Low-carbon MgO - C specimens with dimension of Ф6 mm × 36 mm were prepared using fused magnesia, flake graphite and carbon black as main starting materials, thermoplastic phenolic resin as binder, hexamethyl ene...Low-carbon MgO - C specimens with dimension of Ф6 mm × 36 mm were prepared using fused magnesia, flake graphite and carbon black as main starting materials, thermoplastic phenolic resin as binder, hexamethyl ene tetramine as curing agent, Si powder （ w （Si） 〉 80%, particle size 〈0. 074 mm） and B℃ （ d90 =36. 5 μm ） as antioxidant, pressing under 200 MPa and drying at 200 ℃ for 24 h. The oxidation resistance tests were conducted at 600 ℃ , 1 000 ℃ and 1 400 ℃ for 2 h, respectively. Effects of B4C and Si antioxidant on oxidation resistance of low-carbon MgO - C brick were studied by comparing the areas of the decarburized layers. The results shaw that： （1） When Si powder addition is 3%, at 600 ℃ and 1 000 ℃, the specimens with 0. 5% B4C perform good oxidation resistance; at 1 400 ℃, the oxidation resistance of the specimens is improved with the addition of B4C increasing, and that of the specimen with 0. 7% B4 C is the best. （2） When B4C addition is 0. 5%, at 600 ℃ and 1 000 ℃ ,the oxidation resistances of the specimens with 3% and 5% Si powder are similar, which are better than that of the specimen with 1% Si powder; and at 1 400 ℃ , the oxidation resistance of the specimens is improved obviously with the addition of Si powder increasing, and that of the specimen with 5% Si powder is the best. （3） Bused on the results, it is believed that the low-carbon MgO - C brick with 0. 5% B4C and 3% Si powder performs the best oxidation resistance.展开更多
The effect of Ti （ C, N） on properties of low-carbon MgO - C bricks was investigated. The phase composition and the microstructure of the matrix of low-carbon MgO - C brick containing Ti （ C, N） were studied by XR...The effect of Ti （ C, N） on properties of low-carbon MgO - C bricks was investigated. The phase composition and the microstructure of the matrix of low-carbon MgO - C brick containing Ti （ C, N） were studied by XRD and SEM analysis together with EDS. The results showed that Ti （ C, N） distributed in the matrix of lowcarbon MgO - C brick uniformly after being treated at 1 600 ~C for 3 h in coke powder bed, and Ti （C, N） and MgO formed a solid solution. After the treatment at 1 600 ℃ for 3 h in coke powder bed, the bulk density and cold crushing strength of low-carbon MgO - C brick with Ti （ C, N） decreased, and the apparent porosity and linear change rate of specimens increased. The oxidation resistance of low-carbon MgO - C brick with Ti（ C, N） was superior to that of low-carbon MgO - C brick with no additives, but inferior to that of low-car- bon MgO - C brick with Al powder. The slag resistance of the specimen with Ti （ C, N） was excellent as well.展开更多
The effects of graphite granularity on the properties of low carbon MgO-C based materials have been investigated in the work. Large crystal fused magnesia, natural flake graphite with different particle sizes and anti...The effects of graphite granularity on the properties of low carbon MgO-C based materials have been investigated in the work. Large crystal fused magnesia, natural flake graphite with different particle sizes and anti-oxidant were adopted as raw material for preparation of specimens. However, the results show that the physical properties, oxidation resistance and thermal shock resistance of low carbon MgO-C materials with content of 4.0wt% graphite are improved obviously through the use of special and suitable size graphite. The excellent performance achieved was considered as a result of microstructure modification of MgO-C materials. Therefore, it is suggested that both fine and micro grade natural flake graphite used for production of low carbon MgO-C bricks.展开更多
文摘Low-carbon MgO - C specimens with dimension of Ф6 mm × 36 mm were prepared using fused magnesia, flake graphite and carbon black as main starting materials, thermoplastic phenolic resin as binder, hexamethyl ene tetramine as curing agent, Si powder （ w （Si） 〉 80%, particle size 〈0. 074 mm） and B℃ （ d90 =36. 5 μm ） as antioxidant, pressing under 200 MPa and drying at 200 ℃ for 24 h. The oxidation resistance tests were conducted at 600 ℃ , 1 000 ℃ and 1 400 ℃ for 2 h, respectively. Effects of B4C and Si antioxidant on oxidation resistance of low-carbon MgO - C brick were studied by comparing the areas of the decarburized layers. The results shaw that： （1） When Si powder addition is 3%, at 600 ℃ and 1 000 ℃, the specimens with 0. 5% B4C perform good oxidation resistance; at 1 400 ℃, the oxidation resistance of the specimens is improved with the addition of B4C increasing, and that of the specimen with 0. 7% B4 C is the best. （2） When B4C addition is 0. 5%, at 600 ℃ and 1 000 ℃ ,the oxidation resistances of the specimens with 3% and 5% Si powder are similar, which are better than that of the specimen with 1% Si powder; and at 1 400 ℃ , the oxidation resistance of the specimens is improved obviously with the addition of Si powder increasing, and that of the specimen with 5% Si powder is the best. （3） Bused on the results, it is believed that the low-carbon MgO - C brick with 0. 5% B4C and 3% Si powder performs the best oxidation resistance.
文摘The effect of Ti （ C, N） on properties of low-carbon MgO - C bricks was investigated. The phase composition and the microstructure of the matrix of low-carbon MgO - C brick containing Ti （ C, N） were studied by XRD and SEM analysis together with EDS. The results showed that Ti （ C, N） distributed in the matrix of lowcarbon MgO - C brick uniformly after being treated at 1 600 ~C for 3 h in coke powder bed, and Ti （C, N） and MgO formed a solid solution. After the treatment at 1 600 ℃ for 3 h in coke powder bed, the bulk density and cold crushing strength of low-carbon MgO - C brick with Ti （ C, N） decreased, and the apparent porosity and linear change rate of specimens increased. The oxidation resistance of low-carbon MgO - C brick with Ti（ C, N） was superior to that of low-carbon MgO - C brick with no additives, but inferior to that of low-car- bon MgO - C brick with Al powder. The slag resistance of the specimen with Ti （ C, N） was excellent as well.
文摘The effects of graphite granularity on the properties of low carbon MgO-C based materials have been investigated in the work. Large crystal fused magnesia, natural flake graphite with different particle sizes and anti-oxidant were adopted as raw material for preparation of specimens. However, the results show that the physical properties, oxidation resistance and thermal shock resistance of low carbon MgO-C materials with content of 4.0wt% graphite are improved obviously through the use of special and suitable size graphite. The excellent performance achieved was considered as a result of microstructure modification of MgO-C materials. Therefore, it is suggested that both fine and micro grade natural flake graphite used for production of low carbon MgO-C bricks.