A novel salt-assisted low temperature solid state method using CoCl2.6H2O, FeCl3.6H2O and NaOH as precursor and using NaCI as a dispersant to synthesize high surface area CoFe2O4 nanoparticles, has been investigated. ...A novel salt-assisted low temperature solid state method using CoCl2.6H2O, FeCl3.6H2O and NaOH as precursor and using NaCI as a dispersant to synthesize high surface area CoFe2O4 nanoparticles, has been investigated. The effects of the molar ratio of added salt and calcination temperature on the characteristics of the products were investigated by X-ray diffraction （XRD）, transmission electron microscopy （TEM）, vibrating sample magnetometer （VSM） and Brunauer, Emmett and Teller （BET） surface area analysis. Results showed that the introduction of leachable inert inorganic salt as a hard agglomeration inhibitor in the mixture precursor led to the formation of high dispersive CoFe2O4 nanoparticles; and the increase in specific surface area from 28.28 to 73.97 m^2/g, and the saturation magnetization is 84.6 emu/g.展开更多
基金supported by the National Natural Sci-ence Foundation of China under grant No. 50602024the Youth Foundation of North University of China
文摘A novel salt-assisted low temperature solid state method using CoCl2.6H2O, FeCl3.6H2O and NaOH as precursor and using NaCI as a dispersant to synthesize high surface area CoFe2O4 nanoparticles, has been investigated. The effects of the molar ratio of added salt and calcination temperature on the characteristics of the products were investigated by X-ray diffraction （XRD）, transmission electron microscopy （TEM）, vibrating sample magnetometer （VSM） and Brunauer, Emmett and Teller （BET） surface area analysis. Results showed that the introduction of leachable inert inorganic salt as a hard agglomeration inhibitor in the mixture precursor led to the formation of high dispersive CoFe2O4 nanoparticles; and the increase in specific surface area from 28.28 to 73.97 m^2/g, and the saturation magnetization is 84.6 emu/g.