The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent...The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent catalysts used at different time,indicated that the main reason of the catalyst deactivation was the deposition of carbonaceous species that covered the active Ni and blocked mesopores of the catalyst.The TPO and SEM measurements revealed that the carbonaceous species included both oligomeric and polymeric species with high C/H ratio and showed sheet.Such carbonaceous species might be eliminated through either direct H2 reduction or the combined oxidation-reduction methodologies.展开更多
Nickel and nickel-ceria catalysts supported on high surface area silica, with 6 wt% Ni and 20 wt% CeO2 were prepared by microwave assisted(co) precipitation method. The catalysts were investigated by XRD,TPR and XPS a...Nickel and nickel-ceria catalysts supported on high surface area silica, with 6 wt% Ni and 20 wt% CeO2 were prepared by microwave assisted(co) precipitation method. The catalysts were investigated by XRD,TPR and XPS analyses and they were tested in partial oxidation of methane(CPO). The catalytic reaction was carried out at atmospheric pressure in a temperature range of 400–800℃ with a feed gas mixture containing methane and oxygen in a molecular ratio CH4/O2=2. The Ni catalyst exhibited 60% methane conversion with 60% selectivity to CO already at 500℃. On the contrary, the Ni–Ce catalyst was inert to CPO up to 700℃. Moreover, the former catalyst reproduced its activity at the descending temperatures maintaining a good stability at 600℃, over a reaction time of 80 h, whereas the latter one completely deactivated. Test of CH4 temperature programmed surface reaction(CH4-TPSR) revealed a higher methane activation temperature(> 100℃) for the Ni–Ce catalyst as compared to the Ni one. Noticeable improvement of the ceria containing catalyst occurred when the reaction test started at a temperature higher than the methane decomposition temperature. In this case, the sample achieved the same catalytic behavior of the Ni catalyst. As confirmed by XPS analyses, the distinct electronic state of the supported nickel was responsible for the differences in catalytic behavior.展开更多
A novel glucose oxidase immobilized on three-dimensionally ordered macroporous （3DOM） material has been prepared by firstly preparation of hybrid 3DOM SiO2-NH2 materials using colloidal crystal method, and following...A novel glucose oxidase immobilized on three-dimensionally ordered macroporous （3DOM） material has been prepared by firstly preparation of hybrid 3DOM SiO2-NH2 materials using colloidal crystal method, and following covalent immobilization of glucose oxidase on the pore walls of the 3DOM materials. The materials were characterized by SEM, FTIR, DSC and BET techniques. SEM observation shows that the macropores are highly ordered and are interconnected by small windows. FTIR measurement shows that there are amino and organic groups in the pore walls. The surface area of the 3DOM SiO2-NH2 material is about 10.2 m2/g. The loaded amount of enzyme is increased with amino content in the materials. The immobilized enzyme has high activity, thermal stability and can be reused.展开更多
基金Supported by the National Natural Science Foundation of China(21673132).
文摘The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent catalysts used at different time,indicated that the main reason of the catalyst deactivation was the deposition of carbonaceous species that covered the active Ni and blocked mesopores of the catalyst.The TPO and SEM measurements revealed that the carbonaceous species included both oligomeric and polymeric species with high C/H ratio and showed sheet.Such carbonaceous species might be eliminated through either direct H2 reduction or the combined oxidation-reduction methodologies.
基金The Executive Programme for Cooperation between Italy and India (Prot.No.MAE01054762017)。
文摘Nickel and nickel-ceria catalysts supported on high surface area silica, with 6 wt% Ni and 20 wt% CeO2 were prepared by microwave assisted(co) precipitation method. The catalysts were investigated by XRD,TPR and XPS analyses and they were tested in partial oxidation of methane(CPO). The catalytic reaction was carried out at atmospheric pressure in a temperature range of 400–800℃ with a feed gas mixture containing methane and oxygen in a molecular ratio CH4/O2=2. The Ni catalyst exhibited 60% methane conversion with 60% selectivity to CO already at 500℃. On the contrary, the Ni–Ce catalyst was inert to CPO up to 700℃. Moreover, the former catalyst reproduced its activity at the descending temperatures maintaining a good stability at 600℃, over a reaction time of 80 h, whereas the latter one completely deactivated. Test of CH4 temperature programmed surface reaction(CH4-TPSR) revealed a higher methane activation temperature(> 100℃) for the Ni–Ce catalyst as compared to the Ni one. Noticeable improvement of the ceria containing catalyst occurred when the reaction test started at a temperature higher than the methane decomposition temperature. In this case, the sample achieved the same catalytic behavior of the Ni catalyst. As confirmed by XPS analyses, the distinct electronic state of the supported nickel was responsible for the differences in catalytic behavior.
文摘A novel glucose oxidase immobilized on three-dimensionally ordered macroporous （3DOM） material has been prepared by firstly preparation of hybrid 3DOM SiO2-NH2 materials using colloidal crystal method, and following covalent immobilization of glucose oxidase on the pore walls of the 3DOM materials. The materials were characterized by SEM, FTIR, DSC and BET techniques. SEM observation shows that the macropores are highly ordered and are interconnected by small windows. FTIR measurement shows that there are amino and organic groups in the pore walls. The surface area of the 3DOM SiO2-NH2 material is about 10.2 m2/g. The loaded amount of enzyme is increased with amino content in the materials. The immobilized enzyme has high activity, thermal stability and can be reused.