This study was to develop the flame retardant (FR) protective clothing which had multifunction such anti-bacterial, UV cut, FR function with water repellent and water vapor permeable laminating textiles for industrial...This study was to develop the flame retardant (FR) protective clothing which had multifunction such anti-bacterial, UV cut, FR function with water repellent and water vapor permeable laminating textiles for industrial workers. First of all, the FR yarn and FR textiles were developed for this purpose. Second, the comparison analysis between the halogen laminating textiles and halogen-free laminating textiles were tested to figure out the eco-friendly laminating method. Third, the flame retardant ability was compared the halogen laminated textiles to halogen-free laminated textiles. LOI, UV protection ratio, antibiosis after 50 laundry test, water proof pressure, and moisture permeability of developed textiles were tested. GC-HR-TOF-MS was used for analysis of laminating film (halogen and halogen-free). 4.1 wt% TiO2 yarn showed antibacterial function (Pneumococcus & Staphylococcus aureus: 99.9%), UV Protection (UVA: 90.8, UVB: 92.1), and LOI (33.6). The chosen optimal compounding ratio for PU compound of HRF and HFFR were as followed: PU resin 58.3%, DMF (Dimethyl formamide, δ = 12.2) 8.3%, MEK (Methylethylketone) 8.3% and FR (flame retardants) 25.0%. Binder for laminating should not be included over 10% of FRs because of adhesion between textiles and FR laminating film. There were detected phosphorus compounds in the textiles treated by halogenated type flame retardants and halogenated-free type flame retardants. There were not any detected harmful compounds from all textile samples.展开更多
To study the effects of different proportions of aluminum hydroxide and expandable graphite (EG) composites on flame retardation, sealing, mechanical, electrical and other properties of RTV- 1, aluminum hydroxide/ex...To study the effects of different proportions of aluminum hydroxide and expandable graphite (EG) composites on flame retardation, sealing, mechanical, electrical and other properties of RTV- 1, aluminum hydroxide/expandable graphite (ATH/EG) and silicone rubber composites were prepared by the compression molding method. The experimental results show that heat resistance improves with the increase of proportion of EG. Although the resistance coefficient changes, the composite materials still keep good electrical insulating property. Moreover, oxygen index and expansion index rise first then fall. When ATH/EG is 1:1, the oxygen index reaches the highest; the mechanical property of the silicone rubber is not affected under various environments such as acid, alkali, oily, artificial sea water environments, etc.展开更多
Bisphenol A bis(diphenyl phosphate) oligomer(BDP) is prepared successfully from the reactants consisting of phosphorus oxyehloride (POCl3), bisphenol A and phenol with a Friedel-Crafts catalyst. The resultant pr...Bisphenol A bis(diphenyl phosphate) oligomer(BDP) is prepared successfully from the reactants consisting of phosphorus oxyehloride (POCl3), bisphenol A and phenol with a Friedel-Crafts catalyst. The resultant products were examined with thermtygravimetrie analysis (TGA) and high performance liquid chro- matography(HPLC). Thermogravimetry data shows that BDP decomposes at 375℃ when 5 % weight lost. Experiments results show that catalyst is preferably AICI3 and the amount of it is preferably 1% relative to bisphenol A by mole. POCl3/bisphenol A mole ratio is preferably about 5:1 to 6:1. Experiments unclosed that a seal apparatus is very important to the properties of product.展开更多
Driven by global environmental concerns,many efforts have been made to develop halogen-free flame retardants for rigid polyurethane foam(RPUF).These environmentally benign flame retardants are mainly divided into(i)re...Driven by global environmental concerns,many efforts have been made to develop halogen-free flame retardants for rigid polyurethane foam(RPUF).These environmentally benign flame retardants are mainly divided into(i)reactive,(ii)additive,and(iii)coating types.The last decade has witnessed great progress of these three strategies,which enhance the fire safety of RPUF and maintain even improve the thermal insulation properties.This comprehensive review focuses on the up-to-date design of the reactive,additive,and coating flame retardants,and their effects on flame retardancy and thermal conductivity of RPUF.Moreover,the practical applications of the as-prepared flame-retardant RPUFs are highlighted.Finally,key challenges associated with these three kinds of flame retardants are discussed and future research opportunities are also proposed.展开更多
文摘This study was to develop the flame retardant (FR) protective clothing which had multifunction such anti-bacterial, UV cut, FR function with water repellent and water vapor permeable laminating textiles for industrial workers. First of all, the FR yarn and FR textiles were developed for this purpose. Second, the comparison analysis between the halogen laminating textiles and halogen-free laminating textiles were tested to figure out the eco-friendly laminating method. Third, the flame retardant ability was compared the halogen laminated textiles to halogen-free laminated textiles. LOI, UV protection ratio, antibiosis after 50 laundry test, water proof pressure, and moisture permeability of developed textiles were tested. GC-HR-TOF-MS was used for analysis of laminating film (halogen and halogen-free). 4.1 wt% TiO2 yarn showed antibacterial function (Pneumococcus & Staphylococcus aureus: 99.9%), UV Protection (UVA: 90.8, UVB: 92.1), and LOI (33.6). The chosen optimal compounding ratio for PU compound of HRF and HFFR were as followed: PU resin 58.3%, DMF (Dimethyl formamide, δ = 12.2) 8.3%, MEK (Methylethylketone) 8.3% and FR (flame retardants) 25.0%. Binder for laminating should not be included over 10% of FRs because of adhesion between textiles and FR laminating film. There were detected phosphorus compounds in the textiles treated by halogenated type flame retardants and halogenated-free type flame retardants. There were not any detected harmful compounds from all textile samples.
文摘To study the effects of different proportions of aluminum hydroxide and expandable graphite (EG) composites on flame retardation, sealing, mechanical, electrical and other properties of RTV- 1, aluminum hydroxide/expandable graphite (ATH/EG) and silicone rubber composites were prepared by the compression molding method. The experimental results show that heat resistance improves with the increase of proportion of EG. Although the resistance coefficient changes, the composite materials still keep good electrical insulating property. Moreover, oxygen index and expansion index rise first then fall. When ATH/EG is 1:1, the oxygen index reaches the highest; the mechanical property of the silicone rubber is not affected under various environments such as acid, alkali, oily, artificial sea water environments, etc.
文摘Bisphenol A bis(diphenyl phosphate) oligomer(BDP) is prepared successfully from the reactants consisting of phosphorus oxyehloride (POCl3), bisphenol A and phenol with a Friedel-Crafts catalyst. The resultant products were examined with thermtygravimetrie analysis (TGA) and high performance liquid chro- matography(HPLC). Thermogravimetry data shows that BDP decomposes at 375℃ when 5 % weight lost. Experiments results show that catalyst is preferably AICI3 and the amount of it is preferably 1% relative to bisphenol A by mole. POCl3/bisphenol A mole ratio is preferably about 5:1 to 6:1. Experiments unclosed that a seal apparatus is very important to the properties of product.
基金financially supported by the Australian Research Council(Nos.DP190102992,FT190100188)the National Natural Science Foundation of China(No.51873196)the Key Research and Development Projects of Zhejiang Province(No.2019C01098)。
文摘Driven by global environmental concerns,many efforts have been made to develop halogen-free flame retardants for rigid polyurethane foam(RPUF).These environmentally benign flame retardants are mainly divided into(i)reactive,(ii)additive,and(iii)coating types.The last decade has witnessed great progress of these three strategies,which enhance the fire safety of RPUF and maintain even improve the thermal insulation properties.This comprehensive review focuses on the up-to-date design of the reactive,additive,and coating flame retardants,and their effects on flame retardancy and thermal conductivity of RPUF.Moreover,the practical applications of the as-prepared flame-retardant RPUFs are highlighted.Finally,key challenges associated with these three kinds of flame retardants are discussed and future research opportunities are also proposed.