Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and...Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.展开更多
The paper analyses the wear mechanism of magnesia-chrome bricks for snorkel of RH degasser. High-performance magnesia-chrome bricks with good resistance to molten slag and infiltration resistance have been manufacture...The paper analyses the wear mechanism of magnesia-chrome bricks for snorkel of RH degasser. High-performance magnesia-chrome bricks with good resistance to molten slag and infiltration resistance have been manufactured by means of reasonable fabricating technology. The application results of the developed magnesia-chrome bricks at 300t RH degasser of Baosteel indicate that the lining life has been increased up to 150 heats.展开更多
The state-of-art of magnesia-chrome refractories from direct-bonded magnesia chrome brick to fused-grain rebounded magnesia chrome brick for P-S converter is dis-cribed. The Cr2O3 content of the brick is continually i...The state-of-art of magnesia-chrome refractories from direct-bonded magnesia chrome brick to fused-grain rebounded magnesia chrome brick for P-S converter is dis-cribed. The Cr2O3 content of the brick is continually increased with the reduction of the impurity content of brick , the pre-synthetic raw material it applied and the operating condition of convener is optimized so that the service life of convener is largely enhanced.展开更多
文摘Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.
文摘The paper analyses the wear mechanism of magnesia-chrome bricks for snorkel of RH degasser. High-performance magnesia-chrome bricks with good resistance to molten slag and infiltration resistance have been manufactured by means of reasonable fabricating technology. The application results of the developed magnesia-chrome bricks at 300t RH degasser of Baosteel indicate that the lining life has been increased up to 150 heats.
文摘The state-of-art of magnesia-chrome refractories from direct-bonded magnesia chrome brick to fused-grain rebounded magnesia chrome brick for P-S converter is dis-cribed. The Cr2O3 content of the brick is continually increased with the reduction of the impurity content of brick , the pre-synthetic raw material it applied and the operating condition of convener is optimized so that the service life of convener is largely enhanced.