In indoor design innovation, the material role can not be ignored. In indoor design, using non-conventional decoration materials can make space more personalized and charming. This is one of the material innovation mo...In indoor design innovation, the material role can not be ignored. In indoor design, using non-conventional decoration materials can make space more personalized and charming. This is one of the material innovation modes and also one of the indoor design innovation modes. The design method should obtain more attention.展开更多
The influence of a polyvinyl chloride（PVC）-panel on the cooling load of a residential apartment in Mashad,Iran,is analyzed by the DeST-h software.And the summer natural ventilation of the residential apartment is in...The influence of a polyvinyl chloride（PVC）-panel on the cooling load of a residential apartment in Mashad,Iran,is analyzed by the DeST-h software.And the summer natural ventilation of the residential apartment is investigated to determine the wind speed into the apartment through the computational fluid dynamics software.The evaluation results of the indoor wind velocity show that most parts of the apartment are comfortable.The cooling load of the penthouse can be decreased about 10.5% or 6.5% when an air layer exists or does not exist between the ceiling and the PVC-panel,respectively,indicating that the existence of the air layer can decrease the cooling load.However,the effect of the increase in the air layer＇s thickness on the decrease in the cooling load is obvious.Adding a thin layer of air between the ceiling and the PVC-panel is a good step toward sustainable buildings.展开更多
In this paper,both oxidation and corrosion resistance of low-carbon magnesia-carbon materials containing 4.0wt% graphite with metallic Al and Mg-Al alloy powders as antioxidants were investigated.Meanwhile,the microst...In this paper,both oxidation and corrosion resistance of low-carbon magnesia-carbon materials containing 4.0wt% graphite with metallic Al and Mg-Al alloy powders as antioxidants were investigated.Meanwhile,the microstructures of samples corroded by slag were observed with optical microscope as well.The test results revealed the properties of oxidation and corrosion resistance of low-carbon magnesia-carbon materials could be improved obviously by adding metal Al powder and Mg-Al alloy powder.The rule of improving oxidation resistance was illegibility when metal Al powder and Mg-Al alloy powder were added together.It was harmful to corrosion resistance by mixed adding metal Al powder and Mg-Al alloy powder into the materials,at the same time,the corrosion resistance would decreased with the increasing of Mg-Al alloy content.The corrosion resistance of samples with 0.5wt% or 3.0wt% Mg-Al alloy was better. The oxidation resistance and corrosion resistance of materials with metal Al or Mg-Al alloy respectively were better than that with mixed metal Al and Mg-Al alloy. As a result, Mg-Al alloy was more suitable for low-carbon composite materials than metal Al as additives.展开更多
Effects of Al- Si addition on hot modulus of rup- ture ~ HMOR） . thermal shock resistance ~ TSR~ . phase composition and mierostructure of low-carbon MgO - C materials were investigated. The results show that： Al an...Effects of Al- Si addition on hot modulus of rup- ture ~ HMOR） . thermal shock resistance ~ TSR~ . phase composition and mierostructure of low-carbon MgO - C materials were investigated. The results show that： Al and Si addition to low-carbon MgO - C materials leads to dramatic increase in MOR at elevated temperatures; it increases from 4 MPa to 11 -21 MPa at 1 200 ℃ and from 2 MPa to 21 -29 MPa at 1 400 ℃. Al and Si addition to low-carbon MgO - C materials also improves TSR： residual strength ratio after thermal shock when △T = 1 200 ℃ is increased,from 44% to 73% - 77%. Al reacts with C and N2 to form, Al4C3 and AlN, Si reacts with C to form SiC. Ultimately. in-situ formed non- oxides increase appreciably with temperature rising and are well interlaced in periclase skeleton structure at 1 300 -1 400 ℃. which is beneficial to thermomechanical properties.展开更多
In this paper ,the influence of ZnO and BaO contents on sintering and crystallization of decorative materi-al in the system of CaO-Al2O3-SiO2wwas studied. The opti-mum ZnO 9 BaO contents and sintering or crystallizati...In this paper ,the influence of ZnO and BaO contents on sintering and crystallization of decorative materi-al in the system of CaO-Al2O3-SiO2wwas studied. The opti-mum ZnO 9 BaO contents and sintering or crystallization tem-perature for the glass-ceramic were determined.展开更多
The hole transport material (HTM) plays an extremely important role to determine the power conversion efficiency (PCE) and the stability of perovskite solar cells (PSCs). Herein, we report an effective strategy to imp...The hole transport material (HTM) plays an extremely important role to determine the power conversion efficiency (PCE) and the stability of perovskite solar cells (PSCs). Herein, we report an effective strategy to improve the performance of HTMs by introducing −CF_(3) groups via the rational decorative mode. Upon direct attachment or nonconjugated alkoxyl bridging of −CF_(3) groups on the terminal diphenylamines, the resulting molecular HTMs, i.e., 2,7-BCzA4CF_(3) and 2,7-BCzA4OCCF_(3), show distinct properties. Compared with 2,7-BCzA4CF_(3), the nonconjugated alkoxyl bridging −CF_(3) group-based 2,7-BCzA4OCCF_(3) exhibits better thermal stability, hydrophobicity, and a dramatically upgraded hole mobility by 135.7-fold of magnitude to 1.71 × 10^(−4) cm^(2) V^(−1) S^(−1). The PSCs with 2,7-BCzA4OCCF_(3) as HTM exhibit an PCE of up to 20.53% and excellent long-term stability, maintaining 92.57% of their performance for 30 days in air with humidity of 30% without encapsulation. This work provides beneficial guidelines for the design of new HTMs for efficient and stable PSCs.展开更多
文摘In indoor design innovation, the material role can not be ignored. In indoor design, using non-conventional decoration materials can make space more personalized and charming. This is one of the material innovation modes and also one of the indoor design innovation modes. The design method should obtain more attention.
基金The Programme of Introducing Talents of Discipline to Universities(No.111-2-13)the Project of the State Key Laboratory of Subtropical Building Science of South China University of Technology(No.200833)
文摘The influence of a polyvinyl chloride（PVC）-panel on the cooling load of a residential apartment in Mashad,Iran,is analyzed by the DeST-h software.And the summer natural ventilation of the residential apartment is investigated to determine the wind speed into the apartment through the computational fluid dynamics software.The evaluation results of the indoor wind velocity show that most parts of the apartment are comfortable.The cooling load of the penthouse can be decreased about 10.5% or 6.5% when an air layer exists or does not exist between the ceiling and the PVC-panel,respectively,indicating that the existence of the air layer can decrease the cooling load.However,the effect of the increase in the air layer＇s thickness on the decrease in the cooling load is obvious.Adding a thin layer of air between the ceiling and the PVC-panel is a good step toward sustainable buildings.
文摘In this paper,both oxidation and corrosion resistance of low-carbon magnesia-carbon materials containing 4.0wt% graphite with metallic Al and Mg-Al alloy powders as antioxidants were investigated.Meanwhile,the microstructures of samples corroded by slag were observed with optical microscope as well.The test results revealed the properties of oxidation and corrosion resistance of low-carbon magnesia-carbon materials could be improved obviously by adding metal Al powder and Mg-Al alloy powder.The rule of improving oxidation resistance was illegibility when metal Al powder and Mg-Al alloy powder were added together.It was harmful to corrosion resistance by mixed adding metal Al powder and Mg-Al alloy powder into the materials,at the same time,the corrosion resistance would decreased with the increasing of Mg-Al alloy content.The corrosion resistance of samples with 0.5wt% or 3.0wt% Mg-Al alloy was better. The oxidation resistance and corrosion resistance of materials with metal Al or Mg-Al alloy respectively were better than that with mixed metal Al and Mg-Al alloy. As a result, Mg-Al alloy was more suitable for low-carbon composite materials than metal Al as additives.
文摘Effects of Al- Si addition on hot modulus of rup- ture ~ HMOR） . thermal shock resistance ~ TSR~ . phase composition and mierostructure of low-carbon MgO - C materials were investigated. The results show that： Al and Si addition to low-carbon MgO - C materials leads to dramatic increase in MOR at elevated temperatures; it increases from 4 MPa to 11 -21 MPa at 1 200 ℃ and from 2 MPa to 21 -29 MPa at 1 400 ℃. Al and Si addition to low-carbon MgO - C materials also improves TSR： residual strength ratio after thermal shock when △T = 1 200 ℃ is increased,from 44% to 73% - 77%. Al reacts with C and N2 to form, Al4C3 and AlN, Si reacts with C to form SiC. Ultimately. in-situ formed non- oxides increase appreciably with temperature rising and are well interlaced in periclase skeleton structure at 1 300 -1 400 ℃. which is beneficial to thermomechanical properties.
文摘In this paper ,the influence of ZnO and BaO contents on sintering and crystallization of decorative materi-al in the system of CaO-Al2O3-SiO2wwas studied. The opti-mum ZnO 9 BaO contents and sintering or crystallization tem-perature for the glass-ceramic were determined.
基金This work was financially supported by the National Natural Science Foundation of China(62074095)the Fundamental Research Funds for the Central Universities(GK202002001).
文摘The hole transport material (HTM) plays an extremely important role to determine the power conversion efficiency (PCE) and the stability of perovskite solar cells (PSCs). Herein, we report an effective strategy to improve the performance of HTMs by introducing −CF_(3) groups via the rational decorative mode. Upon direct attachment or nonconjugated alkoxyl bridging of −CF_(3) groups on the terminal diphenylamines, the resulting molecular HTMs, i.e., 2,7-BCzA4CF_(3) and 2,7-BCzA4OCCF_(3), show distinct properties. Compared with 2,7-BCzA4CF_(3), the nonconjugated alkoxyl bridging −CF_(3) group-based 2,7-BCzA4OCCF_(3) exhibits better thermal stability, hydrophobicity, and a dramatically upgraded hole mobility by 135.7-fold of magnitude to 1.71 × 10^(−4) cm^(2) V^(−1) S^(−1). The PSCs with 2,7-BCzA4OCCF_(3) as HTM exhibit an PCE of up to 20.53% and excellent long-term stability, maintaining 92.57% of their performance for 30 days in air with humidity of 30% without encapsulation. This work provides beneficial guidelines for the design of new HTMs for efficient and stable PSCs.