Three-dimensionally ordered macro-porous （3DOM） TiO2 and ceria-modified 3DOM TiO2 supported platinum catalysts were prepared with template and impregnation methods, and the resultant samples were characterized by sc...Three-dimensionally ordered macro-porous （3DOM） TiO2 and ceria-modified 3DOM TiO2 supported platinum catalysts were prepared with template and impregnation methods, and the resultant samples were characterized by scanning electron microscopy（SEM）, X-ray diffractometer（XRD）, high-resolution transmission electron microscopy（HRTEM） and temperature programmed reducfion（TPR） techniques. The catalytic performances over the platinum-based catalysts were investigated for water-gas shift （WGS） reaction in a wide temperature range （180-360 ℃）. The results showed that 3DOM Pt/TiO2 catalyst exhibited obviously better catalytic performance than the corresponding non macro-porous catalyst, owing to the macro-porous structure favoring mass transfer. Addition of celia into 3DOM Pt/TiO2 led to improvement of catalytic activity. TPR and HRTEM results showed that the interaction existed between ceria and titanium oxide and addition of ceria promoted the reducibility of platinum oxide and TiO2 on the interface of platinum and TiO2 particles, which contributed to high activity of the celia modified catalysts. The results indicated that ceria-modified 3DOM Pt/TiO2 was a promising candidate of fuel cell oriented WGS catalyst.展开更多
Three-dimensionally ordered macro-porous （3DOM） Pt/TiO2 catalysts were prepared by template and impregnation methods, and the resultant samples were characterized by using TG-DTA, XRD, SEM, TEM, and TPR techniques. ...Three-dimensionally ordered macro-porous （3DOM） Pt/TiO2 catalysts were prepared by template and impregnation methods, and the resultant samples were characterized by using TG-DTA, XRD, SEM, TEM, and TPR techniques. The catalytic performance for water-gas shift （WGS） reaction was tested, and the influences of some conditions, such as reduction temperature of catalysts, the amount of Pt loadings and space velocity on catalytic performance were investigated. It was shown that Pt particles were homogeneously dispersed on 3DOM TiO2. The reduction of TiO2 surface was important for the catalytic performance. The activity test results showed that the 3DOM Pt/TiO2 catalysts exhibited very good catalytic performance for WGS reaction even at high space velocity, which was owing to the better mass transfer of 3DOM porous structure besides the high intrinsic activity of Pt/TiO2.展开更多
A β-zeolite/polystyrene composite material was synthesized by co-deposition of mono-disperse polystyrene spheres and nano β-zeolite particles in aqueous suspension on a vertical substrate. Macro-porous β-zeolite wa...A β-zeolite/polystyrene composite material was synthesized by co-deposition of mono-disperse polystyrene spheres and nano β-zeolite particles in aqueous suspension on a vertical substrate. Macro-porous β-zeolite was obtained after the polystyrene template was removed by calcination. The micro/macro-pore structure of the prepared β-zeolite was highly ordered. In comparison with other assembly methods, the co-deposition method could obtain a highly ordered macro-porous material with relatively large zeolite filling particles, and therefore the co-deposition of particles with different size is a promising method for the fabrication of macro-porous materials.展开更多
Titania thin films with hierarchically macro-mesoporous were prepared by the addition of bulky organic molecule(1,3,5-trimethylbezenze) in aqueous solution of F127(EO106PO70EO106). After calcined at 673 K,ordered thin...Titania thin films with hierarchically macro-mesoporous were prepared by the addition of bulky organic molecule(1,3,5-trimethylbezenze) in aqueous solution of F127(EO106PO70EO106). After calcined at 673 K,ordered thin films with cubic meso-structure and macropores were formed. DNA(Cytochrome c) was used as probe to study the adsorption ability of macromolecules on this film. The hierarchically macro-mesoporous films show high adsorption ability of DNA molecules compared with conventional titania films and mesoporous titania films,which is attributed to the presence of macropores.展开更多
基金supported by the Ministry of Sciences and Technology of China (863 Programs) (2006AA05Z115, 2007AA05Z104)
文摘Three-dimensionally ordered macro-porous （3DOM） TiO2 and ceria-modified 3DOM TiO2 supported platinum catalysts were prepared with template and impregnation methods, and the resultant samples were characterized by scanning electron microscopy（SEM）, X-ray diffractometer（XRD）, high-resolution transmission electron microscopy（HRTEM） and temperature programmed reducfion（TPR） techniques. The catalytic performances over the platinum-based catalysts were investigated for water-gas shift （WGS） reaction in a wide temperature range （180-360 ℃）. The results showed that 3DOM Pt/TiO2 catalyst exhibited obviously better catalytic performance than the corresponding non macro-porous catalyst, owing to the macro-porous structure favoring mass transfer. Addition of celia into 3DOM Pt/TiO2 led to improvement of catalytic activity. TPR and HRTEM results showed that the interaction existed between ceria and titanium oxide and addition of ceria promoted the reducibility of platinum oxide and TiO2 on the interface of platinum and TiO2 particles, which contributed to high activity of the celia modified catalysts. The results indicated that ceria-modified 3DOM Pt/TiO2 was a promising candidate of fuel cell oriented WGS catalyst.
基金supported by the Ministry of Sciences and Technology of China(863 programs,No 2006AA05Z115 and 2007AA05Z104)
文摘Three-dimensionally ordered macro-porous （3DOM） Pt/TiO2 catalysts were prepared by template and impregnation methods, and the resultant samples were characterized by using TG-DTA, XRD, SEM, TEM, and TPR techniques. The catalytic performance for water-gas shift （WGS） reaction was tested, and the influences of some conditions, such as reduction temperature of catalysts, the amount of Pt loadings and space velocity on catalytic performance were investigated. It was shown that Pt particles were homogeneously dispersed on 3DOM TiO2. The reduction of TiO2 surface was important for the catalytic performance. The activity test results showed that the 3DOM Pt/TiO2 catalysts exhibited very good catalytic performance for WGS reaction even at high space velocity, which was owing to the better mass transfer of 3DOM porous structure besides the high intrinsic activity of Pt/TiO2.
基金the National Basic Research Program of China （No. 2004CB217808） the National Natural Science Foundation of China （No. 20376046）.
文摘A β-zeolite/polystyrene composite material was synthesized by co-deposition of mono-disperse polystyrene spheres and nano β-zeolite particles in aqueous suspension on a vertical substrate. Macro-porous β-zeolite was obtained after the polystyrene template was removed by calcination. The micro/macro-pore structure of the prepared β-zeolite was highly ordered. In comparison with other assembly methods, the co-deposition method could obtain a highly ordered macro-porous material with relatively large zeolite filling particles, and therefore the co-deposition of particles with different size is a promising method for the fabrication of macro-porous materials.
文摘Titania thin films with hierarchically macro-mesoporous were prepared by the addition of bulky organic molecule(1,3,5-trimethylbezenze) in aqueous solution of F127(EO106PO70EO106). After calcined at 673 K,ordered thin films with cubic meso-structure and macropores were formed. DNA(Cytochrome c) was used as probe to study the adsorption ability of macromolecules on this film. The hierarchically macro-mesoporous films show high adsorption ability of DNA molecules compared with conventional titania films and mesoporous titania films,which is attributed to the presence of macropores.