Low-cycle fatigue behavior of solutionized and aged WE43 magnesium alloys at room temperature

The low-cycle fatigue behavior of solutionized(T4)and aged(T6)WE43 magnesium alloys was studied at room temperature.The total strain amplitudes(△ε_(t)/2)were 0.4%,0.5%,0.6%,0.7%and 1.0%.Detailed microstructure evolution was characterized by scanning electron microscope(SEM),electron backscattered diffraction(EBSD)and transmission electron microscopy(TEM).The results showed that plastic strain amplitude decreased with the increasing cycle number in T4 alloy,which is due to the dense persistent slip bands(PSBs)and dynamic precipitates hinderingdislocation slip.In contrast,the plastic strain amplitude increases gradually in T6 alloy,which is attributed to the enhanced activation of pyramidal slip.The low-cycle fatigue life of T6 alloy with larger fatigue ductility coefficient is longer than that of T4 alloy.The Coffin-Manson model can accurately predict the fatigue life of T4 and T6 alloys compared to Jahed-Varvani(JV)energy model.For T4 alloy,the fatigue damage mechanism was dominated by basal slip.For T6 alloy,the enhanced pyramidal slip plays an important role to accommodate plastic deformation.

Microstructural characteristics and low-cycle fatigue properties of AZ91 and AZ91-Ca-Y alloys extruded at different temperatures

The commercial AZ91 alloy and nonflammable SEN9(AZ91-0.3Ca-0.2Y,wt%)alloy are extruded at 300°C and 400°C.Their microstructure,tensile and compressive properties,and low-cycle fatigue(LCF)properties are investigated,with particular focus on the influence of the extrusion temperature.In the AZ91 and SEN9 materials extruded at 300°C(300-materials),numerous fine Mg_(17)Al_(12)particles are inhomogeneously distributed owing to localized dynamic precipitation during extrusion,unlike those extruded at 400°C(400-materials).These fine particles suppress the coarsening of recrystallized grains,decreasing the average grain size of 300-materials.Although the four extruded materials have considerably different microstructures,the difference in their tensile yield strengths is insignificant because strong grain-boundary hardening and precipitation hardening effects in 300-materials are offset almost completely by a strong texture hardening effect in 400-materials.However,owing to their finer grains and weaker texture,300-materials have higher compressive yield strengths than400-materials.During the LCF tests,{10-12}twinning is activated at lower stresses in 400-materials than in 300-materials.Because the fatigue damage accumulated per cycle is smaller in 400-materials,they have longer fatigue lives than those of 300-materials.A fatigue life prediction model for the investigated materials is established on the basis of the relationship between the total strain energy density(ΔW_(t))and the number of cycles to fatigue failure(N_(f)),and it is expressed through a simple equation(ΔW_(t)=10·N_(f)-0.59).This model enables fatigue life prediction of both the investigated alloys regardless of the extrusion temperature and strain amplitude.

Experimental study on uniaxial ratchetting-fatigue interaction of extruded AZ31 magnesium alloy with different plastic deformation mechanisms

The uniaxial ratchetting-fatigue interaction of extruded AZ31 magnesium(Mg)alloy is investigated by uniaxial stress-controlled cyclic tests at room temperature and with addressing the roles of different plastic deformation mechanisms.Different stress levels are prescribed to reflect the cyclic plasticity of the alloy controlled by diverse deformation mechanisms(i.e.,dislocation slipping,deformation twinning and detwinning ones),and then the influences of stress level and stress rate on the ratchetting and fatigue life are discussed.The experimental results demonstrate that different evolution characteristics of whole-life ratchetting and fatigue life presented during cyclic tests with various mean stresses,stress amplitudes and stress rates are determined by the dominated plastic deformation mechanisms.It’s worth noting that the ratchetting can occur in the compressive direction even in the cyclic tests with a positive(tensile)mean stress,and the fatigue life increases first and then decreases with the increase of mean stress on account of the interaction between dislocation slipping and twinning/detwinning mechanisms.Comparing the fatigue lives obtained in the asymmetric stress-controlled and symmetrical strain-controlled cycle tests,it is seen that the ratchetting deformation causes an additional damage,and then leads to a shortening of fatigue life.

Performances of fissured red sandstone after thermal treatment with constant-amplitude and low-cycle impacts

In the engineering practices,it is increasingly common to encounter fractured rocks perturbed by temperatures and frequent dynamic loads.In this paper,the dynamic behaviors and fracture characteristics of red sandstone considering temperatures(25℃,200℃,400℃,600℃,and 800℃)and fissure angles(0°,30°,60°,and 90°)were evaluated under constant-amplitude and low-cycle(CALC)impacts actuated by a modified split Hopkinson pressure bar(SHPB)system.Subsequently,fracture morphology and second-order statistics within the grey-level co-occurrence matrix(GLCM)were examined using scanning electron microscopy(SEM).Meanwhile,the deep analysis and discussion of the mechanical response were conducted through the synchronous thermal analyzer(STA)test,numerical simulations,one-dimensional stress wave theory,and material structure.The multiple regression models between response variables and interactive effects of independent variables were established using the response surface method(RSM).The results demonstrate the fatigue strength and life diminish as temperatures rise and increase with increasing fissure angles,while the strain rate exhibits an inverse behavior.Furthermore,the peak stress intensification and strain rate softening observed during CALC impact exhibit greater prominence at increased fissure angles.The failure is dominated by tensile damage with concise evolution paths and intergranular cracks as well as the compressor-crushed zone which may affect the failure mode after 400℃.The second-order statistics of GLCM in SEM images exhibit a considerable dependence on the temperatures.Also,thermal damage dominated by thermal properties controls the material structure and wave impedance and eventually affects the incident wave intensity.The tensile wave reflected from the fissure surface is the inherent mechanism responsible for the angle effect exhibited by the fatigue strength and life.Ultimately,the peak stress intensification and strain rate softening during impact are determined by both the material structure and compaction governed by thermal damage and tensile wave.

Effect of Hot Deformation on Formation and Growth of Thermal Fatigue Crackin Chromium Wear Resistant Cast Iron

The formation and growth of thermal fatigue crack in chromium wear resistant cast iron was investigated, and the effect of hot deformation on the crack was analyzed by means of optical microscope and scanning electron microscope and high frequency induction thermal fatigue tester. The results show that eutectic carbide is the main location and passage for initiation and extension of thermal fatigue cracks, hot deformation can improve the eutectic carbiders morphology and distribution, inhibit the generation and propagation of thermal fatigue cracks. In the experiment, the propagation rate of thermal fatigue crack reduces with the quantity of hot deformation increasing, which was analyzed in the point view of the activation energy of crack propagation.

Microstructure evolution during heat treatment of Mg-Gd-Y-Zn-Zr alloy and its low-cycle fatigue behavior at 573K

In as-cast Mg?2.1Gd?1.1Y?0.82Zn?0.11Zr(mole fraction,%)alloy,lamellar microstructures that extend from grain boundaries to the interior ofα-Mg grains are identified as clusters ofγ′using a scanning transmission electron microscope equipped with a high-angle annular dark-field detector.Under a total strain-controlled low-cyclic loading at573K,the mechanical response and failure mechanism of Mg?2.1Gd?1.1Y?0.82Zn?0.11Zr alloy(T6peak-aging heat treatment)were investigated.Results show that the alloy exhibits cyclic softening response at diverse total strain amplitudes and573K.The experimental observations using scanning electron microscopy show that the micro-cracks initiate preferentially at the interface between long-period stacking order structures andα-Mg matrix and extend along the basal plane ofα-Mg.The massive long-period stacking order structures distributed at grain boundaries impede the transgranular propagation of cracks.

Low-cycle fatigue behavior of permanent mold cast and die-cast Al-Si-Cu-Mg alloys

Fatigue failure is one of the main failure forms of Al-Si-Cu-Mg aluminum alloys. To feature their mechanical aspect of fatigue behavior, the low-cycle fatigue behavior of permanent mold cast and die-cast AI-Si- Cu-Mg alloys at room temperature was investigated. The experimental results show that both permanent mold cast and die-cast AI-Si-Cu-Mg alloys mainly exhibit cyclic strain hardening. At the same total strain amplitude, the diecast AI-Si-Cu-Mg alloy shows higher cyclic deformation resistance and longer fatigue life than does the permanent mold cast AI-Si-Cu-Mg alloy. The relationship between both elastic and plastic strain amplitudes with reversals to failure shows a monotonic linear behavior, and can be described by the Basquin and Coffin-Manson equations, respectively.

Mechanical and low-cycle fatigue behavior of stainless reinforcing steel for earthquake engineering applications

Use of stainless reinforcing steel （SRS） in reinforced concrete （RC） structures is a promising solution to corrosion issues. However, for SRS to be used in seismic applications, several mechanical properties need to be investigated. These include specified and actual yield strengths, tensile strengths, uniform elongations and low-cycle fatigue behavior. Three types of SRSs （Talley S24100, Talley 316LN and Talley 2205） were tested and the results are reported in this paper. They were compared with the properties of A706 carbon reinforcing steel （RS）, which is typical for seismic applications, and MMFX II, which is a high strength, corrosion resistant RS. Low-cycle fatigue tests of the RS coupons were conducted under strain control with constant amplitude to obtain strain life models of the steels. Test results show that the SRSs have slightly lower moduli of elasticity, higher uniform elongations before necking, and better low-cycle fatigue performance than A706 and MMFX II. All five types of RSs tested satisfy the requirements of the ACI 318 code on the lower limit of the tensile to yield strength ratio. Except Talley 2205, the other four types of RSs investigated meet the ACI 318 requirement that the actual yield strength does not exceed the specified yield strength by more than 18 ksi （124 MPa）. Among the three types of SRSs tested, Talley S24100 possesses the highest uniform elongation before necking, and the best low-cycle fatigue performance.

CYCLIC SOFTENING IN HOT-WORKING DIE STEELS DURING LOW-CYCLE FATIGUE

The characteristics and microstructural changes of cyclic softening in hot-working die steels 5CrNiMo and 5Cr2NiMoVSi were studied under strain controlled low-cycle fatigue.The re- sults show that the cyclic softening is featured in both steels hardened in different conditions under the strain controlled amplitude range of Δε_t/2=0.6-1.8×10^(-2).The softening effect mainly occurs in some initial cycles and the stress amplitude varies slightly in the sequential cycles,i.e.the softening effect is minified.No obvious stress saturation phenomenon was ob- served during the whole cyclic deformation.The TEM analysis shows that the cyclic softening is related to heterogenity of plastic deformation.The softening of the tested steels is caused by the formation of the dislocation cell structure with low density and low internal stress,and by the fragmentation and redissolution of fine carbides into matrix.

Low-cycle fatigue behavior of K416B Ni-based superalloy at 650 ℃

A study on the low-cycle fatigue(LCF)behavior of K 416 B alloy was conducted at 650℃.According to the results,the LCF behavior of K 416 B alloy at 650℃ is mainly manifested as elastic deformation and the fatigue life of the alloy is determined by the level of material strength.When tension-compression fatigue occurs,the deformation mechanism of the alloy is reflected in the form of dislocation slip,and the deformation dislocations are bowed out in the matrix by Orowan mechanism,which leads to a dislocation configuration similar to the Frawk-Reed source.At the late stage of low-cycle fatigue,the fatigue-induced cracks develop from the alloy surface.As fatigue test proceeds,it is possible for the cracks to continue development along the regions of eutectic and the bulk M 6 C carbide due to stress concentration,thus causing the alloy to show cleavage fracture.

A NEW CYCLIC J-INTEGRAL FOR LOW-CYCLE FATIGUE CRACK GROWTH

The constitutive equation under the low-cycle fatigue （LCF） was discussed, and a two-dimensional （2-D） model for simulating fatigue crack extension was put forward in order to propose a new cyclic J-integral. The definition, primary characteristics, physical interpretations and numerical evaluation of the new parameter were investigated in detail. Moreover, the new cyclic J-integral for LCF behaviors was validated by the compact tension （CT） specimens. Results show that the calculated values of the new parameter can correlate well with LCF crack growth rate, during constant-amplitude loading. In addition, the phenomenon of fatigue retardation was explained through the viewpoint of energy based on the concept of the new parameter.

INVESTIGATION OF THE LOW-CYCLE FATIGUE AND FATIGUE CRACK GROWTH BEHAVIORS OF P91 BASE METAL AND WELD JOINTS

Low cycle fatigue tests and crack growth propagations tests on P91 pipe base metal and its weld joints were conducted at three different temperatures: room temperature, 550℃ and 575℃. The strain-life was analyzed, and the changes in fatigue life behavior and fatigue growth rates with increasing temperature were discussed. The different properties of the base metal and its weld joint have been analyzed.

IN SITU OBSERVATION OF DEFORMATION AND FRACTURE FOR SUPERALLOY GH169 UNDER COMBINED FATIGUE-CREEP ACTION

In Situ observation of deformation and fracture for superalloy GH169 under combined fatigue-creep action is made by using high temperature metalloscope,it is shown that under the test conditions the deformution takes place by merely of slipping,twinning and grain houndary sliding,and the mode of failure depends on the microstructure of specimen. lntergranular cracks arise.from W-type voids produced by the stress concentration at triple point which could not be relaxed by the interior deformation of grains and the local deformathm region along grain bounaries.And the crack propagation mechanism is the nucleation,growth and linkage of carities at the grain boundaries.Transgranular cracks form from deformatiom damages within the grain,and its propagation mechanism is shear rupture along the slip phme.

Research on Facial Fatigue Detection of Drivers with Multi-feature Fusion

In order to solve the shortcomings of current fatigue detection methods such as low accuracy or poor real-time performance,a fatigue detection method based on multi-feature fusion is proposed.Firstly,the HOG face detection algorithm and KCF target tracking algorithm are integrated and deformable convolutional neural network is introduced to identify the state of extracted eyes and mouth,fast track the detected faces and extract continuous and stable target faces for more efficient extraction.Then the head pose algorithm is introduced to detect the driver’s head in real time and obtain the driver’s head state information.Finally,a multi-feature fusion fatigue detection method is proposed based on the state of the eyes,mouth and head.According to the experimental results,the proposed method can detect the driver’s fatigue state in real time with high accuracy and good robustness compared with the current fatigue detection algorithms.

Low-Cycle Fatigue Crack Initiation Behavior of Nickel-Based Single Crystal Superalloy

Low-cycle fatigue crack initiation behavior of nickel-based single crystal superalloy at 530℃ was investigated.Results show that the behavior of crack initiation is closely related to the maximum strain.When the maximum strain is 2.0%,the fatigue crack is originated at the position of persistent slip bands on the surface of specimen,which is located on the{111}slip plane.No defects are observed at the crack initiation position.When the maximum strain is lower than 1.6%,the cracks are initiated at the casting defects on sub-surface or at interior of the specimen.The casting defects are located on the{100}slip plane vertical to the axial force.The crack is initiated along the{100}slip plane and then expanded along different{111}slip planes after a short stage of expansion.As the maximum strain decreases,the position of crack initiation gradually changes from the surface to the interior.Moreover,the secondary cracks extending inward along the fracture surface appear in the crack initiation area,and there is obvious stress concentration near the secondary cracks.The dislocation density is high near the fracture surface in the crack initiation zone,where a lot of dislocations cutting into the γ'phase exist.An oxide layer of 50‒100 nm is presented on the fracture surface,and Ni,Al,Cr and Co elements are mainly segregated into the oxide layer of the surface.

Study on the Thermal Fatigue Behavior of Hot Deformed Wear Resistance Cast Iron and Effect of Carbide

The thermal fatigue behavior of wear resistance cast iron with different quantity of deformation has been investigated. The results show that eutectic carbide is the main location and passage for initiation and extension of thermal fatigue cracks, approving that the more serious, the carbide breaks. The higher thermal fatigue resistance of wear resistance cast iron will be and thermal fatigue fracture belongs mainly to brittleness.

DEFORMATION AND FRACTURE OF TiAl PST CRYSTALS UNDER MONOTONIC AND CYCLIC LOADING

Plastic behaviour of TiAl polysynthetically twinned (PST) crystals is reviewed to show our knowledge and understanding for receiving a good combination of strength and ductility of two phase TiAl alloys under monotonic and cyclic loading conditions. Anisotropy and mechanism of strength, ductility, toughness. cyclic hardening and fatigue life are described focusing on the effect of lamellar structure.

Analysis of meso-inhomogeneous deformation on a metal material surface under low-cycle fatigue

A polycrystalline Voronoi aggregation with a free surface is applied as the representative volume element（RVE）of the nickel-based GH4169 superalloy.Considering the plastic deformation mechanism at the grain level and the Bauschinger effect,a crystal plasticity model reflecting the nonlinear kinematic hardening of crystal slipping system is applied.The microscopic inhomogeneous deformation during cyclic loading is calculated through numerical simulation of crystal plasticity.The deformation inhomogeneity on the free surface of the RVE under cyclic loading is described respectively by using the following parameters：standard deviation of the longitudinal strain in macro tensile direction,statistical average of first principal strains,and standard deviation of longitudinal displacement.The relationship between the fatigue cycle number and the evolution of inhomogeneous deformation of the material’s free surface is investigated.This research finds that：（1）The inhomogeneous deformation of the material free surface is significantly higher than that of the RVE inside;（2）the increases of the characterization parameters of inhomogeneous deformation on the free surface with cycles reflect the local maximum deformation of the RVE growing during cyclic loading;（3）these parameters can be used as criteria to assess and predict the low-cycle fatigue life rationally.

Evolution characteristics of microstructure and properties in AZ31 alloy during high cycle fatigue processes

In order to investigate the microstructure and properties evolution of the AZ31magnesium alloy in different cycles(including104(sample1),106(sample2)and none(sample3,no fatigue tests on the samples))of high cycle deformation,thescanning electron microscopy(SEM)and electron back-scattered diffraction technique(EBSD)were fully used.It is found that many{1012}tension twins(near21%,volume fraction),a few{1011}compression twins and{1011}?{1012}secondary twins aregenerated during tension?compression cyclic deformation.The volume fractions of{1012}twins in samples1,2and3are8%,21%and4%,respectively.By analyzing the fatigue fracture of the samples,larger area of fatigue striations and cleavage fracture insamples are also observed,as well as the shallower dimples.The twin laminae are likely to occur in the crack initiation zone whiledimples are in the final fracture region and the dimple size increases with the increase of the cycle number.The dimple diameters ofsamples1,2and3are14.8,31.2and8.5μm,respectively.It turns out that both the fatigue strength and elongation of the samplesslightly decrease with increasing the cycle number.