Gating system optimization of low pressure casting A356 aluminum alloy intake manifold based on numerical simulation

To eliminate the shrinkage porosity in low pressure casting of an A356 aluminum alloy intake manifold casting, numerical simulation on fi lling and solidifi cation processes of the casting was carried out using the ProCAST software. The gating system of the casting is optimized according to the simulation results. Results show that when the gating system consists of only one sprue, the fi lling of the molten metal is not stable; and the casting does not follow the sequence solidifi cation, and many shrinkage porosities are observed through the casting. After the gating system is improved by adding one runner and two in-gates, the fi lling time is prolonged from 4.0 s to 4.5 s, the fi lling of molten metal becomes stable, but this casting does not follow the sequence solidifi cation either. Some shrinkage porosity is also observed in the hot spots of the casting. When the gating system was further improved by adding risers and chill to the hot spots of the casting, the shrinkage porosity defects were eliminated completely. Finally, by using the optimized gating system the A356 aluminum alloy intake manifold casting with integrated shape and smooth surface as well as dense microstructure was successfully produced.

Effect of pressurizing speed on filling behavior of gradual expansion structure in low pressure casting of ZL205A alloy

The mold filling behavior of gradual expansion structure in low pressure casting was studied by two phase flow model using the Volume of Fluid method, and was verified by water simulation with a Plexiglas mold. To get smooth mold filling process and provide a guide for the pressurizing speed design in the producing practice, the mathematical model with the pressurizing speed, expansion angle and height of the gradual expansion structure was established. For validation experiments, ZL205 A alloy castings were produced under two different pressurizing speeds. Weibull probability plots were used to assess the fracture mechanisms under different pressurizing speeds. Mechanical properties of ZL205 A alloy were applied to assess the entrainment of oxide film. The results show that the filling process of a gradual expansion structure in a low pressure casting can be divided into the spreading stage and filling stage by gate velocity. The gate velocity continues to increase in the gradual expansion structure, and increases with the increase of pressurizing speed or expansion angle. Under the effect of the falling fluid raised by the jet flow along the sidewall, the fluid velocity decreases in the jet zone from ingate to free surface. As such, oxide film entrainment does not occur when the gate velocity is greater than the critical velocity, andthe gate velocity no longer reflects the real state of the free surface. The scatter of the mechanical properties is strongly affected by the entrainment of oxide films.

Pressurization control system for low pressure crucible casting

A new compact pressurization control system of the low pressure casting machine for crucible pressure casting has been developed. It is especially designed for the production of high-quality aluminum or magnesium alloy parts with low input cost. This machine with such a system has the virtue of economical and compact, and combines the Fuzzy-PID technology and achieves accuracies of ±2.5 mbar. At present, this machine has been adopted by several users in China for the production of aluminum alloy castings with high property requirements. Furthermore, for magnesium alloy castings, this machine can be used with the gas protect unit.

THE PRODUCTION OF FOAM ALUMINIUM ALLOY BY LOW-PRESSURE INFILTRATION METHOD

The influence of technical parameters on the infiltrating height of the moltenmetal in the process of Producing aluminium alloy foam by low-pressure infiltration method were investigated.Experiments indicated that the height increases with the preheating temperature of granules,theexternal pressureand the pouring temperature of molten alloy,among which the action of pre heating temperature of granules is more effective.There exists a critical pre heating temperature for different size of granules.

Effect of pressure on the feeding characteristics of ZCuZn16Si4 alloy

The experimental and numerical simulation methods were employed to study the effect of pressure on the feeding characteristics of ZCuZn16Si4 alloy castings. The results proved that different pressures would lead to different feeding distance of riser over a suitable pressure range, and the pressure can be used to greatly improve the feeding characteristics compared with gravity casting. It should be pointed out that current porosity criteria in the numerical simulation codes cannot yet be applied well enough to predict the porosity defects of low-pressure copper alloy castings.

Study on Numerical Simulation of Mold Filling and Solidification Processes under Pressure Conditions

The mold filling and solidification simulation for the high pressure die casting (HPDC) and low pressure die casting (LPDC) processes were studied. A mathematical model considering the turbulent flow and heat transfer phenomenon during the HPDC process has been established and parallel computation technique was used for the mold filling simulation of the process. The laminar flow characteristics of the LPDC process were studied and a simplified model for the mold filling process of wheel castings has been developed. For the solidification simulation under pressure conditions, the cyclic characteristics and the complicated boundary conditions were considered and techniques to improve the computational efficiency are discussed. A new criterion for predicting shrinkage porosity of Al alloy under low pressure condition has been developed in the solidification simulation process.

Determining casting defects in near-net shape casting aluminum parts by computed tomography

Three types of near-net shape casting alumi- num parts were investigated by computed tomography to determine casting defects and evaluate quality. The first, second, and third parts were produced by low-pressure die casting （Al-12Si-0.8Cu-0.5Fe-0.9Mg-0.7Ni-0.2Zn alloy）, die casting （A356, A1-7Si-0.3Mg）, and semi-solid casting （A356, A1-TSi-0.3Mg）, respectively. Unlike die casting （second part）, low-pressure die casting （first part） sig- nificantly reduced the formation of casting defects （i.e., porosity） due to its smooth filling and solidification under pressure. No significant casting defect was observed in the third part, and this absence of defects indicates that semi- solid casting could produce high-quality near-net shape casting aluminum parts. Moreover, casting defects were mostly distributed along the eutectic grain boundaries. This finding reveals that refinement of eutectic grains is necessary to optimize the distribution of casting defects and reduce their size. This investigation demonstrated that computed tomography is an efficient method to determine casting defects in near-net shape casting aluminum parts.