For a longitudinal welded joint, the tensile residual stresses are as high as the yield stress of the metal, so that the weld toes are sensitive to fatigue load. In this case a low transformation temperature electrode...For a longitudinal welded joint, the tensile residual stresses are as high as the yield stress of the metal, so that the weld toes are sensitive to fatigue load. In this case a low transformation temperature electrode (LTTE) is one of the most useful methods used to improve the fatigue strength of the longitudinal welded joint, because the tensile residual stress is reduced or changed into compressive stress. Three kinds of longitudinal welded joints were selected to conduct fatigue tests. The tests results show that the fatigue strengths at 2×10 6 cycles of the joints welded with LTTE were improved by 41%, 47% and 59% respectively compared with those of the joints welded with E5015, and the fatigue lives at 162 MPa were improved by 9.9 times, 9.6 times and 46.8 times respectively. Furthermore, the LTTE method is not necessary to add process after welding and so that it can be valuable method to improve the fatigue performance of longitudinal welded joints.展开更多
A new welding electrode, low transformation temperature electrode (LTTE), was introduced in this paper. It was described in design principle, mechanics, chemical compositions of their deposited metal and manufacturing...A new welding electrode, low transformation temperature electrode (LTTE), was introduced in this paper. It was described in design principle, mechanics, chemical compositions of their deposited metal and manufacturing methods. It was proved that the best transformation starting temperature from austenite to martensite of the deposited metal of LTTE was at about 191℃ and it was obtained by adding alloying elements such as Cr, Ni, Mn and Mo. The microstructure of the weld metal of the LTTE was low carbon martensite and residual austenite. The compressive residual stress was induced around the weld of the LTTE and the -145 MPa in compression could be obtained in middle of weld metal. The fatigue tests showed that the fatigue strength of the longitudinal welded joints welded with the LTTE at 2×106 cycles was improved by 59% compared with that of the same type of welded joints welded with conventional E5015 and the fatigue life was increased by 47 times at 162 MPa. It is a very valuable method to improve the fatigue performance of welded joints.展开更多
文摘For a longitudinal welded joint, the tensile residual stresses are as high as the yield stress of the metal, so that the weld toes are sensitive to fatigue load. In this case a low transformation temperature electrode (LTTE) is one of the most useful methods used to improve the fatigue strength of the longitudinal welded joint, because the tensile residual stress is reduced or changed into compressive stress. Three kinds of longitudinal welded joints were selected to conduct fatigue tests. The tests results show that the fatigue strengths at 2×10 6 cycles of the joints welded with LTTE were improved by 41%, 47% and 59% respectively compared with those of the joints welded with E5015, and the fatigue lives at 162 MPa were improved by 9.9 times, 9.6 times and 46.8 times respectively. Furthermore, the LTTE method is not necessary to add process after welding and so that it can be valuable method to improve the fatigue performance of longitudinal welded joints.
基金This project was supported by the National Natural Science Foundation of China under grant No.50175079.
文摘A new welding electrode, low transformation temperature electrode (LTTE), was introduced in this paper. It was described in design principle, mechanics, chemical compositions of their deposited metal and manufacturing methods. It was proved that the best transformation starting temperature from austenite to martensite of the deposited metal of LTTE was at about 191℃ and it was obtained by adding alloying elements such as Cr, Ni, Mn and Mo. The microstructure of the weld metal of the LTTE was low carbon martensite and residual austenite. The compressive residual stress was induced around the weld of the LTTE and the -145 MPa in compression could be obtained in middle of weld metal. The fatigue tests showed that the fatigue strength of the longitudinal welded joints welded with the LTTE at 2×106 cycles was improved by 59% compared with that of the same type of welded joints welded with conventional E5015 and the fatigue life was increased by 47 times at 162 MPa. It is a very valuable method to improve the fatigue performance of welded joints.