Two types of low carbon MgO - C refractories with 6% graphite were prepared using microporous magnesiarich spinel （5 - 3 and 3 - 1 mm ） and fused magnesia （5 - 3 and 3 - 1 mm ） as coarse aggregates, respectively, ...Two types of low carbon MgO - C refractories with 6% graphite were prepared using microporous magnesiarich spinel （5 - 3 and 3 - 1 mm ） and fused magnesia （5 - 3 and 3 - 1 mm ） as coarse aggregates, respectively, fused magnesia （ ≤1 mm） as fine aggregate, magnesia powder （≤ 0. 088 mm ） , flake graphite powder （ ≤0. 088 mm）, metal Al powder （ 〈0. 074 mm） as matrix, and phenol resin as binder. After curing at 220 ℃ and coke-embedded firing at 1 500 ℃ , the apparent porosity, cold crushing strength, cold modulus of rupture, permanent linear change on heating, thermal shock resistance and slag resistance of the specimens were studied comparatively. The results indicate that： （ 1 ） after curing at 220 ℃ and coke-embedded firing at 1 500 ℃, the specimen with microporous magnesia-rich spinel replacing fused magnesia has lower bulk density and higher apparent porosity than the common low car- bon MgO - C specimen. After curing at 220 ℃, the specimen with microporous aggregate has lower strength than common low carbon MgO - C specimen, but after coke-embedded firing at 1 500℃, it has higher strength and lower permanent linear change on heating; （2） low carbon MgO - C specimen using microporous magnesia-rich spinel to replace fused magnesia aggregate has better thermal shock resistance but worse slag resistance.展开更多
The effects of Sm_(2) O_(3) as an additive on the densification of a pre-synthesized magnesia-rich spinel were investigated.The sintering behavior of the material was characterized by analyzing its dilatometric charac...The effects of Sm_(2) O_(3) as an additive on the densification of a pre-synthesized magnesia-rich spinel were investigated.The sintering behavior of the material was characterized by analyzing its dilatometric characteristics,linear shrinkage,bulk density,apparent porosity,phase structure,and micro structure.Moreover,the cold modulus of rupture(CMOR) and microhardness of the spinel were measured.The results show that samarium oxide reacts with the spinel to form SmAlO_(3)(a rare-earth aluminate) to improve the sintering performance and mechanical properties of the spinel. The formation of magnesite phases decreases the rupture strength of the spinel.However,this MgO phase is inlaid in spinel grains boundary,has a pinning effect which can improve the sinterability of the spinel.展开更多
文摘Two types of low carbon MgO - C refractories with 6% graphite were prepared using microporous magnesiarich spinel （5 - 3 and 3 - 1 mm ） and fused magnesia （5 - 3 and 3 - 1 mm ） as coarse aggregates, respectively, fused magnesia （ ≤1 mm） as fine aggregate, magnesia powder （≤ 0. 088 mm ） , flake graphite powder （ ≤0. 088 mm）, metal Al powder （ 〈0. 074 mm） as matrix, and phenol resin as binder. After curing at 220 ℃ and coke-embedded firing at 1 500 ℃ , the apparent porosity, cold crushing strength, cold modulus of rupture, permanent linear change on heating, thermal shock resistance and slag resistance of the specimens were studied comparatively. The results indicate that： （ 1 ） after curing at 220 ℃ and coke-embedded firing at 1 500 ℃, the specimen with microporous magnesia-rich spinel replacing fused magnesia has lower bulk density and higher apparent porosity than the common low car- bon MgO - C specimen. After curing at 220 ℃, the specimen with microporous aggregate has lower strength than common low carbon MgO - C specimen, but after coke-embedded firing at 1 500℃, it has higher strength and lower permanent linear change on heating; （2） low carbon MgO - C specimen using microporous magnesia-rich spinel to replace fused magnesia aggregate has better thermal shock resistance but worse slag resistance.
基金Project supported by the National Natural Science Foundation of China (U20A20239,51672195,51474166)。
文摘The effects of Sm_(2) O_(3) as an additive on the densification of a pre-synthesized magnesia-rich spinel were investigated.The sintering behavior of the material was characterized by analyzing its dilatometric characteristics,linear shrinkage,bulk density,apparent porosity,phase structure,and micro structure.Moreover,the cold modulus of rupture(CMOR) and microhardness of the spinel were measured.The results show that samarium oxide reacts with the spinel to form SmAlO_(3)(a rare-earth aluminate) to improve the sintering performance and mechanical properties of the spinel. The formation of magnesite phases decreases the rupture strength of the spinel.However,this MgO phase is inlaid in spinel grains boundary,has a pinning effect which can improve the sinterability of the spinel.