The grain refinement of superalloy IN718 under the action of low voltage pulsed magnetic field was investigated. The experimental results show that fine equiaxed grains are acquired under the action of low voltage pul...The grain refinement of superalloy IN718 under the action of low voltage pulsed magnetic field was investigated. The experimental results show that fine equiaxed grains are acquired under the action of low voltage pulsed magnetic field. The refinement effect of the pulsed magnetic field is affected by the melt cooling rate and superheating. The decrease of cooling rate and superheating enhance the refinement effect of the low voltage pulsed magnetic field. The magnetic force and the melt flow during solidification are modeled and simulated to reveal the grain refinement mechanism. It is considered that the melt convection caused by the pulsed magnetic field, as well as cooling rate and superheating contributes to the refinement of solidified grains.展开更多
The low voltage pulsed magnetic field(LVPMF)disrupts the columnar dendrite growth,and the columnarto-equiaxed transition(CET)occurs during the directional solidification of superalloy K4169.Within the pulse voltage ra...The low voltage pulsed magnetic field(LVPMF)disrupts the columnar dendrite growth,and the columnarto-equiaxed transition(CET)occurs during the directional solidification of superalloy K4169.Within the pulse voltage ranging from 100Vto 200 V,a transition from columnar to equiaxed grain was observed,and the grain size decreased as the pulse voltage rised.As the pulse frequency increased,the CET occurred,and the grains were refined.However,the grains became coarse,and the solidification structure was columnar crystal again when frequency increased to 10 Hz.The LVPMF had an optimal frequency to promote CET.The LVPMF on the CET was affected by the withdrawal speed and increasing the withdrawal speed enhances the CET.The distribution of electromagnetic force and flow field in the melt under the LVPMF were modeled and simulated to reveal the CET mechanism.It is considered that the CET should be attributed to the coupling effects of magnetic vibration and melt convection induced by the LVPMF.展开更多
基金Project(2010CB631205)supported by the National Basic Research Program of ChinaProject(51034012)supported by the National Natural Science Foundation of China
文摘The grain refinement of superalloy IN718 under the action of low voltage pulsed magnetic field was investigated. The experimental results show that fine equiaxed grains are acquired under the action of low voltage pulsed magnetic field. The refinement effect of the pulsed magnetic field is affected by the melt cooling rate and superheating. The decrease of cooling rate and superheating enhance the refinement effect of the low voltage pulsed magnetic field. The magnetic force and the melt flow during solidification are modeled and simulated to reveal the grain refinement mechanism. It is considered that the melt convection caused by the pulsed magnetic field, as well as cooling rate and superheating contributes to the refinement of solidified grains.
基金supported by the National Natural Science Foundation of China(No.51674236)the Key Research and Development Program of Liaoning Province(2019JH2/10100009)+1 种基金the National Science and Technology Major Project(No.2017-VI-00-0073)the National Key Research and Development Program(No.2018YFA0702900).
文摘The low voltage pulsed magnetic field(LVPMF)disrupts the columnar dendrite growth,and the columnarto-equiaxed transition(CET)occurs during the directional solidification of superalloy K4169.Within the pulse voltage ranging from 100Vto 200 V,a transition from columnar to equiaxed grain was observed,and the grain size decreased as the pulse voltage rised.As the pulse frequency increased,the CET occurred,and the grains were refined.However,the grains became coarse,and the solidification structure was columnar crystal again when frequency increased to 10 Hz.The LVPMF had an optimal frequency to promote CET.The LVPMF on the CET was affected by the withdrawal speed and increasing the withdrawal speed enhances the CET.The distribution of electromagnetic force and flow field in the melt under the LVPMF were modeled and simulated to reveal the CET mechanism.It is considered that the CET should be attributed to the coupling effects of magnetic vibration and melt convection induced by the LVPMF.