The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol （PVA） as binder by spray granulation method, The electromagnet...The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol （PVA） as binder by spray granulation method, The electromagnetic parameters of Fe and C composite particles were analyzed by vector network. The complex permittivity and magnetic permeability of Fe and C composite particles matched well with increasing C nanoparticle content, and then the microwave loss property was improved. A minimum reflection loss （RL） of -42.7 dB at 3.68 GHz for a composite with 4.6 mm in thickness can be obtained when the content ratio of the C nanoparticles, the modified Fe nanoparticles and the PVA is 21：49：30 （Sample 3）.展开更多
基金the support from the National Natural Science Foundation of China(No.51171033)the Fundamental Research Funds for the Central Universities(DUT15LAB05,DUT16LAB03)
文摘The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol （PVA） as binder by spray granulation method, The electromagnetic parameters of Fe and C composite particles were analyzed by vector network. The complex permittivity and magnetic permeability of Fe and C composite particles matched well with increasing C nanoparticle content, and then the microwave loss property was improved. A minimum reflection loss （RL） of -42.7 dB at 3.68 GHz for a composite with 4.6 mm in thickness can be obtained when the content ratio of the C nanoparticles, the modified Fe nanoparticles and the PVA is 21：49：30 （Sample 3）.