Magnesium alloy wires were processed by micro-arc oxidation （MAO） in a modified silicate-phosphate composite electrolyte containing hydroxyapatite （HA） nanopowders and NaOH. Effects of NaOH content in the composit...Magnesium alloy wires were processed by micro-arc oxidation （MAO） in a modified silicate-phosphate composite electrolyte containing hydroxyapatite （HA） nanopowders and NaOH. Effects of NaOH content in the composite electrolyte on the microstructure and properties of the MAO ceramic coatings on magnesium alloy wires were studied. It is found that the arc voltage of magnesium alloy wires in the micro-arc oxidation process is significantly reduced while the oxidation rate is accelerated. Addition of 2 g/L NaOH in the composite electrolyte is a better choice for improving corrosion resistance of magnesium alloy wires. During early simulated body fluids （SBF） immersion, the micro-arc oxidized magnesium alloy wires undergo a slow and stable degradation. After soaking for 28 d, the protective ceramic coating still shows no damage but significant degradation is observed for magnesium alloy wires after immersion for more than 60 d.展开更多
The degradation behaviors of the novel high-strength AZ31B magnesium alloy wires after surface modification using micro-arc-oxidization （MAO） and subse- quently sealing with poly-L-lactic acid （PLLA） in different ...The degradation behaviors of the novel high-strength AZ31B magnesium alloy wires after surface modification using micro-arc-oxidization （MAO） and subse- quently sealing with poly-L-lactic acid （PLLA） in different simulated physiological environments were investigated. The results show the surface MAO micropores could be physically sealed by PLLA, thus forming an effective protection to corrosion resistance for the wires. In simulated gastric fluid （SGF） at a low pH value （1.5 or 2.5）, the treated wires have a high degradation rate with a rapid decrease of mass, diameter, mechanical properties and a significant increase of pH value of the immersion fluid. However, surface modification could effectively reduce the degradation rate of the treated wires in SGF with a pH value above 4.0. For the treated wires in simulated intestinal fluid at pH =8.5, their strength retention ability is higher than that in strong acidic SGF. And the loss rate of mass is faster than that of diameter, while the pH value of the immersion fluid decreases. It should be noted that the modified wires in simulated body environment have the best strength retention ability. The wires show the different degradation behaviors indicating their different degradation mechanisms, which are also proposed in this work.展开更多
基金Project (BE2011778) supported by Science and Technology Support Program of Jiangsu Province,ChinaProjects (CityU 112510,112212) supported by Hong Kong Research Grants Council (RGC) General Research Funds (GRF) ,China
文摘Magnesium alloy wires were processed by micro-arc oxidation （MAO） in a modified silicate-phosphate composite electrolyte containing hydroxyapatite （HA） nanopowders and NaOH. Effects of NaOH content in the composite electrolyte on the microstructure and properties of the MAO ceramic coatings on magnesium alloy wires were studied. It is found that the arc voltage of magnesium alloy wires in the micro-arc oxidation process is significantly reduced while the oxidation rate is accelerated. Addition of 2 g/L NaOH in the composite electrolyte is a better choice for improving corrosion resistance of magnesium alloy wires. During early simulated body fluids （SBF） immersion, the micro-arc oxidized magnesium alloy wires undergo a slow and stable degradation. After soaking for 28 d, the protective ceramic coating still shows no damage but significant degradation is observed for magnesium alloy wires after immersion for more than 60 d.
文摘The degradation behaviors of the novel high-strength AZ31B magnesium alloy wires after surface modification using micro-arc-oxidization （MAO） and subse- quently sealing with poly-L-lactic acid （PLLA） in different simulated physiological environments were investigated. The results show the surface MAO micropores could be physically sealed by PLLA, thus forming an effective protection to corrosion resistance for the wires. In simulated gastric fluid （SGF） at a low pH value （1.5 or 2.5）, the treated wires have a high degradation rate with a rapid decrease of mass, diameter, mechanical properties and a significant increase of pH value of the immersion fluid. However, surface modification could effectively reduce the degradation rate of the treated wires in SGF with a pH value above 4.0. For the treated wires in simulated intestinal fluid at pH =8.5, their strength retention ability is higher than that in strong acidic SGF. And the loss rate of mass is faster than that of diameter, while the pH value of the immersion fluid decreases. It should be noted that the modified wires in simulated body environment have the best strength retention ability. The wires show the different degradation behaviors indicating their different degradation mechanisms, which are also proposed in this work.