Property alterations of Sn-0.6Cu-0.05Ni-Ge lead-free solder by Ag, Bi, In and Sb addition

The Sn-Cu-Ni-Ge solder is a strong challenger to the Sn-Ag-Cu（SAC） solders as a replacement for the Sn-Pb eutectic solder. This research investigated the effects of addition of Ag, Bi, In, and Sb on the physical properties of the Sn-0.6 Cu-0.05 Ni-Ge（SCNG） lead-free solder and the interfacial reaction with the Cu substrate. The melting behavior, microstructure, tensile strength, and wettability of the SCNG-x（x=Ag, Bi, In, Sb） solders were examined. The findings revealed that the introduction of Ag, Bi, In, and Sb minimally altered the solidus temperature, liquidus temperature, and tensile strength of the solder. However, the cooling behavior and solidified microstructure of the solder were affected by the concentration of the alloying elements. The wettability of the SCNG solder was improved with the doping of the alloying elements except Sb. The thickness of intermetallic layer was increased by the addition of the alloying elements and was related to the cooling behavior of the solder. The morphology of intermetallic layer between the SCNG-x solders and the Cu substrate was different from that of the typical SAC solders. In conclusion, alloying the SCNG solder with Ag, Bi, In or Sb is able to improve particular properties of the solder.

Influence of Cu content on microstructure,grain orientation and mechanical properties of Sn-xCu lead-free solders

The effect of Cu content on the microstructure,grain orientation and mechanical properties of Sn-xCu(x=0-4.0 wt.%)lead-free solder was studied.Results showed that added Cu induced the formation of intermetallic phases.Only theη-Cu;Sn;andε-Cu;Sn phases were present in theβ-Sn matrix.For all contents,the strongly preferred orientation of theβ-Sn phase was formed on the{001}plane.In Sn doped with 1.0 wt.%Cu,theη-Cu;Sn;phase exhibited the preferred orientation of{0001}plane,whereas doping with 3.0 or 4.0 wt.%Cu transformed the preferred orientation to the{010}plane.In addition,only the{0001}and{■}planes were present in theε-Cu;Sn phase.The high Cu contents contributed to an increased number of low-angle boundaries,high residual strain,tensile strength and microhardness.

Electromotive force measurements in liquid Ag-In-Pd lead-free alloys

Emf technique was employed to determine indium activities in the liquid Ag-In-Pd alloys using galvanic cells with yttria-stabilised-zirconia as solid electrolyte according to the scheme： kanthal/rhenium, Ag-In-Pd, In2O3 ｜ YSZ ｜ Ni, NiO, Pt. Composition and temperature measurement ranges were limited, because of very steep liquidus surface; 35 compositions for Xpd up to 0.3 were investigated and at temperatures from near-liquidus up to 1700 K. High temperature experiments required special moly furnace to be constructed with unique automatic gas supply system for fumace winding protective atmosphere. Emf readings were taken and recorded by automatic data acquisition system. Linear dependence of emf on temperature was observed for all compositions investigated, and results were approximated by straight line equa- tions. Then In activities were calculated using well-known relations and taking into account correction for thermoelectric power between kanthal and platinum. Results are to be used along with other existing data to perform assessment of the ternary system under accord.

Effects of Ni-Doping on Microstructures and Properties of Zn-20Sn High-Temperature Lead-Free Solders

In the present work, the effect of Ni doping on the microstructures and properties of Zn-20 Sn high temperature lead-free solder has been investigated. Interestingly,Ni was present as the form of Ni-Zn compounds in the microstructure of Zn-20 Sn-xNi alloy.When the Ni-doping amount was 0.2~0.4 wt.%, the presence of δ phase was found, and when the doping amoun was 0.8 wt.%, the presence of γ phase was observed. With the increase of Ni content, the liquidus temperature increased but the solidus temperature did not change obviously. In addition, the microhardness and electrical resistivities of Zn-20 Sn-xNi solder increased gradually. And the spreading area and shear strength increased firstly but decreased afterwards. When the content of Ni was 0.4 wt.%, the spreading area and shear strength of solder reached to be maximum. After the addition of 0.4 wt.% Ni, the microstructure of the interfacial intermetallic compound(IMC) layer of the interface didn't change, but the total thickness of the IMC layer reduced. The δ-phase was embedded in the grain boundary of ε-Cu Zn5, which hindered the diffusion of atoms. The thickness of IMC layer at the interface reduced, which led to the improvement of the shear strength of the interface.

Structure and Properties of Sn-9Zn Lead-Free Solder Alloy with Heat Treatment

The Sn-9Zn lead-free solder alloy was prepared by conventional casting technique then cold-rolled into long sheets of 1 mm thickness and 3 mm width. It was annealed at 80, 120 and 160°C for 60 min to investigate the effect of isochronal heat treatment on structure and mechanical properties of the cold rolled Sn-9Zn alloy. The results showed that, the crystallite size and lattice strain have opposite behavior with increasing annealing temperature due to recovery and recrystalization processes associated with the heat treatment process. Vickers micro-hardness number increases continuously from 155 to 180 MPa with increasing annealing temperature. Ultimate tensile strength (UTS) was also calculated. It was found that, it is equal to 61.4 MPa for the non annealed sample and slightly decreases to 60.5 and 58.2 MPa for samples annealed at 80 and 120°C, respectively. While, increases to 65.4 MPa for the sample annealed at 160°C. Also, ductility increases with increasing annealing temperature in opposite manor with the UTS. The new method for Micro-creep behavior as well as the creep rate calculated by this method has been characterized at room temperature.

Solderability of Electrodeposited Fe-Ni Alloys with Eutectic SnAgCu Solder

Solderabilities of electrodeposited Fe-Ni alloys with SnAgCu solder were examined by wetting balance measurements and compared to those of pure Ni and pure Fe platings. Excellent solderability was found on the Ni-52Fe plating as both the wetting force and kinetics approached or exceeded those on the pure Ni. However, upon further increase in Fe content to 75 at. pct, the solderability of the alloy was severely degraded even though it was still better than that of the pure Fe plating. X-ray photoelectron spectroscopy showed that such a strong dependence of solderability on Fe content is related to the much thinner, incomplete oxide coverage of Ni-rich plating surface.

Interfacial reaction behavior and mechanical properties of 5A06 Al alloy soldered with Sn-1Ti-xGa solders at a low temperature

Active soldering of 5A06 Al alloy was performed at 300 ℃ by using Sn-1Ti and Sn-1Ti-0.3Ga active solders, respectively. Theeffects of soldering time on the microstructure and mechanical properties of the joints were investigated. The results showed that the Sn-1Tisolder broke the oxide film on the surface of the Al substrate and induced intergranular diffusion in the Al substrate. When Ga was added tothe solder, severe dissolution pits appeared in the Al substrate due to the action of Sn-1Ti-0.3Ga solder, and many Al particles were flakedfrom the matrix into the solder seam. Under thermal stress and the Ti adsorption effect, the oxide film cracked. With increasing solderingtime, the shear strength of 5A06 Al alloy joints soldered with Sn-1Ti and Sn-1Ti-0.3Ga active solders increased. When soldered for 90 min,the joint soldered with Sn-1Ti-0.3Ga solder had a higher shear strength of 22.12 MPa when compared to Sn-1Ti solder.

Effect of Sb content on properties of Sn-Bi solders

The effect of Sb content on the properties of Sn-Bi solders was studied. The nonequilibrium melting behaviors of a series of Sn-Bi-Sb solders were examined by differential scanning calorimetry （DSC）. The spreading test was carried out to characterize the wettability of Sn-Bi-Sb solders on Cu substrate. The mechanical properties of the solders/Cu joints were evaluated. The results show that the ternary alloy solders contain eutectic structure resulting from quasi-peritetic reaction. With the increase of Sb content, the amount of the eutectic structure increases. At a heating rate of 5 ℃/min, Sn-Bi-Sb alloys exhibit a higher melting point and a wider melting range. A small amount of Sb has an impact on the wettability of Sn-Bi solders. The reaction layers form during spreading process. Sb is detected in the reaction layer while Bi is not detected. The total thickness of reaction layer between solder and Cu increases with the increase of the Sb content. The shear strength of the Sn-Bi-Sb solders increases as the Sb content increases.

Preparation and Properties of Particle Reinforced Sn-Zn-based Composite Solder

Particle reinforced Sn-Zn based composite solders were obtained by adding Cu powders to Sn-9Zn melts. The microstructure analysis reveals that in situ CusZn8 particles are formed and distributed uniformly in the composite solders. The strength and plasticity of the composite solders were improved, and creep resistance was considerably enhanced. The wettability of these composite solders is also better than that of Sn-9Zn.

EFFECTS OF Zn CONCENTRATION ON WETTABILITY OF Sn-Zn ALLOY ON Cu AND ON THE INTERFACIAL MICROSTRUCTURE BETWEEN Sn-Zn ALLOY AND Cu

The potential of using a hypoeutectic, instead of eutectic, Sn-Zn alloy as a lead-free solder has been discussed. The nonequilibrium melting behaviors of a series of Sn-Zn alloys were examined by differential thermal analysis. It was found that at a heating rate of 5℃/min, Sn-6.SZn exhibited no melting range. Dipping and spreading tests were carried out to characterize the wettability of Sn-Zn alloys on Cu. Both tests exhibited that Sn-6.5Zn has significantly better wettability on Cu than Sn-9Zn. The reaction layers formed during the spreading tests were examined. When the Zn concentration fell between 2.5wt%-9wt%, two reaction layers were formed at the interface, a thick and flat Cu5Zn8 adjacent to Cu and a thin and irregular Cu-Zn-Sn layer adjacent to the alloy. Only a Cu0Sn5 layer was formed when the Zn concentration decreased to 0.5wt%. The total thickness of the reaction layer（s） between the alloy and Cu was found to increase linearly with the Zn concentration.