Interaction of Hydrogen and Retained Austenite in Bainite/Martensite Dual-Phase High Strength Steel

The hydrogen trapping phenomena in two bainite/martensite dual-phase high strength steels(U20Si and U20DSi)were investigated by electrochemical permeation technique.The hydrogen diffusivity was calculated from data of permeation delay time,and the diffusion coefficient in U20 Si is far less than that in U20 DSi.Moreover,the hydrogen diffusivity decreases as the volume percent of retained austenite increases.The experiment results show that there are different hydrogen trappings and different volume percents of retained austenite in U20 Si and U20 DSi.The retained austenite is precipitated as films.The trap binding energy for the retained austenite and hydrogen is calculated to be 40.4kJ·mol-1.

Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite （CFB/M） complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of ＂soft structure＂. It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.

Effect of zirconium addition on the austenite grain coarsening behavior and mechanical properties of 900 MPa low carbon bainite steel

The ultra-fine bainitic microstructure of a 900 MPa low carbon bainitic Cu-Ni-Mo-B steel was obtained by a newly developed relaxation precipitation control （RPC） phase transformation processing. In a pan-cake like prior-austenite grain, the micro- structure consisted of lath bainite, a little of abnormal granular bainite, and acicular ferrite. The effect of zirconium carbonitrides on the austenite grain coarsening behavior was studied by transmission electron microscopy （TEM）. The results show that, the lath is narrower with increasing cooling rate. The ratio of all kinds of bainitic microstructure is proper with the intermediate cooling rate; and Zr-containing precipitates distribute uniformly, which restrains austenite grain growing in heat-affected welding zone.

EFFECT OF MICROSTRUCTURE ON CORROSION FATIGUE BEHAVIOUR OF A LOW CARBON BAINITE STEEL

The behaviour towards corrosion fatigue of low carbon bainite steel with various microstructures after tempered at different temperatures has been examined. The susceptibility of the steel to corrosion fatigue may be improved by tempering at 300℃.

Complex Precipitation Mechanism of Ti-Nb-V Microalloyed Bainitic Base High Strength Steel

The addition of high Ti（>0.1%） in microalloyed bainitic high strength steel was designed, and the precipitation morphology of steels with different Ti, Nb, and V contents was studied by utilizing transmission electron microscopy（TEM）. Based on the classical nucleation-crystal growth theory and the Johnson-Mehl-Avrami equation, the precipitation thermodynamic and kinetic model of second phase particles in austenite was established in the form of（Nbx,Vy,Tiz）C, and the complex precipitation mechanism of second phase particles was emphatically studied. The experimental results show that the complex precipitation particles could be divided into two categories: the coarser particles with about 100 nm grain size and the independent complex precipitation particles in the form of（Nb,V,Ti）C with 35-50 nm grain size. The latter has a better precipitation strengthening effect, and the calculated PTT curve shows a typical "C" shape. When the deformed storage energy is 3 820 J?mol-1, the fastest precipitation temperature of calculated PTT curve is 925 °C, and the calculated result is essentially consistent with experimental values. The increase of Ti content increased the nose point temperature and expanded the range of fastest precipitation temperature.

The welding application of high strength steels used in engineering machinery

With the rapid development of low alloy steel strength level,more problems caused by welding are exposed day by day.Recently,the efforts have been paid to improve or enchance the low toughness of heated affected zone and welded metal which can enchance the comprehensive mechanical properties that is the core scientific problems of its safe operation by researching crack initiation and crack propragation attracted a rapidly growing interest.This article focuses on the research status and progress of welding technology and joint microstructure and properties of advanced steel materials.The influence of shielding gas on the microstructure evolution of deposited metals,the effect heat input of welded joint performance,interpass temperature and alloy elements on welded joints microstructure and M-A constituent evolution and properties are reviewed in detail.And for the heat affected zone,the grain size and microstructure as well as the shape,size,and distribution of M-A constituent,have a significant impact on the impact toughness.This paper is an attempt to review the effect of different welding process parameters on welded metal and HAZ of HSLA steels.

Effect of Fast Cooling Rate on the Microstructure and Mechanical Properties of Low-Carbon High-Strength Steel Annealed in the Intercritical Region

The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator and a continuous annealing thermomeehanical simulator. The results showed that the microstructure consisted of ferrite and bainite as the main phases with a small amount of retained austenite and martensite islands at cooling rate of 5 and 50 ℃/s, respectively. Fast cooling after continuous annealing affected all constituents of the microstructure. The mechanical properties were improved considerably. Ultimate tensile strength （U-TS） increased and total elongation （TEL） decreased with increasing cooling rate in all specimens. The specimen 1 at a cooling rate of 5 ℃/s exhibited the maximum TEL and UTSxTEL （20% and 27 200 MPa%, respectively） because of the competition between weakening by presence of the retained austenite plus the carbon indigence by carbide precipitation, and strengthening by martensitic islands and precipitation. The maximum UTS and YS （1 450 and 951 MPa, respectively） were obtained for specimen 2 at a cooling rate of 50 ℃/s. This is attributed to the effect of dispersion strengthening of finer martensite islands and the effect of precipitation strengthening of carbide precipitates.

Bainite Transformation Under Continuous Cooling of Nb-Microalloyed Low Carbon Steel

Utilizing Gleeble-1500 thermomechanical simulator, the influences of hot deformation parameters on continuous cooling bainite transformation in Nb-microalloyed low carbon steel were investigated. The results indicate that bainite starting temperature decreases with raising cooling rate and increases with increasing deformation temperature. Deformation has an accelerative effect on the bainite transformation when the specimens are deformed at 950 ℃. When the deformation temperature increases, the effect of deformation on bainite starting temperature is weakened. The amount of bainite is influenced by strain, cooling rate, and deformation temperature. When the specimens are deformed below 900 ℃, equiaxed ferrites are promoted and the bainite transformation is suppressed.

Effect of microstructure on the low temperature toughness of high strength pipeline steels

Microstructure observations and drop-weight tear test were performed to study the microstructures and mechanical properties of two kinds of industrial X70 and two kinds of industrial X80 grade pipeline steels. The effective grain size and the fraction of high angle grain boundaries in the pipeline steels were investigated by electron backscatter diffraction analysis. It is found that the low temperature toughness of the pipeline steels depends not only on the effective grain size, but also on other microstructural factors such as martensite-austenite （MA） constituents and precipitates. The morphology and size of MA constituents significantly affect the mechanical properties of the pipeline steels. Nubby MA constituents with large size have significant negative effects on the toughness, while smaller granular MA constituents have less harmful effects. Similarly, larger Ti-rich nitrides with sharp corners have a strongly negative effect on the toughness, while fine, spherical Nb-rich carbides have a less deleterious effect. The low temperature toughness of the steels is independent of the fraction of high angle grain boundaries.

Kinetics of bainite-to-austenite transformation during continuous reheating in low carbon microalloyed steel

A dilatometer was used to study the kinetics of bainite-to-austenite transformation in low carbon microalloyed steel with the initial microstructure of bainite during the continuous reheating process. The bainite-to-austenite trans- formation was observed to take place in two steps at low heating rate. The first step is the dissolution of bainite, and the second one is the remaining bainite-to-austenite transformation controlled by a dissolution process. The calculation result of the kinetics of austenite formation shows that the two steps occur by diffusion at low heating rate. However, at high heating rate the bainite-to-austenite transformation occurs in a single step, and the process is mainly dominated by shear. The growth rate of austenite reaches the maximum at about 835℃ at different heating rates and the growth rate of austenite as a function of temperature increases with the increase in heating rate.

Effects of Deformation on Bainite Transformation During Continuous Cooling of Low Carbon Steels

Hot deformation experiments were carried out on Gleeble 1500 thermo-mechanical simulator. The bainite transformation after deformation was investigated by optical microstructure analysis. The results indicated that the deformation accelerated the bainite transformation when the deformation was carried out at high temperature and no or little ferrite was precipitated before bainite transformation; when the deformation was carried out at low temperature, the deformation hindered the bainite transformation because a lot of ferrite precipitated before bainite transformation.

Microstructure and mechanical properties of high-strength low alloy steel by wire and arc additive manufacturing

A high-building multi-directional pipe joint(HBMDPJ)was fabricated by wire and arc additive manufacturing using high-strength low-alloy(HSLA)steel.The microstructure characteristics and transformation were observed and analyzed.The results show that the forming part includes four regions.The solidification zone solidifies as typical columnar crystals from a molten pool.The complete austenitizing zone forms from the solidification zone heated to a temperature greater than 1100℃,and the typical columnar crystals in this zone are difficult to observe.The partial austenitizing zone forms from the completely austenite zone heated between Ac1(austenite transition temperature)and1100℃,which is mainly equiaxed grains.After several thermal cycles,the partial austenitizing zone transforms to the tempering zone,which consistes of fully equiaxed grains.From the solidification zone to the tempering zone,the average grain size decreases from 75 to20μm.The mechanical properties of HBMDPJ satisfies the requirement for the intended application.

Multiphase microstructure formation and its effect on fracture behavior of medium carbon high silicon high strength steel

This work investigated the evolution of multiphase microstructure and impact fracture behavior of medium carbon high silicon high strength steel subjected to the austempering treatment at 240,360,and400℃.The results show that martensite,bainite,and retained austenite(RA)are the main microstructural phases.The austempering treatments at 360 and 400℃ caused the formation of carbon-poor ferrite in the matrix,and the transformation of ultrafine bainite into coarse lath bainite and granular bainite,respectively.Thick filmy RA was distributed between bainite laths.The polygonal martensiteaustenite islands and blocky RA formed along the grain boundaries.The average carbon concentration in the matrix decreased with the temperature increase,while the impact toughness initially increased and then dropped with temperature.The quasi-cleavage brittle fracture dominated the impact fracture mechanism of the sample austempered at 240℃ by forming tearing surfaces and tearing steps.The microcracks disappeared in the RA on the prior austenite grain boundaries.On the other side,the fracture surface of the sample austempered at 360℃ exhibited ductile fracture with deep dimples and brittle fracture with cleavage river patterns.The polygonal martensite-austenite islands or blocky RA constrained the microcracks.After austempered at 400℃,the brittle fracture was dominant,showing river patterns,and the microcracks propagated through the granular bainite without any resistance.

Numerical simulation of residual stress and deformation for submerged arc welding of Q690D high strength low alloy steel thick plate

The finite element simulation software SYSWELD is used to numerically simulate the temperature field,residual stress field,and welding deformation of Q690D thick plate multi-layer and multi-pass welding under different welding heat input and groove angles.The simulation results show that as the welding heat input increases,the peak temperature during the welding process is higher,and the residual stress increases,they are all between 330–340 MPa,and the residual stress is concentrated in the area near the weld.The hole-drilling method is used to measure the actual welding residual stress,and the measured data is in good agreement with the simulated value.The type of post-welding deformation is angular deformation,and as the welding heat input increases,the maximum deformation also increases.It shows smaller residual stress and deformation when the groove angle is 40°under the same heat input.In engineering applications,under the premise of guaranteeing welding quality,smaller heat input and 40°groove angle should be used.

Effect of Microstructure on Corrosion Fatigue Behavior of 1500 MPa Level Carbide-Free Bainite/Martensite Dual-Phase High Strength Steel

Influence of microstructure of the experimental steels on the corrosion fatigue behavior in 3.5% of NaCl aqueous solution was studied.Experimental results show that compared with the full martensite（FM）steel,the carbide-free bainite/martensite（CFB/M）steel has higher corrosion fatigue strength and corrosion fatigue crack threshold（ΔKthcf）,and lower corrosion crack propagation rate [（da/dN）cf].

EFFECT OF CARBON CONTENT ON MICROSTRUCTURE AND PROPERTIES OF HIGH STRENGTH AND HIGH ELONGATION STEELS

The micro structure and mechanical properties of new kind of hot-rolled high strength and high elongation steels with retained austenite were studied by discussing the influence of different carbon content. The research results indicate that carbon content has a significant effect on retaining austenite and consequently resulting in high elongation. Besides, new findings about relationship between carbon content and retained austenite as well as properties were discussed in the paper.

Effect of High Pressure Heat Treatment on Microstructure and Compressive Properties of Low Carbon Steel

The effect of high pressure heat treatment on microstructure and compressive properties of low carbon steel were investigated by optical microscope,transmission electron microscope,hardness tester and compression test methods.The results show that martensite appears in low carbon steel at 1-5GPa GPa and 950°C for 15 minutes treatment,high pressure heat treatment can improve the hardness and compressive properties of the steel,the yield strength of the steel increases with increasing pressure,and its compressive properties are better than that treated under normal pressure quenching.

Effect of welding processes on mechanical and microstructural characteristics of high strength low alloy naval grade steel joints

Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, distortion and fatigue damage. These problems can be eliminated by solid state welding process such as friction stir welding(FSW). In this investigation, a comparative evaluation of mechanical(tensile, impact,hardness) properties and microstructural features of shielded metal arc(SMA), gas metal arc(GMA) and friction stir welded(FSW) naval grade HSLA steel joints was carried out. It was found that the use of FSW process eliminated the problems related to fusion welding processes and also resulted in the superior mechanical properties compared to GMA and SMA welded joints.

Effect of Boron on Delayed Fracture Resistance of Medium-Carbon High Strength Spring Steel

The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.