The effect of rare earth metals(REM)on the characteristics of auto-tempering and decomposition of martensite for low-carbon and low-alloy steels(20SiMn2V and 20SiMn2VRE)was investigated using TEM,dilatometer and micro...The effect of rare earth metals(REM)on the characteristics of auto-tempering and decomposition of martensite for low-carbon and low-alloy steels(20SiMn2V and 20SiMn2VRE)was investigated using TEM,dilatometer and microhardness test.Results show that both ε.and θ carbides,during auto-tempering, may precipitate from the low-carbon martensite matrix at the same time in the 20SiMn2V steel,however,the precipitation of the ε-carbides can be inhibited by the REM contained in the 20SiMn2 VRE steel,resulting in change of the type of precipitated carbides and decrease of the extent of auto-tempering.The“in-situ”ob- servations show that the decomposition of martensite is also inhibited by the REM contained in the 20SiMn2 VRE steel during low temperature tempering.展开更多
In this study,normalized 00 Cr13 Ni5 Mo low-carbon martensitic stainless steel was tempered at temperatures ranging between 500-700 ℃ for 8 h and its mechanical properties were determined. The results show that the m...In this study,normalized 00 Cr13 Ni5 Mo low-carbon martensitic stainless steel was tempered at temperatures ranging between 500-700 ℃ for 8 h and its mechanical properties were determined. The results show that the mechanical properties vary with a variation in the tempering temperature. Samples tempered at 650 ℃exhibited a good combination of properties and a low yield ratio. Scanning electron microscopy observations and Xray diffraction analysis revealed that the tempering process involved carbide precipitation,austenitic inversion,and quenching,and the properties of materials changed with a change in the tempering temperature.展开更多
文摘The effect of rare earth metals(REM)on the characteristics of auto-tempering and decomposition of martensite for low-carbon and low-alloy steels(20SiMn2V and 20SiMn2VRE)was investigated using TEM,dilatometer and microhardness test.Results show that both ε.and θ carbides,during auto-tempering, may precipitate from the low-carbon martensite matrix at the same time in the 20SiMn2V steel,however,the precipitation of the ε-carbides can be inhibited by the REM contained in the 20SiMn2 VRE steel,resulting in change of the type of precipitated carbides and decrease of the extent of auto-tempering.The“in-situ”ob- servations show that the decomposition of martensite is also inhibited by the REM contained in the 20SiMn2 VRE steel during low temperature tempering.
文摘In this study,normalized 00 Cr13 Ni5 Mo low-carbon martensitic stainless steel was tempered at temperatures ranging between 500-700 ℃ for 8 h and its mechanical properties were determined. The results show that the mechanical properties vary with a variation in the tempering temperature. Samples tempered at 650 ℃exhibited a good combination of properties and a low yield ratio. Scanning electron microscopy observations and Xray diffraction analysis revealed that the tempering process involved carbide precipitation,austenitic inversion,and quenching,and the properties of materials changed with a change in the tempering temperature.