Calcium sulfate hemihydrate whiskers were synthesized successfully via one-step hydrothermal crystallization method using phosphogypsum at 130 °C for 240 min with an initial slurry mass fraction of 2.5 wt%. The p...Calcium sulfate hemihydrate whiskers were synthesized successfully via one-step hydrothermal crystallization method using phosphogypsum at 130 °C for 240 min with an initial slurry mass fraction of 2.5 wt%. The phase compositions, microstructures, thermal properties and molecular structures of asprepared samples were analyzed by XRD, ESEM, EDS, TG-DTA, and FT-IR. The influence of raw materials’ ball-milling time on the morphologies of whiskers was investigated. The effects of impurities on crystallization morphologies and length to diameter ratio(L/D) of calcium sulfate hemihydrate whiskers were studied. The results indicated that the calcium sulfate dihydrate crystalline could be translated directly into fibrous calcium sulfate hemihydrate whiskers. It was beneficial to form fine fiber structure when the ball-milling time of the raw material was 15 min. Aspect ratio of calcium sulfate hemihydrate whiskers decreased with increasing content of impurities. Moreover, the relative growth mechanism of whisker crystals via one-step hydrothermal crystallization method was discussed in detail.展开更多
Mg2B2O5 whiskers with high aspect ratio were synthesized by coprecipitation and sintering process using MgCl2-6H2O, H3BO3, and NaOH as raw materials and KCl as a flux. Their formation process was investigated by therm...Mg2B2O5 whiskers with high aspect ratio were synthesized by coprecipitation and sintering process using MgCl2-6H2O, H3BO3, and NaOH as raw materials and KCl as a flux. Their formation process was investigated by thermogravimetry and differential scanning calo- rimetry （TG-DSC）, X-ray diffraction （XRD）, and scanning electron microcopy （SEM）. It is found that the products synthesized at 832℃ are monoclinic Mg2B205 whiskers with a diameter of 200-400 nm and a length of 50-80 μm. Transmission electron microscopy （TEM） and selected area electron diffraction （SAED） analyses show that the whiskers obtained at 832℃ are single crystalline and grow along with the [010] direction. The growth mechanism of Mg2B2O5 whiskers was also presented.展开更多
In this paper,the solid waste desulfurization gypsum produced by coal-fired power plants was used as a raw material to prepare calcium sulfate whiskers with high application prospects.Calcium sulfate whiskers with uni...In this paper,the solid waste desulfurization gypsum produced by coal-fired power plants was used as a raw material to prepare calcium sulfate whiskers with high application prospects.Calcium sulfate whiskers with uniform morphology and high aspect ratio can be prepared by hydrothermal method in sulfuric acid solution.A new process of desulfurization gypsum activated by high-energy grinding to reduce the reaction temperature and sulfuric acid concentration was developed.Through the comparison of product morphology,the best grinding time was determined to be 3.5 h.The mechanism of desulfurization gypsum through physical–chemical coupling to reduce energy consumption was clarified.The activation of desulfurization gypsum by grinding and the acidic environment provided by the sulfuric acid solution made the calcium sulfate solution reached rapid saturation and accelerated the nucleation rate.By calculating the conversion and crystallization rate of calcium sulfate whiskers,it was found that there were obvious"autocatalytic"kinetic characteristics during the crystallization process.展开更多
The thermal expansion behaviors of commercially-available SiC whisker reinforced pure aluminum composites subjected to different heat treatments were studied. The results indicated that the thermal expansion behaviors...The thermal expansion behaviors of commercially-available SiC whisker reinforced pure aluminum composites subjected to different heat treatments were studied. The results indicated that the thermal expansion behaviors were greatly affected by heat treatment. To explain the results, the microstructures and thermal mismatch stresses in the matrix of the composite were examined by the transmission electron microscope and X-ray diffraction, respectively. The results show that the dislocation density and thermal mismatch stresses in the matrix of the composites water-quenched from 600°C are much higher than those of the composite slowly cooled from 600°C. The analysis suggests that the coefficients of thermal expansion (CTE) are closely related to the change of thermal mismatch stresses and the yield strength of the matrix of the composite. The comparison of the coefficients of thermal expansion between experiments and calculations suggests that the temperature behaviors of CTE of SiC/Al composite agree better with those of Kerner's model within lower temperature range.展开更多
The growth habit of the basic magnesium oxysulfate whisker was investigated based on the theoreticalmodelof anion coordination polyhedron growth units.It is found that typicalbasic magnesium oxysulfate whisker growth ...The growth habit of the basic magnesium oxysulfate whisker was investigated based on the theoreticalmodelof anion coordination polyhedron growth units.It is found that typicalbasic magnesium oxysulfate whisker growth is consistent with anion tetrahedralcoordination incorporation rules.The growth units of basic magnesium oxysulfate whiskers are [Mg-（OH）_4]^（2-） and HSO_4^-.[Mg-（OH）_4]^（2-） is the favorable growth unit and whisker growth is in the direction of the [Mg-（OH）_4]^（2-） combination.A plurality of [Mg-（OH）_4]^（2-） s combine and become a larger dimensionalgrowth unit in a one-dimensionaldirection.Then HSO_4^- and larger dimensionalgrowth units connect as basic magnesium sulfate whiskers,according to the structuralcharacteristics of the basic magnesium sulfate whisker,which can guide the synthesis of magnesium hydroxide whisker.展开更多
Single crystalline calcium chloroborate（Ca2B5O9Cl） whiskers with uniform diameter have been fabricated by a two-step process. The precursor was firstly prepared by the sedimentation reaction between CaCl2, H3BO3 and...Single crystalline calcium chloroborate（Ca2B5O9Cl） whiskers with uniform diameter have been fabricated by a two-step process. The precursor was firstly prepared by the sedimentation reaction between CaCl2, H3BO3 and Na OH aqueous solutions, and then sintered at different temperatures for 6 h with KCl as flux. The XRD indicates that the product synthesized at 600 °C is Orthorhombic Ca2B5O9Cl. SEM and TEM results show that the Ca2B5O9Cl is whisker with the diameter about 0.2-0.5 μm and the length up to 15 μm. SAED analysis shows that the whisker is single crystalline and grows along [001] direction. The possible formation process and growth mechanism were proposed.展开更多
Elucidating the effect of growth periods on the quality of calcium sulfate whiskers(CSWs)prepared from calcium sulfate dihydrate(DH)is imperative.Herein,crystal seeds and whiskers were prepared from DH in a water–gly...Elucidating the effect of growth periods on the quality of calcium sulfate whiskers(CSWs)prepared from calcium sulfate dihydrate(DH)is imperative.Herein,crystal seeds and whiskers were prepared from DH in a water–glycerol system.Longer whiskers were obtained from crystal seeds prepared via hydration of DH for 30 s than via ball milling for 5 min followed by hydration for 20 s.The attachment of cetyltrimethyl ammonium bromide and glycerol additives to the whisker tops promoted whisker growth.The whisker sponges exhibited good thermal barrier properties and compression cycle stability.展开更多
Large and uniform tetrapod-like ZnO whiskers （T-ZnO） were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The...Large and uniform tetrapod-like ZnO whiskers （T-ZnO） were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The products are pure hexagonal wurtzite crystals with tetrapod shape and edge size of center body 56 μm and needle length of 100130 μm. The size and shape of ZnO particles are fully controlled by the growth conditions and T-ZnO can be obtained only at 8501 000 ℃ and total gas flow rate ranging from 40 to 250 L·h-1 in which the size of the T-ZnO particles varies slightly with temperature. The process of the formation of T-ZnO is that T-ZnO may nucleate at the initial stage with a complete tetrapod shape and develop to the large size, but not the process of （preferential） growth of octahedral nuclei and subsequent growth of the needles. The experiment presents a new method to prepare T-ZnO economically by using the waste hot dipping zinc.展开更多
BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium ch/oride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as ...BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium ch/oride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as a crystal growth modifier at room temperature. The as-prepared products were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. The influences of experimental parameters on the size and morphology of BaCO3 whiskers were investigated and discussed. It was found that the as-prepared BaCO3 whiskers are single crystals with diameter ranging from 100 to 300 run, and grow along the crystallographic a-axis or [100] direction. BaCO3 whiskers with different morphologies, such as branching and dendritic structure, can be obtained depending on the experimental conditions. With increasing PSMA concentration, the diameter of BaCO3 whiskers decreases.展开更多
A novel optical fiber tactile sensory system is proposed for obstacle avoidance of mobile robot. The principle of this whisker like tactile sensor is based on the geometric curvature changes of the optical fiber, whic...A novel optical fiber tactile sensory system is proposed for obstacle avoidance of mobile robot. The principle of this whisker like tactile sensor is based on the geometric curvature changes of the optical fiber, which modulate the optical fiber′s light output. With high compliance of plastic optical fiber, the whiskers can produce only small flexing force upon mechanical contact with an obstacle. It can produce reliable proximity signals in extended tactile range, which can be translated into a larger stopping distance for the mobile robot. This sensor is lightweight, and of low cost to allow as many sensor, as necessary to be mounted on a robot.展开更多
BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium chloride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as ...BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium chloride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as a crystal growth modifier at room temperature. The as-prepared products were characterized by scanning electron microscopy （SEM）,transmission electron microscopy （TEM）,and X-ray diffraction （XRD）. The influences of experimental parameters on the size and morphology of BaCO3 whiskers were investigated and discussed. It was found that the as-prepared BaCO3 whiskers are single crystals with diameter ranging from 100 to 300?nm,and grow along the crystallographic a-axis or [100] direction. BaCO3 whiskers with different morphologies,such as branching and dendritic structure,can be obtained depending on the experimental conditions. With increasing PSMA concentration,the diameter of BaCO3 whiskers decreases.展开更多
以γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)改性的硫酸钙晶须(CSW)为高密度聚乙烯(HDPE)的填料,采用熔融共混法制备了HDPE/CSW复合材料。通过SEM、XRD、TG、DSC表征了KH570改性的CSW对复合材料HDPE/CSW的性能影响。结果表明,改性CSW...以γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)改性的硫酸钙晶须(CSW)为高密度聚乙烯(HDPE)的填料,采用熔融共混法制备了HDPE/CSW复合材料。通过SEM、XRD、TG、DSC表征了KH570改性的CSW对复合材料HDPE/CSW的性能影响。结果表明,改性CSW质量分数为20%时,HDPE/CSW的拉伸和弯曲强度比纯HDPE分别增加9.28%和33.04%,且易产生异相结晶,提升了HDPE/CSW复合材料的耐热性和结晶度。纯HDPE的热降解反应活化能为244.11 k J/mol,改性CSW质量分数为50%时,HDPE/CSW复合材料的热降解反应活化能降到236.99 kJ/mol,表明CSW提升了HDPE/CSW复合材料的热降解反应速率,扩展了复合材料的使用范围。展开更多
基金Funded by the National High-tech Research and Development Program of China(2011AA06A106)
文摘Calcium sulfate hemihydrate whiskers were synthesized successfully via one-step hydrothermal crystallization method using phosphogypsum at 130 °C for 240 min with an initial slurry mass fraction of 2.5 wt%. The phase compositions, microstructures, thermal properties and molecular structures of asprepared samples were analyzed by XRD, ESEM, EDS, TG-DTA, and FT-IR. The influence of raw materials’ ball-milling time on the morphologies of whiskers was investigated. The effects of impurities on crystallization morphologies and length to diameter ratio(L/D) of calcium sulfate hemihydrate whiskers were studied. The results indicated that the calcium sulfate dihydrate crystalline could be translated directly into fibrous calcium sulfate hemihydrate whiskers. It was beneficial to form fine fiber structure when the ball-milling time of the raw material was 15 min. Aspect ratio of calcium sulfate hemihydrate whiskers decreased with increasing content of impurities. Moreover, the relative growth mechanism of whisker crystals via one-step hydrothermal crystallization method was discussed in detail.
基金financially supported by the Department of Science and Technology of Qinghai Province of China(Grant No.2010-G-208)
文摘Mg2B2O5 whiskers with high aspect ratio were synthesized by coprecipitation and sintering process using MgCl2-6H2O, H3BO3, and NaOH as raw materials and KCl as a flux. Their formation process was investigated by thermogravimetry and differential scanning calo- rimetry （TG-DSC）, X-ray diffraction （XRD）, and scanning electron microcopy （SEM）. It is found that the products synthesized at 832℃ are monoclinic Mg2B205 whiskers with a diameter of 200-400 nm and a length of 50-80 μm. Transmission electron microscopy （TEM） and selected area electron diffraction （SAED） analyses show that the whiskers obtained at 832℃ are single crystalline and grow along with the [010] direction. The growth mechanism of Mg2B2O5 whiskers was also presented.
基金supported by the State Key Laboratory of Mineral Processing Science and Technology Open Fund(BGRIMM-KJSKL-2017-16)Liaoning Provincial Department of Education Youth Project(LJ2017QL028)Coal Resource Safety Mining and Clean Utilization Engineering Research Center Open Fund(LNTU15KF18)。
文摘In this paper,the solid waste desulfurization gypsum produced by coal-fired power plants was used as a raw material to prepare calcium sulfate whiskers with high application prospects.Calcium sulfate whiskers with uniform morphology and high aspect ratio can be prepared by hydrothermal method in sulfuric acid solution.A new process of desulfurization gypsum activated by high-energy grinding to reduce the reaction temperature and sulfuric acid concentration was developed.Through the comparison of product morphology,the best grinding time was determined to be 3.5 h.The mechanism of desulfurization gypsum through physical–chemical coupling to reduce energy consumption was clarified.The activation of desulfurization gypsum by grinding and the acidic environment provided by the sulfuric acid solution made the calcium sulfate solution reached rapid saturation and accelerated the nucleation rate.By calculating the conversion and crystallization rate of calcium sulfate whiskers,it was found that there were obvious"autocatalytic"kinetic characteristics during the crystallization process.
文摘The thermal expansion behaviors of commercially-available SiC whisker reinforced pure aluminum composites subjected to different heat treatments were studied. The results indicated that the thermal expansion behaviors were greatly affected by heat treatment. To explain the results, the microstructures and thermal mismatch stresses in the matrix of the composite were examined by the transmission electron microscope and X-ray diffraction, respectively. The results show that the dislocation density and thermal mismatch stresses in the matrix of the composites water-quenched from 600°C are much higher than those of the composite slowly cooled from 600°C. The analysis suggests that the coefficients of thermal expansion (CTE) are closely related to the change of thermal mismatch stresses and the yield strength of the matrix of the composite. The comparison of the coefficients of thermal expansion between experiments and calculations suggests that the temperature behaviors of CTE of SiC/Al composite agree better with those of Kerner's model within lower temperature range.
基金Funded by the National Natural Science Foundation of China(No.51272207)
文摘The growth habit of the basic magnesium oxysulfate whisker was investigated based on the theoreticalmodelof anion coordination polyhedron growth units.It is found that typicalbasic magnesium oxysulfate whisker growth is consistent with anion tetrahedralcoordination incorporation rules.The growth units of basic magnesium oxysulfate whiskers are [Mg-（OH）_4]^（2-） and HSO_4^-.[Mg-（OH）_4]^（2-） is the favorable growth unit and whisker growth is in the direction of the [Mg-（OH）_4]^（2-） combination.A plurality of [Mg-（OH）_4]^（2-） s combine and become a larger dimensionalgrowth unit in a one-dimensionaldirection.Then HSO_4^- and larger dimensionalgrowth units connect as basic magnesium sulfate whiskers,according to the structuralcharacteristics of the basic magnesium sulfate whisker,which can guide the synthesis of magnesium hydroxide whisker.
基金Funded by the National Natural Science Foundation of China(No.51402323)the West Light Foundation of the Chinese Academy of Sciences(No.Y412031006)the Natural Science Foundation of Qinghai Province,China(No.2014-ZJ-938Q)
文摘Single crystalline calcium chloroborate（Ca2B5O9Cl） whiskers with uniform diameter have been fabricated by a two-step process. The precursor was firstly prepared by the sedimentation reaction between CaCl2, H3BO3 and Na OH aqueous solutions, and then sintered at different temperatures for 6 h with KCl as flux. The XRD indicates that the product synthesized at 600 °C is Orthorhombic Ca2B5O9Cl. SEM and TEM results show that the Ca2B5O9Cl is whisker with the diameter about 0.2-0.5 μm and the length up to 15 μm. SAED analysis shows that the whisker is single crystalline and grows along [001] direction. The possible formation process and growth mechanism were proposed.
基金supported by the Degradable Plastics Engineering Research Center of Yunnan Provincial Education Department(KKPU202205001).
文摘Elucidating the effect of growth periods on the quality of calcium sulfate whiskers(CSWs)prepared from calcium sulfate dihydrate(DH)is imperative.Herein,crystal seeds and whiskers were prepared from DH in a water–glycerol system.Longer whiskers were obtained from crystal seeds prepared via hydration of DH for 30 s than via ball milling for 5 min followed by hydration for 20 s.The attachment of cetyltrimethyl ammonium bromide and glycerol additives to the whisker tops promoted whisker growth.The whisker sponges exhibited good thermal barrier properties and compression cycle stability.
文摘Large and uniform tetrapod-like ZnO whiskers （T-ZnO） were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The products are pure hexagonal wurtzite crystals with tetrapod shape and edge size of center body 56 μm and needle length of 100130 μm. The size and shape of ZnO particles are fully controlled by the growth conditions and T-ZnO can be obtained only at 8501 000 ℃ and total gas flow rate ranging from 40 to 250 L·h-1 in which the size of the T-ZnO particles varies slightly with temperature. The process of the formation of T-ZnO is that T-ZnO may nucleate at the initial stage with a complete tetrapod shape and develop to the large size, but not the process of （preferential） growth of octahedral nuclei and subsequent growth of the needles. The experiment presents a new method to prepare T-ZnO economically by using the waste hot dipping zinc.
基金This work was financially supported by the National Natural Science Foundation of China (Nos. 50272049 and 20473059).
文摘BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium ch/oride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as a crystal growth modifier at room temperature. The as-prepared products were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. The influences of experimental parameters on the size and morphology of BaCO3 whiskers were investigated and discussed. It was found that the as-prepared BaCO3 whiskers are single crystals with diameter ranging from 100 to 300 run, and grow along the crystallographic a-axis or [100] direction. BaCO3 whiskers with different morphologies, such as branching and dendritic structure, can be obtained depending on the experimental conditions. With increasing PSMA concentration, the diameter of BaCO3 whiskers decreases.
文摘A novel optical fiber tactile sensory system is proposed for obstacle avoidance of mobile robot. The principle of this whisker like tactile sensor is based on the geometric curvature changes of the optical fiber, which modulate the optical fiber′s light output. With high compliance of plastic optical fiber, the whiskers can produce only small flexing force upon mechanical contact with an obstacle. It can produce reliable proximity signals in extended tactile range, which can be translated into a larger stopping distance for the mobile robot. This sensor is lightweight, and of low cost to allow as many sensor, as necessary to be mounted on a robot.
文摘BaCO3 whiskers exhibiting different morphologies were fabricated by a simple precipitation reaction of barium chloride with sodium carbonate in the absence and presence of poly-（styrene-alt-maleic acid） （PSMA） as a crystal growth modifier at room temperature. The as-prepared products were characterized by scanning electron microscopy （SEM）,transmission electron microscopy （TEM）,and X-ray diffraction （XRD）. The influences of experimental parameters on the size and morphology of BaCO3 whiskers were investigated and discussed. It was found that the as-prepared BaCO3 whiskers are single crystals with diameter ranging from 100 to 300?nm,and grow along the crystallographic a-axis or [100] direction. BaCO3 whiskers with different morphologies,such as branching and dendritic structure,can be obtained depending on the experimental conditions. With increasing PSMA concentration,the diameter of BaCO3 whiskers decreases.
文摘以γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)改性的硫酸钙晶须(CSW)为高密度聚乙烯(HDPE)的填料,采用熔融共混法制备了HDPE/CSW复合材料。通过SEM、XRD、TG、DSC表征了KH570改性的CSW对复合材料HDPE/CSW的性能影响。结果表明,改性CSW质量分数为20%时,HDPE/CSW的拉伸和弯曲强度比纯HDPE分别增加9.28%和33.04%,且易产生异相结晶,提升了HDPE/CSW复合材料的耐热性和结晶度。纯HDPE的热降解反应活化能为244.11 k J/mol,改性CSW质量分数为50%时,HDPE/CSW复合材料的热降解反应活化能降到236.99 kJ/mol,表明CSW提升了HDPE/CSW复合材料的热降解反应速率,扩展了复合材料的使用范围。