcining temperature, the peak position of excitation and emission spectra remains basically unchanged, but its relative intensity increases gradually.展开更多
Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manom...Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manometer α Al2 O3 synthesisby LCSwas done, α Al2 O3 withtheparticlesize50 ～80 NM wasgot under properconditions.展开更多
The effects of various combustion conditions (i. e. particle size of coals, oxygen concentration in combustion gas and coal content in the fuel bed, etc.), on reducing conversion of NO_x during coal combustion were st...The effects of various combustion conditions (i. e. particle size of coals, oxygen concentration in combustion gas and coal content in the fuel bed, etc.), on reducing conversion of NO_x during coal combustion were studied. Under the present combustion conditions, coals with smaller particle size gave the lower conversion of NO_x, and as expected that an decrease in overall stoichiometric ratio, whether by an decrease in O_2 content in combustion gas or by an increase in coal content in fuel bed would lead to a lower conversion of NO_x. In order to investigate the effect of metallic oxide layers on restraining NO_x formation, the combustion experiments for coal granules with adhering layer of various metallic oxides including Fe_2O_3, Ni_2O_3 and mixed oxides Fe-Ni-O_x were conducted in a packed bed combustor. The combustion experiments have shown that most of adhering materials gave considerable effect on reduction of NO_x emission during coal combustion.展开更多
The formation characteristics of NO_x during combustion of four typical Chinese coals have been studied in a packed bed combustor. The studies included the effects of chemical composition of coals and volatile matters...The formation characteristics of NO_x during combustion of four typical Chinese coals have been studied in a packed bed combustor. The studies included the effects of chemical composition of coals and volatile matters, and combustion conditions, i.e. preheating temperatures of combustion gas, on conversion of NO_x during combustion. In term of the combustion experiments, there is a close relation between coal composition and conversions of NO_x. Coals with a higher nitrogen content give a lower F_(NO_x)~0, and coals with a higher volatile content give a lower F_(NO_x)~0. The further devolatilization experiments showed that volatile matters in the coal have an important effect on reducing conversion of coal-nitrogen to NO_x. It was interpreted as that the release of volatile matters during combustion caused a fuel-rich circumstance in the vicinity of coal particles which may restrain the formation of NO_x. Preheating temperatures of combustion gas has significant effects on conversions of NO_x and there exist a critical preheating temperature. At such temperature, lower F_(NO_x)~0 can be reached.展开更多
This paper reports a field testing of full scale PCC (Pulverized Coal Combustion) boiler study into the influence of constricted air distribution on NO x emissions at unit 3 (125 MW power units, 420 t/h boiler) of Gui...This paper reports a field testing of full scale PCC (Pulverized Coal Combustion) boiler study into the influence of constricted air distribution on NO x emissions at unit 3 (125 MW power units, 420 t/h boiler) of Guixi power station, Jiangxi and puts forward the methods to decrease NO x emissions and the principle of boiler operation and regulation through analyzing NO x emissions state under real running condition. Based on boiler constricted air distribution, the experiment mainly tested the influence of primary air, excessive air, boiler load and milling sets (tertiary air) on NO x emissions and found its influence characteristics. A degraded bituminous coal is simply adopted to avoid the test results from other factors.展开更多
This article did a research about exhaust gas constituent inside the catalytic combustion furnace with Pd-based honeycomb monoliths of lean natural gas-air mixtures and discussed the feature of the exhaust gas. In add...This article did a research about exhaust gas constituent inside the catalytic combustion furnace with Pd-based honeycomb monoliths of lean natural gas-air mixtures and discussed the feature of the exhaust gas. In addition, the near-zero pollutant emissions of catalytic combustion burner was proved by a test report provided by NIM. From a low-carbon prospective, the application prospect of catalytic combustion furnace was展开更多
为了认识稠油开发过程中低温氧化与高温氧化阶段原油变化规律,利用静态氧化釜开展稠油的高低温氧化实验,借助傅里叶变换离子回旋共振质谱分析技术对高低温氧化前后的原油分子量及O、N、S杂原子化合物特征开展研究,结果表明:原油低温氧...为了认识稠油开发过程中低温氧化与高温氧化阶段原油变化规律,利用静态氧化釜开展稠油的高低温氧化实验,借助傅里叶变换离子回旋共振质谱分析技术对高低温氧化前后的原油分子量及O、N、S杂原子化合物特征开展研究,结果表明:原油低温氧化阶段分子量分布特征与原样相似,相对分子量分布范围在200~750,整体呈平缓状单峰型分布,高温氧化阶段分子量分布范围前移,呈明显的前峰单峰型分布;杂原子化合物中的O元素在低温氧化阶段主要以无环的饱和二元酸形式存在,在高温氧化阶段受环化、芳构化及脱甲基作用的影响,伴随着侧链烷基及杂原子基团的断裂和芳构化过程,造成原油中杂原子化合物向着碳数更小、双键当量(double bond equivalents,DBE)值更低的方向演化。该研究探索了温度与原油结构及化学组成之间的关系,对于指导稠油开发现场具有重要意义。展开更多
文摘The homogeneously dispersed, less agglomerated (Nd0.01Y0.99)3Al5O12 nano-sized powders were synthesized by the low temperature combustion (LCS), using Nd2O3, Y2O3, Al(NO3)3·9H2O, ammonia water and citric acid as starting materials. This method effectively solves the problems caused by solid-state reaction at high temperature and hard agglomerates brought by the chemical precipitation method. The powders were characterized by TG-DTA, XRD, FT-IR, TEM respectively and the photoluminescence (PL) spectra of (Nd0.01Y0.99)3Al5O12 green and sintered ceramic disks were measured. The results show that the forming temperature of YAG crystal phase is 850 ℃ and YAP crystal phase appearing during the calcinations transforms to pure YAG at 1050 ℃. The particle size of the powders synthesized by the LCS is in a range of 20～50 nm depending on the thermal treatment temperatures. The effectively induced cross section (σin) with the value 4.03×10-19 cm2 of (Nd0.01Y0.99)3Al5O12 ceramics is about 44% higher than that of single crystal.
基金This work was supported by the Scientific Research Foundation of Shaanxi University of Science and Technology (No. SUST-B06)
文摘Pr-CeO2 Nano-crystalline red pigments were prepared by low-temperature combustion with a later hydrothermal treatment using Ce（NO3）3·6H2O and Pr6O11 as raw materials. The phase composition, coloring mechanism and morphology of pigments were analyzed by XRD, SEM, EDS and XPS. Results showed that Pr-CeO2 solid solution with a fluorite structure was obtained by the diffusion of Pr^＋3 into CeO2 crystal lattice during the synthesis process. XPS analysis indicated that Pr^＋3 substitutes Ce^＋4 in CeO2 and is compensated by oxygen vacancies. Compared with low-temperature combustion synthesis, the Pr-CeO2 pigments prepared with a subsequent hydrothermal treatment have an average grain size of about 16.70 nm, and the crystallinity and red tonality are improved.
基金supported by the technology development fund of China Petroleum & Chemical Corporation (Sinopec 312016 and 314054)
文摘An attempt was made to extend mild combustion to forward flow furnace, such as the refinery and petrochemical tube furnace. Three dimensional numerical simulation was carried out to study the performance of this furnace. The Eddy Dissipation Concept(EDC) model coupled with the reaction mechanism DRM-19 was used. The prediction showed a good agreement with the measurement. The effect of air nozzle circle(D), air nozzle diameter(d), air nozzle number(N), and air preheating temperature(Tair) on the flow, temperature and species fields, and the CO and NO emissions was investigated. The results indicate that there are four zones in the furnace, viz.: a central jet zone, an ignition zone, a combustion reaction zone, and a flue gas zone, according to the distribution profiles of H_2 CO and OH. The central jet entrains more flue gas in the furnace upstream with an increasing D while the effect of D is negligible in the downstream. The air jet momentum increases with a decreasing d or an increasing Tair, and entrains more flue gas. The effect of N is mainly identified near the burner exit. More heat is absorbed in the radiant section and less heat is discharged to the atmosphere with a decreasing d and an increasing N as evidenced by the flue gas temperature. The CO and NO emissions are less than 50 μL/L and 10 μL/L, respectively, in most of conditions.
文摘YAG:Ce3+ phosphor was prepared by sol-gel low-temperature combustion method. The effects of the precursor properties and calcining temperature on the crystallization process, microscopic morphology and luminescent properties of phosphor were studied. The results indicate that the pure phase of YAG can be obtained at 800 ℃ by sol-gel low temperature combustion method, using citric acid as complexing agent. When the molar ratio of metal ion to citric acid is 2.0 and pH value is 2, the crystallinity increases and the phosphor particle size grows up gradually with the increase of the calcining temperature. The powders were characterized through thermal analysis, X-ray diffraction analysis and scanning electron microscope analysis. The excitation spectra of YAG:Ce3+ phosphor take on a double peak structure, and the peak value of the main excitation spectra occurs at 460 nm and that of the emission spectra is near 530 nm. With the gradual increase of the calcining temperature, the peak position of excitation and emission spectra remains basically unchanged, but its relative intensity increases gradually.
文摘Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manometer α Al2 O3 synthesisby LCSwas done, α Al2 O3 withtheparticlesize50 ～80 NM wasgot under properconditions.
文摘The effects of various combustion conditions (i. e. particle size of coals, oxygen concentration in combustion gas and coal content in the fuel bed, etc.), on reducing conversion of NO_x during coal combustion were studied. Under the present combustion conditions, coals with smaller particle size gave the lower conversion of NO_x, and as expected that an decrease in overall stoichiometric ratio, whether by an decrease in O_2 content in combustion gas or by an increase in coal content in fuel bed would lead to a lower conversion of NO_x. In order to investigate the effect of metallic oxide layers on restraining NO_x formation, the combustion experiments for coal granules with adhering layer of various metallic oxides including Fe_2O_3, Ni_2O_3 and mixed oxides Fe-Ni-O_x were conducted in a packed bed combustor. The combustion experiments have shown that most of adhering materials gave considerable effect on reduction of NO_x emission during coal combustion.
文摘The formation characteristics of NO_x during combustion of four typical Chinese coals have been studied in a packed bed combustor. The studies included the effects of chemical composition of coals and volatile matters, and combustion conditions, i.e. preheating temperatures of combustion gas, on conversion of NO_x during combustion. In term of the combustion experiments, there is a close relation between coal composition and conversions of NO_x. Coals with a higher nitrogen content give a lower F_(NO_x)~0, and coals with a higher volatile content give a lower F_(NO_x)~0. The further devolatilization experiments showed that volatile matters in the coal have an important effect on reducing conversion of coal-nitrogen to NO_x. It was interpreted as that the release of volatile matters during combustion caused a fuel-rich circumstance in the vicinity of coal particles which may restrain the formation of NO_x. Preheating temperatures of combustion gas has significant effects on conversions of NO_x and there exist a critical preheating temperature. At such temperature, lower F_(NO_x)~0 can be reached.
文摘This paper reports a field testing of full scale PCC (Pulverized Coal Combustion) boiler study into the influence of constricted air distribution on NO x emissions at unit 3 (125 MW power units, 420 t/h boiler) of Guixi power station, Jiangxi and puts forward the methods to decrease NO x emissions and the principle of boiler operation and regulation through analyzing NO x emissions state under real running condition. Based on boiler constricted air distribution, the experiment mainly tested the influence of primary air, excessive air, boiler load and milling sets (tertiary air) on NO x emissions and found its influence characteristics. A degraded bituminous coal is simply adopted to avoid the test results from other factors.
文摘This article did a research about exhaust gas constituent inside the catalytic combustion furnace with Pd-based honeycomb monoliths of lean natural gas-air mixtures and discussed the feature of the exhaust gas. In addition, the near-zero pollutant emissions of catalytic combustion burner was proved by a test report provided by NIM. From a low-carbon prospective, the application prospect of catalytic combustion furnace was
文摘为了认识稠油开发过程中低温氧化与高温氧化阶段原油变化规律,利用静态氧化釜开展稠油的高低温氧化实验,借助傅里叶变换离子回旋共振质谱分析技术对高低温氧化前后的原油分子量及O、N、S杂原子化合物特征开展研究,结果表明:原油低温氧化阶段分子量分布特征与原样相似,相对分子量分布范围在200~750,整体呈平缓状单峰型分布,高温氧化阶段分子量分布范围前移,呈明显的前峰单峰型分布;杂原子化合物中的O元素在低温氧化阶段主要以无环的饱和二元酸形式存在,在高温氧化阶段受环化、芳构化及脱甲基作用的影响,伴随着侧链烷基及杂原子基团的断裂和芳构化过程,造成原油中杂原子化合物向着碳数更小、双键当量(double bond equivalents,DBE)值更低的方向演化。该研究探索了温度与原油结构及化学组成之间的关系,对于指导稠油开发现场具有重要意义。