Kinetics of bainite-to-austenite transformation during continuous reheating in low carbon microalloyed steel

A dilatometer was used to study the kinetics of bainite-to-austenite transformation in low carbon microalloyed steel with the initial microstructure of bainite during the continuous reheating process. The bainite-to-austenite trans- formation was observed to take place in two steps at low heating rate. The first step is the dissolution of bainite, and the second one is the remaining bainite-to-austenite transformation controlled by a dissolution process. The calculation result of the kinetics of austenite formation shows that the two steps occur by diffusion at low heating rate. However, at high heating rate the bainite-to-austenite transformation occurs in a single step, and the process is mainly dominated by shear. The growth rate of austenite reaches the maximum at about 835℃ at different heating rates and the growth rate of austenite as a function of temperature increases with the increase in heating rate.

INFLUENCE OF HOT DEFORMATION ON CONTINUOUSCOOLING BAINITIC TRANSFORMATION IN A LOWCARBON STEEL

The influence of hot deformation conditions on continuous cooling bainitic transformation has been investigated for a low carbon microalloyed steel. The CCT diagrams show that deformation in unrecrpstallized austcnite ation can accelerate transformation process. Bainitic transformation in intermediate transformation temperature region is prominent, and the proeutectoid polygonal ferrite transformation at evelated high temperature is suppressed. According to optical and TEM analyses, low carbon bainitic ferrite is characterized by granular and lathlike ferrite, based on the cooling rate and deformation conditions. For nondeformation, groaps of coarse parallel ferrite lath form from the prior austenite grain boundaries with the same crystallographic orientation. For heavy deformaton, cell structure within the austenite grains due to the high dislocation density formed, which provides more nucleation sites for bainite ferrite. So deformation can discontinue the growth of ferrite laths and decrease the length of ferrite laths.

DEFORMATION ENHANCED FERRITE TRANSFORMATION IN PLAIN LOW CARBON STEEL

The microstructure evolution during deformation enhanced transformation of undercooled austenite of a plain low carbon steel has been investigated by means of hot compression simulation experiment under various conditions of strain rate, deformation temperature and strain. The effect of austenite grain size on the strain enhanced ferrite transformation has been studied. The ferrite dynamic recrystallization involved in successive hot deformation has been explored.

Bainite Transformation Under Continuous Cooling of Nb-Microalloyed Low Carbon Steel

Utilizing Gleeble-1500 thermomechanical simulator, the influences of hot deformation parameters on continuous cooling bainite transformation in Nb-microalloyed low carbon steel were investigated. The results indicate that bainite starting temperature decreases with raising cooling rate and increases with increasing deformation temperature. Deformation has an accelerative effect on the bainite transformation when the specimens are deformed at 950 ℃. When the deformation temperature increases, the effect of deformation on bainite starting temperature is weakened. The amount of bainite is influenced by strain, cooling rate, and deformation temperature. When the specimens are deformed below 900 ℃, equiaxed ferrites are promoted and the bainite transformation is suppressed.

Effects of Deformation on Bainite Transformation During Continuous Cooling of Low Carbon Steels

Hot deformation experiments were carried out on Gleeble 1500 thermo-mechanical simulator. The bainite transformation after deformation was investigated by optical microstructure analysis. The results indicated that the deformation accelerated the bainite transformation when the deformation was carried out at high temperature and no or little ferrite was precipitated before bainite transformation; when the deformation was carried out at low temperature, the deformation hindered the bainite transformation because a lot of ferrite precipitated before bainite transformation.

Effect of silicon and prior deformation of austenite on isothermal transformation in low carbon steels

Isothermal transformation （TTT） behavior of the low carbon steels with two Si contents （0.50 wt pct and 1.35 wt pct） was investigated with and without the prior deformation. The results show that Si and the prior deformation of the austenite have significant effects on the transformation of the ferrite and bainite. The addition of Si refines the ferrite grains, accelerates the polygonal ferrite transformation and the formation of M/A constituents, leading to the improvement of the strength. The ferrite grains formed under the prior deformation of the austenite become more homogeneous and refined. However, the influence of deformation on the tensile strength of both steels is dependent on the isothermal temperatures. Thermodynamic calculation indicates that Si and prior deformation reduce the incubation time of both ferrite and bainite transformation, but the effect is weakened by the decrease of the isothermal temperatures.

Effects of C and Mn elements on deformation-enhanced ferrite transformation in low carbon (Mn) steels

Effects of C and Mn contents on the deformation-enhanced ferrite transformation （DEFT） in low carbon （Mn） steels have been investigated by hot compression. The microstructures of 2-4μm ultra-fine equiaxed ferrite grains with minors distributed homogeneously can be obtained by DEFT in all the tested steels. The more pronounced refinement is achieved as the C or Mn content increasing because of the higher-density nucleating sites and lower growth rate. The effectiveness of C on the level of refinement is more obvious than that of Mn.

PHASE TRANSFORMATION UNIT OF BAINITIC FERRITE AND ITS SURFACE RELIEF IN LOW AND MEDIUM CARBON ALLOY STEELS

The lath-or plate-shaped bainitic ferrite of low and medium carbon alloy steels consists of packets of ferrite sublaths which are composed of many finer and regular ferrite blocks.They are uniform shear growth units of bainitic phase transformation.No carbide is precipitated from them.The bainitic O-carbides are precipitated from γ-α interface or carbon-rich austenite.The mode of arrangement of the units in ferrite sublath packet is in uni-or bi-di- rection.Single surface relief is produced by the accumulation of uniform shear strains with all the ferrite units arranged unidirectionally in a sublath packet,while tent-shaped surface relief is formed by the integration of the uniform shear strains of two groups with ferrite units piling up in two directions and growing face to face;whereas if they grow back to back,the integra- tion will be responsible for invert-tent-shaped surface relief.The interface trace between two groups of ferrite units in a sublath packet is shown as“midrib”.

Investigation into the stress-strain curves of deformation-induced ferrite transformation in a low carbon steel

A series of tests of deformation-induced ferrite transformation （DIP-T） in a low carbon steel were carried out by the Gleeble-3500 hot simulation machine at a temperature range of Ae3-Ar3. The overall stress-strain curves during DIFT can be divided into three typical types： ＂double-humped＂,＂ single-humped＂ and ＂transitional＂. The peaks exhibited in the curve are involved with deformation-induced transformation which happened in grains or at the grain boundaries. According to the stress-time curve and strain-time curve, strain capacity dramatically postponed the strain-induced transformation, which leads to the start of the transformation right ahead of the finish of deformation and the majority of the ferrite transformation process mainly happened after the deformation. Deformation-induced transformation is a metadynamic transformation process with dynamic nucleation.

Low-temperature phase transformation from nanotube to sp^3 superhard carbon phase

Numerous new carbon allotropes have been uncovered by compressing carbon nanotubes based on our computational investigation. The volume compression calculations suggest that these new phases have a very high anti-compressibility with a large bulk modulus （B0）. The predicted B0 of new phases is larger than that of c-BN （373 GPa） and smaller than that of diamond （453 GPa）. All of the predicted structures are superhard transparent materials with a larger band gap and possess the covalent characteristics with sp3-hybridized electronic states. The simulated results will help us better understand the structural phase transition of cold-compressed carbon nanotubes.

Low-carbon transformation of industrial structure in China

The traditional economic growth mode of "three highs and one low(high input, high consumption, high pollution and low effi ciency)" makes China get the achievements of economic development and prosperity during the reform and opening up with more than 30 years, but behind this extensive mode of economic growth is excessive consumption of natural resources and a lot of greenhouse gases emissions, this not only limits the growth rate of China's economy, but makes a tremendous negative impact on the environment which is diffi cult for us to survive. Therefore, realizing industrial structure low-carbon effectively and developing a low-carbon economy characterized by "low-power, low consumption, low pollution and low emissions", become China's new target selection to transform economic development mode and realize the goal of optimization and upgrading of industrial structure and sustainable development.

Exploring the “Green” Transformation Planning of Industrial Parks in the Era of Low Carbon Economy

The core function of the low carbon economy is to change the economic development trend of the whole society. It is necessary to carry out industrial transformation and upgrading according to the concept of sustainable development and to realize integrated technological innovation and efficient economic development without violating the law of ecological and environmental development. In the era of the low-carbon economy, industrial parks should solidly promote the green transformation planning process. Relying on the basic logical framework of green transformation of industrial parks, it can build a green development quality evaluation system of industrial parks and formulate a green planning mechanism and green economic cycle development model in line with the background of the low-carbon economy.

Transformation of Carbon and Nitrogen by Earthworms in the Decomposition Processes of Broad-leaved Litters

Earthworms are the important constituents in the decayed food web and the main ecological conditioners in the process of decomposition and nutrient mineralization. The transformation of organic carbon (C) and total nitrogen (N) in the broad-leaved litters ingested by earthworms was researched by means of a laboratory experiment. Experimental samples were collected from broad-leaved Korea Pine mixed forest in Liangshui National Natural Reserve (47°10′50″N, 128°53′20″E) in the northeastern Xiao Hinggan Mountains of Northeast China. The contents of organic C and total N in earthworms, leaf litters and earthworm faeces were analyzed. Results show that the organic C content was in the fol- lowing order: leaf litters>faeces>earthworms, while total N content was contrary to that of the organic C. The organic C contents in the different leaf litters were in the following order: Tilia amurensis>Betula costata>Acer mono, whereas the total N contents in the different leaf litters were: Betula costata>Tilia amurensis>Acer mono. The contents of organic C and total N in the faeces from the different leaf litters were almost consistent with the contents of the leaf litters. After the leaf litters were ingested by earthworms, the organic C, which was transformed to increase earthworms' weights, ac- counted for 3.90%-13.31% of the total ingestion by earthworms, while that in the earthworm faeces accounted for 6.14%-13.70%. The transformed organic C through the other metabolism (e.g., respiration) of earthworms accounted for 75.04%-89.92%. The ingested organic C by earthworms was mostly used for metabolic activities. The N ingested by earthworms was less than organic C. It is estimated that 37.08% of total N was transformed to increase the earthworm's weight, 19.97% into earthworm faeces and 47.86% for the consumption of the earthworm's activities. The earthworms not only increased the content of organic C and total N in the soil, but also decreased the values of C/N in the soil and leaf litters. Earthworms play a major role in the leaf litters' decomposition and transformation.

Genetic Transformation of Watermelon with Pumpkin DNA by Low Energy Ion Beam-mediated Introduction

The No.601 watermelon (citrullus lanatus) seeds were treated with 25 keV N+ implantation at the dosage of 7.8 ×1016 ions/cm2. After treatment, watermelon seeds were incubated with 380μg/μl pumpkin (Cucubita, maxima Duch) DNA solution at 35 ℃ for 5 hours. By two-generations of selection and resistance screening at seedling stage, one transformed material was selected out, whose rind color is similar to that of the donor pumpkin and whose size of seeds is between that of the donor and the receptor. Using AFLP (amplified fragment length polymorphism) technique, two polymorphic DNA fragments were amplified. This primarily testified that the donor DNA fragments/gene were introduced into the receptor cell and integrated into the genomic DNA of the receptor.

Super long-range diffusion of carbon during proeutectoid ferrite transformation

In order to explore the possible diffusion distance of carbon during proeutectoid ferrite transformation, a slow cooling test of low carbon steel was carried out under vacuum of the thermal simulator. The microstructure and thermal expansion curve were discussed and the carbon concentration inside the sample was measured. The ferrite layer of about 450 μm thickness was obtained without pearlite on the surface of the sample in the microstructure. The thermal expansion curve shows that the ferrite layer without pearlite is formed during the local phase transformation, which is followed by the global transformation. The carbon concentration in the core of the sample (0.061%) is significantly higher than that of the bulk material (0.054%). All results show that carbon has long-range diffusion from the outer layer to the inner layer of the sample. The transformation is predominantly interface-controlled mode during local transformation, and the interface migration rate is about 2.25 μm/s.

Properties of Activated Carbons from Sugarcane Leaves and Rice Straw Derived Charcoals by Activation at Low Temperature via KMnO_(4)Pre-Oxidation-Hydrolysis

Activated carbon preparation from sugarcane leaves and rice straw by carbonization(250℃–400℃)and activation at 500℃were studied.The effects of pre-oxidation,hydrolysis of derived charcoals by boiled KMnO4 aqueous solution were evaluated.The derived charcoals products were pretreated using oxidation-hydrolysis with 1–5 wt.%KMnO4 at 100℃and then activated at 500℃.The derived charcoal and activated carbon products were characterized by FTIR,XRD,SEM-EDS and BET.Iodine number and methylene blue number of derived products were also used for the analysis of the products.It was found that fabricated charcoal materials made at 350℃–400℃possess good characteristics with low content of surface functional groups and high carbon content.After pre-oxidation-hydrolysis and activation at 500℃,the resulting derived activated carbon materials from charcoals with 400℃carbonization temperature have high content of oxygen containing surface functional groups such as Mn-O,Si-O,Si-O-Si,C-O,or O-H.In addition,MnO_(2) accumulated on the surface of the derived activated carbon products.The surface area and pore volume of the activated carbon products have also increased with increasing of KMnO_(4) concentration from 1 to 3 wt.%and then decreased with 5 wt.%used during activation.Therefore,activated carbon products made by pre-oxidation-hydrolysis with 3 wt.%KMnO_(4) were used for Fe(Ⅲ)adsorption experiments.It was found that Fe(Ⅲ)adsorption on the activated carbon materials can be fitted with both the Freundlich and the Langmuir models.The calculated maximum Fe(Ⅲ)adsorption capacities of sugarcane leaves derived activated carbon and rice straw derived activated carbon products were 50.00 and 39.37 mg/g,respectively.It was shown that the effect of pre-oxidation-hydrolysis by KMnO_(4) and activation at 500℃are beneficial for activated carbon preparation with environmentally friendly and low-cost simplified operation.

Collaborative robust dispatch of electricity and carbon under carbon allowance trading market

The launch of the carbon-allowance trading market has changed the cost structure of the power industry.There is an asynchronous coupling mechanism between the carbon-allowance-trading market and the day-ahead power-system dispatch.In this study,a data-driven model of the uncertainty in the annual carbon price was created.Subsequently,a collaborative,robust dispatch model was constructed considering the annual uncertainty of the carbon price and the daily uncertainty of renewable-energy generation.The model is solved using the column-and-constraint generation algorithm.An operation and cost model of a carbon-capture power plant(CCPP)that couples the carbon market and the economic operation of the power system is also established.The critical,profitable conditions for the economic operation of the CCPP were derived.Case studies demonstrated that the proposed low-carbon,robust dispatch model reduced carbon emissions by 2.67%compared with the traditional,economic,dispatch method.The total fuel cost of generation decreases with decreasing,conservative,carbon-price-uncertainty levels,while total carbon emissions continue to increase.When the carbon-quota coefficient decreases,the system dispatch tends to increase low-carbon unit output.This study can provide important guidance for carbon-market design and the low-carbon-dispatch selection strategies.

Effects of nano-AlN on phase transformation of low temperature vitrified bond during sintering process

The effects of nano-AlN and sintering temperature on bending strength and wear resistance of low temperature vitrified bond for diamond grinding tools were studied. Furthermore, the phase transformation during sintering process was investigated by means of thermo-gravimetric analysis (TG), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results show that the higher bending strength and wear resistance of low temperature vitrified bond are obtained by adding nano-AlN in bonds and sintering at optimum temperature. Nano-AlN added in bonds promotes the crystallization during sintering process and refines the grain sizes of crystalline phase.