Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS...Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS and XRD techniques.Compact,uniform,and medium-phosphorus Ni-P coating with mixed crystalline-amorphous microstructure was obtained by applying a cathodic current density of4mA/cm^2at50℃.Also,island-like nickel clusters were deposited on the alloy surface under the same plating condition but without applying the cathodic current.In addition,the durability of the magnesium alloy against corrosion was strongly improved after plating via EPEP technique which was revealed by electrochemical examinations in3.5%NaCl(mass fraction)corrosive electrolyte.The results of the electrochemical examinations were confirmed by microscopic observations.Thickness,microhardness,porosity and adhesive strength of the deposits were also qualified.展开更多
The cavitation-erosion behavior of (Ti,Cr)N multi-component coatings produced by arcion-plating on grey cast iron was studied by using an ultrasonic cavitation -erosion testing appara-tus and scanning electron microsc...The cavitation-erosion behavior of (Ti,Cr)N multi-component coatings produced by arcion-plating on grey cast iron was studied by using an ultrasonic cavitation -erosion testing appara-tus and scanning electron microscopy. The test results indicated that surface roughness of thesubstrate, surface morphology of the coating, substrate bias voltage and the thickness of the coat-ing had certain influence on the erosion rate. Arc ion-plated (Ti,Cr)N multi-component coatingsshowed better cavitation -erosion resistance than single component coatings because of highermicrohardness and good adhesion.展开更多
文摘Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS and XRD techniques.Compact,uniform,and medium-phosphorus Ni-P coating with mixed crystalline-amorphous microstructure was obtained by applying a cathodic current density of4mA/cm^2at50℃.Also,island-like nickel clusters were deposited on the alloy surface under the same plating condition but without applying the cathodic current.In addition,the durability of the magnesium alloy against corrosion was strongly improved after plating via EPEP technique which was revealed by electrochemical examinations in3.5%NaCl(mass fraction)corrosive electrolyte.The results of the electrochemical examinations were confirmed by microscopic observations.Thickness,microhardness,porosity and adhesive strength of the deposits were also qualified.
文摘The cavitation-erosion behavior of (Ti,Cr)N multi-component coatings produced by arcion-plating on grey cast iron was studied by using an ultrasonic cavitation -erosion testing appara-tus and scanning electron microscopy. The test results indicated that surface roughness of thesubstrate, surface morphology of the coating, substrate bias voltage and the thickness of the coat-ing had certain influence on the erosion rate. Arc ion-plated (Ti,Cr)N multi-component coatingsshowed better cavitation -erosion resistance than single component coatings because of highermicrohardness and good adhesion.
