Preparation and Characterization of Fe3O4 Magnetic Nano-particles by ^（60）Co γ-ray Irradiation

By using a new method, ^60Co γ-ray irradiation, Fe3O4 magnetic nano-particles were successfully synthesized at room temperature under ambient pressure. The structure, morphology and magnetic properties of these nanoparticles were characterized by X-ray diffraction （XRD）, transmission electron microscope （TEM） and vibrating sample magnetometer （VSM）, respectively. The radiation formation mechanism was also discussed. The results show that the absorbed dose can greatly influence the structure, morphology and magnetic properties of the products. XRD and TEM studies show that the product prepared by γ-ray irradiation （10 kGy） is pure FesO4 phase and the mean diameter of these nano-particles is about 21 nm. The Fe3O4 nano-particles synthesized by γ-ray irradiation （10 kGy） are mainly in small cubic shape and the size uniformity of these particles is good.

Heat-Affected Behavior of the Magnetic Properties of Iron Nano-Particles

The high surface energy makes metal nano-particles reactive and easy to get oxidized or burned in the open air, which results in decreasing or entirely losing their functions and properties. In this paper, the magnetic property behavior of iron nano-particle, which is one kind of the typical magnetic nano-materials, has been investigated. The iron nano-particles were heated to different temperatures in an open-air stove. After that, they were firstly examined by TEM to observe the changes of their outline of shapes and then measured by VSM to trace the changes of their magnetic properties. The test results show that iron nano-particles can keep their magnetic property with saturation magnetic induction intensity Bs around 136—161 emu/g,remanent magnetic induction intensity Br around 14.8—17.4 emu/g and coercive force Hc around 290—302 Oe when the temperature goes up to 523 K. The explanation to such outstanding oxidization-proof ability has been given that there exists a single crystal and lattice-shared Gamma-Fe2O3 shell covering the pure iron core, which prevents the spherical iron nano-particles from further oxidization.

Low‑Temperature Oxidation Induced Phase Evolution with Gradient Magnetic Heterointerfaces for Superior Electromagnetic Wave Absorption

Gradient magnetic heterointerfaces have injected infinite vitality in optimizing impedance matching,adjusting dielectric/magnetic resonance and promoting electromagnetic(EM)wave absorption,but still exist a significant challenging in regulating local phase evolution.Herein,accordion-shaped Co/Co_(3)O_(4)@N-doped carbon nanosheets(Co/Co_(3)O_(4)@NC)with gradient magnetic heterointerfaces have been fabricated via the cooperative high-temperature carbonization and lowtemperature oxidation process.The results indicate that the surface epitaxial growth of crystal Co_(3)O_(4) domains on local Co nanoparticles realizes the adjustment of magnetic-heteroatomic components,which are beneficial for optimizing impedance matching and interfacial polarization.Moreover,gradient magnetic heterointerfaces simultaneously realize magnetic coupling,and long-range magnetic diffraction.Specifically,the synthesized Co/Co_(3)O_(4)@NC absorbents display the strong electromagnetic wave attenuation capability of−53.5 dB at a thickness of 3.0 mm with an effective absorption bandwidth of 5.36 GHz,both are superior to those of single magnetic domains embedded in carbon matrix.This design concept provides us an inspiration in optimizing interfacial polarization,regulating magnetic coupling and promoting electromagnetic wave absorption.

Characterization and Magnetic Properties of Cobalt Nano-Particles Prepared by Metal Vapor Synthesis Technique

The metal vapor synthesis technique was employed to prepare Co nanoparticles. The characteristics and properties of the particles were studied by transmission electron microscopy, X-ray diffraction, temperature-programmed desorption, chemisorption and magnetic measurements. The experimental results showed that the particle size of Co powders depended on the initial Co concentration in the toluene matrix, reaching average crystallite diameter of 1.5 nm for the highest concentration (6.4 at. pct) investigated. The particles with size of 10 nm exist, due to the agglomerates of microcrystallites. The Co particles were surrounded by a thin carbonaceous layer formed due to toluene decomposition on cocondate melt-down and subsequent warming to room temperature. The carbonaceous layer was composed primarily of C1 fragments. The Co powders demonstrated ferromagnetic behavior.

Advancement in utilization of magnetic resonance imaging and biomarkers in the understanding of schizophrenia

Historically,psychiatric diagnoses have been made based on patient’s reported symptoms applying the criteria from diagnostic and statistical manual of mental disorders.The utilization of neuroimaging or biomarkers to make the diagnosis and manage psychiatric disorders remains a distant goal.There have been several studies that examine brain imaging in psychiatric disorders,but more work is needed to elucidate the complexities of the human brain.In this editorial,we examine two articles by Xu et al and Stoyanov et al,that show developments in the direction of using neuroimaging to examine the brains of people with schizo-phrenia and depression.Xu et al used magnetic resonance imaging to examine the brain structure of patients with schizophrenia,in addition to examining neurotransmitter levels as biomarkers.Stoyanov et al used functional magnetic resonance imaging to look at modulation of different neural circuits by diagnostic-specific scales in patients with schizophrenia and depression.These two studies provide crucial evidence in advancing our understanding of the brain in prevalent psychiatric disorders.

Magnetic resonance imaging evaluation and nuclear receptor binding SET domain protein 1 mutation in the Sotos syndrome with attention-deficit/hyperactivity disorder

Sotos syndrome is characterized by overgrowth features and is caused by alterations in the nuclear receptor binding SET domain protein 1 gene.Attentiondeficit/hyperactivity disorder(ADHD)is considered a neurodevelopment and psychiatric disorder in childhood.Genetic characteristics and clinical presentation could play an important role in the diagnosis of Sotos syndrome and ADHD.Magnetic resonance imaging(MRI)has been used to assess medical images in Sotos syndrome and ADHD.The images process is considered to display in MRI while wavelet fusion has been used to integrate distinct images for achieving more complete information in single image in this editorial.In the future,genetic mechanisms and artificial intelligence related to medical images could be used in the clinical diagnosis of Sotos syndrome and ADHD.

Repetitive transcranial magnetic stimulation in Alzheimer’s disease:effects on neural and synaptic rehabilitation

Alzheimer’s disease is a neurodegenerative disease resulting from deficits in synaptic transmission and homeostasis.The Alzheimer’s disease brain tends to be hyperexcitable and hypersynchronized,thereby causing neurodegeneration and ultimately disrupting the operational abilities in daily life,leaving patients incapacitated.Repetitive transcranial magnetic stimulation is a cost-effective,neuro-modulatory technique used for multiple neurological conditions.Over the past two decades,it has been widely used to predict cognitive decline;identify pathophysiological markers;promote neuroplasticity;and assess brain excitability,plasticity,and connectivity.It has also been applied to patients with dementia,because it can yield facilitatory effects on cognition and promote brain recovery after a neurological insult.However,its therapeutic effectiveness at the molecular and synaptic levels has not been elucidated because of a limited number of studies.This study aimed to characterize the neurobiological changes following repetitive transcranial magnetic stimulation treatment,evaluate its effects on synaptic plasticity,and identify the associated mechanisms.This review essentially focuses on changes in the pathology,amyloidogenesis,and clearance pathways,given that amyloid deposition is a major hypothesis in the pathogenesis of Alzheimer’s disease.Apoptotic mechanisms associated with repetitive transcranial magnetic stimulation procedures and different pathways mediating gene transcription,which are closely related to the neural regeneration process,are also highlighted.Finally,we discuss the outcomes of animal studies in which neuroplasticity is modulated and assessed at the structural and functional levels by using repetitive transcranial magnetic stimulation,with the aim to highlight future directions for better clinical translations.

Preparation and drug releasing property of magnetic chitosan-5-fluorouracil nano-particles

In order to synthesize the targeting drug carrier system,magnetic chitosan-5-fluorouracil nano-particles were prepared by using 5-fluorouracil(5-Fu)as model drug,Fe3O4 nano-particles as kernel,chitosan as enveloping material and glutaraldehyde as cross linking agent through ultrasonic technique.The morphology of the magnetic chitosan-5-Fu nano-particles was observed with a transmission electron microscope(TEM).The results showed that magnetic chitosan-5-Fu nano-particles were prepared in spherical structure with a size range of 50-60 nm.The delivering capacity and drug releasing properties of magnetic chitosan-5-Fu nano-particles were investigated by UV-vis spectrum analysis.The results showed that the loading capacity was 13.4%and the cumulative release percentage in the phosphate buffer(pH=7.2)solutions was 68%in 30 h.These data indicate that the wrapped drug of magnetic chitosan-5-Fu nano-particles was slowly-released.The magnetic response of magnetic chitosan-5-Fu nano-particles was studied by UV-vis spectrometer to detect the changes of solution absorbance.Without external magnetic field,the nano-particle deposition rate was slow.When being subjected to 8 mT magnetic field,the particle sedimentation rate was increased rapidly.The results showed that magnetic chitosan-5-Fu nano-particles have a magnetic stability and strong targeting characteristics.

High temperature frictional wear behaviors of nano-particle reinforced NiCoCrAlY cladded coatings

The NiCoCrAlY coatings strengthened by three nano-particles with the same addition were prepared on a Ni-base super alloy using laser cladding technique. The dry frictional wear behaviors of the coatings at 500 ℃ in static air were investigated. The comparison was made with the coating without nano-particles. The results show that the wear mechanism of the NiCoCrAlY coatings with nano-particles, like the coating without nano-particles, is the delamination wear due to the strong plastic deformation and oxidative wear. However, the frictional coefficient of the coatings increases and presents the decrease trend with the increase of sliding distance after adding nano-particles. Moreover, the wear rate of the coatings with nano-particles is only 34.0%-64.5% of the coating without nano-particles. Among the three nano-particles, the improvement of nano-SiC on the high temperature wear resistance of the coating is the most significant.

Microstructure and Oxidation Behaviors of Nano-particles Strengthened NiCoCrAlY Cladded Coatings on Superalloys

Nano-particles which can largely improve the microstructure and oxidation resistance of materials are often used as a strengthening component in metal matrix composites. However, few studies were reported on its application in the bond coat of duplex structure thermal barrier coating（TBC）. Three kinds of NiCoCrAlY coatings strengthened by different nano-particles with the same addition （1%, mass fraction） were prepared by the laser cladding technique on Ni-based superalloy substrates, aiming to study the effects of the nano-particles on microstructure and oxidation resistance of NiCoCrAlY coatings （the bond coat of the duplex structure thermal barrier coatings）. Scanning electron microscope （SEM）, X-ray diffractometer（XRD） and thermogravimetry were employed to investigate their morphologies, phases and cyclic oxidation behaviors in atmosphere at 1 050℃, compared with the coating without nano-particles. With the addition of nano-particles, the growth pattern of the grains at the interface changed from epitaxial growth to non-epitaxial growth or part-epitaxial growth; slender dendrites were broken and cellularized; cracks and pores were restrained; and the oxidation weight-gain and the stripping resistance of the oxide scale were improved as well. Among the three kinds of nano-particles, the SiC nano-particles showed the most improvement on microstructure, while the CeO2 nano-particles were insufficient, but its effects on the oxidation resistance are the same as those of the SiC nano-particles. Based on the discussions of the influence mechanism, it is believed that CeO2 nano-particles would show better improvement than SiC nano-particles if the proper amount is added and the proper preparation technique of micro-nanometer composite powders is adopted, with the synergistic action of nanometer effect and reactive element effect.

Surface tension of lithium bromide aqueous solution/ammonia with additives and nano-particles

In order to investigate the effect of additives and nano-particle on the surface tensions of lithium bromide(Li Br) aqueous solution/ammonia, many experiments were carried out based on Wilhelmy plate method. Firstly, the surface tension of Li Br aqueous solution with 1-octanol was measured and then the comparison between the measured results and previous experimental results was given to verify the measuring accuracy. Some new additives, such as cationic surfactants cetyltrimethyl ammonium chloride(CTAC), and cetyltrimethyl ammonium bromide(CTAB) were chosen in the experiments. The experimental results show that CTAC and CTAB can obviously reduce the surface tension of Li Br aqueous solution/ammonia. In addition, it is found that nano-particles cannot remarkably decrease the surface tension of Li Br aqueous solution/ammonia. However, the mixed addition of additives and nano-particles can remarkably affect the surface tension of Li Br aqueous solution/ammonia. That is to say, additives play more important role in reducing the surface tension of Li Br aqueous solution/ammonia. But nano-particles may enhance the heat transfer in the absorption refrigeration process.

Effect of nano-particle size on product distribution and kinetic parameters of Fe/Cu/La catalyst in Fischer-Tropsch synthesis

Effects of nano-particle size on hydrocarbon production rates and distributions for precipitated Fe/Cu/La catalysts in Fischer-Tropsch synthesis were investigated.Nano-structured iron catalyst was prepared by micro-emulsion method.The concept of two superimposed AndersonSchulz-Flory （ASF） distributions has been applied for the representation of the effects of reaction conditions and nano-particles size on kinetics parameters and product distributions.These results reveal that by reducing the particle size of catalyst,the break in ASF distributions was decreased.Also useful different kinetics equations for synthesis of C3 to C9 and C10 to C22 were determined by using α1 and α2 chain growth probabilities.

Influence of SiO_2 nano-particles on microstructures and properties of Ni-W-P/CeO_2-SiO_2 composites prepared by pulse electrodeposition

Ni-W-P base composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by pulse co-deposition of Ni,W,P,CeO2 and SiO2 nano-particles.The influence of SiO2 concentrations in bath on microstructures and properties of Ni-W-P/CeO2-SiO2 composites was studied,and the characteristics were assessed by chemical compositions,element distribution,surface morphologies,deposition rate and microhardness.The results indicate that when SiO2 concentration in bath is controlled at 20 g/L,the composites possess the fastest deposition rate,the highest microhardness,compact microstructures,smaller crystallite sizes and uniform distribution of W,P,Ce and Si within Ni-W-P matrix metal.Increasing SiO2 concentration in bath from 10 to 20 g/L leads to the refinement in grain size and the inhomogeneity of microstructures.While when SiO2 concentration is increased to 30 g/L,the crystallite sizes increase again and some bosses with nodulation shape appear on the surface of composites.

Pressure-Induced Structural Transitions of the Zinc Sulfide Nano-particles with Different Sizes

ZnS nano-particles with average sizes of 10 nm and 5 nm were fabricated by sol-gel method, and their pressure-induced phase transformations were in-situ examined in a diamond anvil cell by energy dispersive X-ray diffraction （EDXD） from ambient pressure to 35.0 GPa. From the obtained interplanar spacing data,the volume compression ratios were derived at different pressures, and then the bulk modulus and its pressure derivative were obtained by fitting to the Murnaghan equation. It is found that both ZnS nano-particles initially in the zinc-blende phase transformed to cubic NaCl structure in the presence of pressure and the transition was reversible when the pressure was released. Moreover, it is suggested that a smaller particle size will induce a larger transition pressure.

BRITTLE-DUCTILE TRANSITION OF PP/EPDM/ELASTOMERIC NANO-PARTICLE TERNARY BLENDS

The brittle-ductile transition is a very important phenomenon for polymer toughening. Polypropylene （PP） is often toughened by using rubbers, e.g., ethylene-propylene diene monomer （EPDM） has often been used as a modifier. In this article, the toughening of PP by using a new kind of rubber, known as elastomeric nano-particle （ENP）, and the brittleductile transition of PP/EPDM/ENP was studied. Compared to PP/EPDM binary blends, the brittle-ductile transition of PP/EPDM/ENP ternary blends occurred at lower EPDM contents. SEM experiment was carried out to investigate the etched and impact-fractured surfaces. ENP alone had no effect on the impact strength of PP, however, with the same EPDM content, PP/EPDM/ENP ternary blends had smaller particle size, better dispersion and smaller interparticle distance in contrary to PP/EPDM binary blends, which promoted the brittle-ductile transition to occur earlier.

Friction and Wear of Polymer Composites Filled by Nano-Particles: A Review

Composites formed by adding nano-scale particles to a polymer matrix results in improving electrical, mechanical, and thermal properties of the composite. Good tribological properties can be obtained for polymers filled with nano-scale fillers compared to that filled with micro-scale particles. The friction and wear resistance of these composites is found to increase with increasing filler concentration. It is also possible to use multi-functional fillers to develop high performance composites which cannot be achieved by using a single filler.

Crystallization characteristics of Ni-W-P composite coatings reinforced by CeO_2 and SiO_2 nano-particles

Ni-W-P composite coatings reinforced by Ce O2 and Si O2 nano-particles on the surface of common carbon steels, were prepared by double pulse electrodeposition. The crystallization course was characterized by phase structures, crystallinity, grain sizes and microstructures. The results indicate that as-deposited composite coating is amorphous. Whereas it turns into the crystalline structure with 98.25% crystallinity, and Ni3 P, Ni2 P and Ni5P2 alloy phases precipitate from structures at 400 °C. Thereafter, Ni2 P and Ni5P2 metastable alloy phases turn into Ni3 P stable alloy phase at 500 °C. The crystallization course of the composite coating has finished when being heat-treated at 700 °C. The average sizes of Ni grains increase with the rise of heat treatment temperature from400 °C to 700 °C. Ce O2 and Si O2 nano-particles deposited into Ni-W-P alloys can delay the crystallization course and habit the growth of alloy phases.

The influence of nano-particle tracers on the slip length measurements by microPTV

Direct measurement of slip length is based on the measured fluid velocity near solid boundary. However, previous micro particle image velocimetry/particle tracking velocimetry （microPIV/PTV） measurements have reported surprisingly large measured near-wall velocities of pressure-driven flow in apparent contradiction with the no-slip hy-pothesis and experimental results from other techniques. To better interpret the measured results of the microPIV/PTV, we performed velocity profile measurements near a hy-drophilic wall （z = 0.25-1.5 μm） with two sizes of tracer particles （φ 50 nm and φ200 nm）. The experimental results indicate that, at less than 1 μm from the wall, the deviations between the measured velocities and no-slip theoretical values obviously decrease from 93% of φ200 nm particles to 48% of φ50 nm particles. The Boltzmann-like exponential measured particle concentrations near wall were found. Based on the non linear Boltzmann distribution of particle concentration and the effective focus plane thickness, we illustrated the reason of the apparent velocity increase near wall and proposed a method to correct the measured velocity profile. By this method, the deviations between the corrected measured velocities and the no-slip theoretical velocity decrease from 45.8% to 10%, and the measured slip length on hy-drophilic glass is revised from 75 nm to 16 nm. These results indicated that the particle size and the biased particle concentration distribution can significantly affect near wall velocity measurement via microPIV/PTV, and result in larger measured velocity and slip length close to wall.

Conditions for laser-induced plasma to effectively remove nano-particles on silicon surfaces

Particles can be removed from a silicon surface by means of irradiation and a laser plasma shock wave.The particles and silicon are heated by the irradiation and they will expand differently due to their different expansion coefficients,making the particles easier to be removed.Laser plasma can ionize and even vaporize particles more significantly than an incident laser and,therefore,it can remove the particles more efficiently.The laser plasma shock wave plays a dominant role in removing particles,which is attributed to its strong burst force.The pressure of the laser plasma shock wave is determined by the laser pulse energy and the gap between the focus of laser and substrate surface.In order to obtain the working conditions for particle removal,the removal mechanism,as well as the temporal and spatial characteristics of velocity,propagation distance and pressure of shock wave have been researched.On the basis of our results,the conditions for nano-particle removal are achieved.

Unveiling of Terahertz Emission from Ultrafast Demagnetization and the Anomalous Hall Effect in a Single Ferromagnetic Film

Using THz emission spectroscopy,we investigate the elementary spin dynamics in ferromagnetic single-layer Fe on a sub-picosecond timescale.We demonstrate that THz radiation changes its polarity with reversal of the magnetization applied by the external magnetic field.In addition,it is found that the sign of THz polarity excited from different sides is defined by the thickness of the Fe layer and Fe/dielectric interface.Based on the thickness and symmetry dependences of THz emission,we experimentally distinguish between the two major contributions:ultrafast demagnetization and the anomalous Hall effect.Our experimental results not only enrich understanding of THz electromagnetic generation induced by femtosecond laser pulses but also provide a practical way to access laser-induced ultrafast spin dynamics in magnetic structures.