Friction and wear behavior and mechanism of low carbon microalloyed steel containing Nb

Dry sliding friction and wear test of Nb containing low carbon microalloyed steel was carried out at room temperature,and the effect of Nb on the wear behavior of the steel,as welll as the mechanism was studied.Scanning electron microscopy(SEM) and energy dispersive spectrometry(EDS) were employed to analyze the morphology and composition of the worn surface,and the structure evolution of the plastic deformation layer.The carbide content and type in the steel were analyzed by the electrolytic extraction device and X-ray diffraction(XRD).The experimental results demonstrate that the addition of 0.2% Nb can refine the grain and generate Nb C to improve the wear resistance of the steel.By enhancing the load and speed of wear experiment,the wear mechanism of the test steel with 0.2% Nb changes from slight oxidation wear to severe adhesion wear and oxidation wear.Compared with the load,the increase in the rotation speed exerts a greater influence on the wear of the test steel.

Oxide and Sulfide Dispersive Precipitation and Effects on Microstructure and Properties of Low Carbon Steels

Electron microscopic investigation on low carbon steel strips produced by the CSP process has been carried out. Large number of oxide dispersive precipitates have been observed in the ferrite matrix of the steel strips. Dimension of them is about 10~20 nm. Electron diffraction study showed that the structure of these precipitates consists with cubic system spinel structure. Their lattice parameter is about 0.83 nm. The results implied that they should be complex oxides of Fe, Al et al. Small sulfide particles with 100-300 nm in size have also been observed. Remarkable strengthening and grain refinement effects can be obtained by the precipitations. The oxygen and sulfur in steels could play beneficial role under certain conditions.

Cleanliness of Ti-bearing Al-killed ultra-low-carbon steel during different heating processes

During the production of Ti-bearing Al-killed ultra-low-carbon(ULC) steel, two different heating processes were used when the converter tapping temperature or the molten steel temperature in the Ruhrstahl–Heraeus(RH) process was low: heating by Al addition during the RH decarburization process and final deoxidation at the end of the RH decarburization process(process-Ⅰ), and increasing the oxygen content at the end of RH decarburization, heating and final deoxidation by one-time Al addition(process-Ⅱ). Temperature increases of 10°C by different processes were studied; the results showed that the two heating processes could achieve the same heating effect. The T.[O] content in the slab and the refining process was better controlled by process-Ⅰ than by process-Ⅱ. Statistical analysis of inclusions showed that the numbers of inclusions in the slab obtained by process-Ⅰ were substantially less than those in the slab obtained by process-Ⅱ. For process-Ⅰ, the Al_2O_3 inclusions produced by Al added to induce heating were substantially removed at the end of decarburization. The amounts of inclusions were substantially greater for process-Ⅱ than for process-Ⅰ at different refining stages because of the higher dissolved oxygen concentration in process-Ⅱ. Industrial test results showed that process-Ⅰ was more beneficial for improving the cleanliness of molten steel.

Bainite Transformation Under Continuous Cooling of Nb-Microalloyed Low Carbon Steel

Utilizing Gleeble-1500 thermomechanical simulator, the influences of hot deformation parameters on continuous cooling bainite transformation in Nb-microalloyed low carbon steel were investigated. The results indicate that bainite starting temperature decreases with raising cooling rate and increases with increasing deformation temperature. Deformation has an accelerative effect on the bainite transformation when the specimens are deformed at 950 ℃. When the deformation temperature increases, the effect of deformation on bainite starting temperature is weakened. The amount of bainite is influenced by strain, cooling rate, and deformation temperature. When the specimens are deformed below 900 ℃, equiaxed ferrites are promoted and the bainite transformation is suppressed.

Solidification Structure of Low Carbon Steel Strips with Different Phosphorus Contents Produced by Strip Casting

In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail. It was found that the strips possessed a fine microstructure compared with the mould cast steels. With increasing phosphorus content more ferrite has been formed with finer grains.

Analysis of the formation conditions and characteristics of interphase and random vanadium precipitation in a low-carbon steel during isothermal heat treatment

The characteristics of nanosized precipitates in steels depend on the heat-treatment parameters. The effects of characteristics of vanadium precipitates formed during isothermal heat treatment on the hardness of the ferrite matrix in low-carbon vanadium-alloyed steel were investigated through analysis of transmission electron microscopy images and microhardness measurements. The results show that, during isothermal holding in the temperature range from 675 to 750℃, only interphase precipitation occurs, whereas only random precipitation occurs in the ferrite matrix during holding at 600℃. Furthermore, during isothermal heat treatment between 600 and 675℃, both random and interphase precipitates occurred in the ferrite. Nanoscale vanadium carbides with different atomic ratios of vanadium(V) and carbon(C) were the dominant precipitates in the random and interphase precipitates. The sizes of random precipitation carbides were smaller than those of interphase ones. Also, the sample isothermally heat treated at 650℃ for 900s exhibited a higher hardness with a narrower hardness distribution.

Decarburization rate of RH refining for ultra low carbon steel

The decarburization behaviors of ultra low carbon steel in a 210-t RH vacuum degasser were investigated under practical operat- ing conditions. According to the apparent decarburization rate constant （Kc） calculated by the carbon content in the samples taken from the hot melt in a ladle at an interval of 1-2 min, it is observed that the total decarburization reaction period in RH can be divided into the quick decarburization period and the stagnant decarburization period, which is quite different from the traditional one with three stages. In this study, the average apparent decarburization rate constant during the quick decarburization period is 0.306 min^-1, and that of the stagnant period is 0.072 min^-1. Increasing the initial carbon content and enhancing the exhausting capacity can increase the apparent decarburization rate constant in the quick decarburization period. The decarburization reaction comes into the stagnant decarburization period when the carbon content in molten steel is less than 14× 10^-6 after 10 min of decarburization.

Kinetics of bainite-to-austenite transformation during continuous reheating in low carbon microalloyed steel

A dilatometer was used to study the kinetics of bainite-to-austenite transformation in low carbon microalloyed steel with the initial microstructure of bainite during the continuous reheating process. The bainite-to-austenite trans- formation was observed to take place in two steps at low heating rate. The first step is the dissolution of bainite, and the second one is the remaining bainite-to-austenite transformation controlled by a dissolution process. The calculation result of the kinetics of austenite formation shows that the two steps occur by diffusion at low heating rate. However, at high heating rate the bainite-to-austenite transformation occurs in a single step, and the process is mainly dominated by shear. The growth rate of austenite reaches the maximum at about 835℃ at different heating rates and the growth rate of austenite as a function of temperature increases with the increase in heating rate.

Experimental study on Ti+Nb bearing ultra-low carbon bake hardening sheet steel hot-rolled in the ferrite region

A Ti＋Nb bearing ultra-low carbon bake hardening sheet steel hot-rolled in the conventional austenite region and in the ferrite region with lubrication was experimentally studied. Subsequent cold rolling and continuous annealing processes were also conducted. The results show that microstructures of ultra-low carbon bake hardening hot strips at room temperature are basically irregular polygonal ferrites. The yield strength, ultimate tensile strength, n value, and r value of the No.2 specimen hot-rolled in the ferrite region with lubrication are 243 MPa, 364 MPa, 0.29, and 1.74, respectively, which are similar to those of the No.1 specimen hot-roiled in the conventional austenite region. The elongation rate and bake hardening value of No.2 specimen are 51% and 49.4 MPa, respectively, which are greater than those of No. 1 specimen. The No.2 specimen hot-rolled in the ferrite region with lubrication exhibits good mechanical properties and relatively excellent baking hardening performance. Therefore, the hot rolling experiment of Ti＋Nb bearing ultra-low carbon bake hardening steel in the ferrite region with lubrication is feasible and can be considered in the future industrial trial production.

Effects of Deformation on Bainite Transformation During Continuous Cooling of Low Carbon Steels

Hot deformation experiments were carried out on Gleeble 1500 thermo-mechanical simulator. The bainite transformation after deformation was investigated by optical microstructure analysis. The results indicated that the deformation accelerated the bainite transformation when the deformation was carried out at high temperature and no or little ferrite was precipitated before bainite transformation; when the deformation was carried out at low temperature, the deformation hindered the bainite transformation because a lot of ferrite precipitated before bainite transformation.

Aspects of microstructure in low carbon steels produced by the CSP process

The solidification structure, microstructure evolution during rolling andprecipitates with nanometers in dimension of the low carbon steels produced by CSP process with thinslabs have been studied in recent years. Important differences in microstructure and mechanicalproperties between the CSP products and the conventional one were observed. These differences mayarise from the much rapider solidification rate and cooling rate after casting of the thin slabs.Some aspects of the microstructure for the low carbon steels of the CSP thin slabs are summarizedand compared with the conventional one.

INFLUENCE OF HOT DEFORMATION ON CONTINUOUSCOOLING BAINITIC TRANSFORMATION IN A LOWCARBON STEEL

The influence of hot deformation conditions on continuous cooling bainitic transformation has been investigated for a low carbon microalloyed steel. The CCT diagrams show that deformation in unrecrpstallized austcnite ation can accelerate transformation process. Bainitic transformation in intermediate transformation temperature region is prominent, and the proeutectoid polygonal ferrite transformation at evelated high temperature is suppressed. According to optical and TEM analyses, low carbon bainitic ferrite is characterized by granular and lathlike ferrite, based on the cooling rate and deformation conditions. For nondeformation, groaps of coarse parallel ferrite lath form from the prior austenite grain boundaries with the same crystallographic orientation. For heavy deformaton, cell structure within the austenite grains due to the high dislocation density formed, which provides more nucleation sites for bainite ferrite. So deformation can discontinue the growth of ferrite laths and decrease the length of ferrite laths.

DEFORMATION ENHANCED FERRITE TRANSFORMATION IN PLAIN LOW CARBON STEEL

The microstructure evolution during deformation enhanced transformation of undercooled austenite of a plain low carbon steel has been investigated by means of hot compression simulation experiment under various conditions of strain rate, deformation temperature and strain. The effect of austenite grain size on the strain enhanced ferrite transformation has been studied. The ferrite dynamic recrystallization involved in successive hot deformation has been explored.

Austenite Recrystallization and Controlled Rolling of Low Carbon Steels

The dynamic recrystallization and static recrystallization in a low carbon steel were investigated through single-pass and double-pass experiments. The results indicate that as the deformation temperature increases and the strain rate decreases, the shape of the stress-strain curve is changed from dynamic recovery shape to dynamic recrystallization shape. The austenite could not recrystallize within a few seconds after deformation at temperature below 900 ℃. According to the change in microstructure during deformation, the controlled rolling of low carbon steel can be divided into four stages： dynamic recrystallization, dynamic recovery, strain-induced ferrite transformation, and rolling in two-phase region. According to the microstructure after deformation, the controlled rolling of low carbon steel can be divided into five regions： non-recrystallized austenite, partly-recrystallized austenite, fully-recrystallized austenite, austenite to ferrite transformation, and dual phase.

Effect of tempering temperature on the mechanical properties and microstructure of an copper-bearing low carbon bainitic steel

The effect of tempering temperature on the microstructure and mechanical properties of ultra-high strength, copperbearing, low-carbon bainitic steel has been investigated in the experiment. The results showed that the microstructure was mainly the laths of bainite in the as-quenched steel. The bainitic laths were restored and combined after the steel tempered at various tempera- tures. There were rnartensite/austenite （M/A） islands and numerous dislocations within and between the bainitic laths, while very t-me precipitates of ε-Cu were also observed within the laths. With increasing the tempered temperature from 400 to 600℃, the yield strength （YS） increased from 877 to 957 MPa, whereas the ultimate tensile strength （UTS） decreased from 1020 to 985 MPa. The Charpy V-notch （CVN） varied from 68.5 to 42 J, and the value was minimal for the steel tempered at 500℃. 2008 University of Science and Technology Beijing. All rights reserved.

A method to study interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel

A novel diffusion couple method was used to investigate the interface diffusion of arsenic into a Nb-Ti microalloyed low carbon steel and its effects on phase transformation at the interface. It is discovered that the content of arsenic has great effect on grain growth and phase transformation at high temperature. When the arsenic content is no more than lwt%, there is no obvious grain growth and no obvious ferrite transitional region formed at the diffusion interface. However, when the arsenic content is no less than 5wt%, the grain grows very rapidly. In addition, the arsenic-enriched ferrite transitional layer forms at the diffusion interface in the hot-rolling process, which results from a slower diffusion rate of arsenic atoms than that of carbon in ferrite.

Controlled Rolling and Cooling Process for Low Carbon Cold Forging Steel

Effect of controlled rolling and cooling process on the mechanical properties of low carbon cold forging steel was investigated for different processing parameters of a laboratory hot rolling mill. The results show that the specimens with fast cooling after hot rolling exhibit very good mechanical properties, and the improvement of the mechanical properties can be attributed mainly to the ferrite-grain refinement. The mechanical properties increase with decreasing final cooling temperature within the range from 670 ℃ to 570 ℃ due to the finer interlamellar spacing of pearlite colony. The specimen with fast cooling after low temperature rolling shows the highest values of the mechanical properties. The effect of the ferrite grain size on the mechanical properties was greater than that of pearlite morphology in the present study. The mechanical properties of specimens by controlled rolling and cooling process without thermal treatment were greatly superior to that of the same specimens by the conventional rolling, and their tensile strength reached 490 MPa grade even in the case of low temperature rolling without controlled rolling. It might be expected to realize the substitution medium-carbon by low-carbon for 490 MPa grade cold forging steel with controlled rolling and cooling process.

Surface Ferrite Grain Refinement and Mechanical Properties of Low Carbon Steel Plates

Considering the specialities of the steel plate production, the TMCP study has been carried out with Gleeble 2000 tester to explore the possibility of fine grained ferrite in the low carbon steel plates with the chemical composition of C 0.13--0.18, Si 0.12-0.18, Mn 0.50-0. 65, P 0. 010-0. 025, and S 0. 005-0. 028. The plates with thickness of 8. 7 mm in which the ferrite grain size is smaller than 8μm have been produced by special de- formation process in the laboratory. Furthermore, the trial production of special plain carbon steel plates of 16-25 mm in thickness and 2 000- 2 800 mm in width with fine grained ferrite has been successfully carried out in the Shougang Steel Plate Rolling Plant. The ferrite grain size is 5.5-7μm in the surface layers and 9.5-15μm in the central layer respectively. The yield strength is 320- 360 MPa, tensile strength is 440-520 MPa and the elongation is 25%- 34 %. It is very important for the rolling plants to improve the low carbon steel plates＇ mechanical properties. The results show that the ferrite grains in the surface layer can be refined effectively by the appropriate rolling process, and the strength can be also increased.