The reduction of high-chromium vanadium–titanium magnetite as a typical titanomagnetite containing 0.95wt% V2O5 and 0.61wt% Cr2O3 by H2–CO–CO2 gas mixtures was investigated from 1223 to 1373 K. Both the reduction d...The reduction of high-chromium vanadium–titanium magnetite as a typical titanomagnetite containing 0.95wt% V2O5 and 0.61wt% Cr2O3 by H2–CO–CO2 gas mixtures was investigated from 1223 to 1373 K. Both the reduction degree and reduction rate increase with increasing temperature and increasing hydrogen content. At a temperature of 1373 K, an H2/CO ratio of 5/2 by volume, and a reduction time of 40 min, the degree of reduction reaches 95%. The phase transformation during reduction is hypothesized to proceed as follows: Fe2O3 → Fe3O4 → FeO → Fe; Fe9 TiO 15 + Fe2Ti3O9 → Fe2.75Ti0.25O4 → FeT iO 3 → TiO 2;(Cr0.15V0.85)2O3 → Fe2VO4; and Cr1.3Fe0.7O3 → FeC r2O4. The reduction is controlled by the mixed internal diffusion and interfacial reaction at the initial stage; however, the interfacial reaction is dominant. As the reduction proceeds, the internal diffusion becomes the controlling step.展开更多
To achieve the high-efficiency utilization of vanadium-titanium magnetite( VTM),reduction experiments were conducted to determine the carbothermic reduction mechanism of VTM. Effects of volatile matter,temperature,t...To achieve the high-efficiency utilization of vanadium-titanium magnetite( VTM),reduction experiments were conducted to determine the carbothermic reduction mechanism of VTM. Effects of volatile matter,temperature,time,and carbon ratio( molar ratio of fixed carbon in coal to oxygen in iron oxides of VTM) on reduction degree were investigated.Results show that reduction degree increases with increasing volatile matter in coal,temperature,time,and carbon ratio.Phase transformation,microstructure,and reduction path were analyzed by X-ray diffraction,scanning electron microscopy,energy-dispersive X-ray spectroscopy,and Fact Sage 6. 0. The thermoravimetry-differential scanning calorimetry-quadrupole mass spectrometer method was used for kinetic analysis of the main reduction process. Results indicate that the kinetic mechanism follows the principle of random nucleation and growth( n = 4),and the activation energy values at 600-900 and 900-1 350 ℃ are 88. 7 and 295. 5 kJ / mol,respectively.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51090384)the National High-Tech Research and Development Program of China (No. 2012AA062302)the Fundamental Research Funds for the Central Universities of China (Nos. N110202001 and N130602003)
文摘The reduction of high-chromium vanadium–titanium magnetite as a typical titanomagnetite containing 0.95wt% V2O5 and 0.61wt% Cr2O3 by H2–CO–CO2 gas mixtures was investigated from 1223 to 1373 K. Both the reduction degree and reduction rate increase with increasing temperature and increasing hydrogen content. At a temperature of 1373 K, an H2/CO ratio of 5/2 by volume, and a reduction time of 40 min, the degree of reduction reaches 95%. The phase transformation during reduction is hypothesized to proceed as follows: Fe2O3 → Fe3O4 → FeO → Fe; Fe9 TiO 15 + Fe2Ti3O9 → Fe2.75Ti0.25O4 → FeT iO 3 → TiO 2;(Cr0.15V0.85)2O3 → Fe2VO4; and Cr1.3Fe0.7O3 → FeC r2O4. The reduction is controlled by the mixed internal diffusion and interfacial reaction at the initial stage; however, the interfacial reaction is dominant. As the reduction proceeds, the internal diffusion becomes the controlling step.
基金Item Sponsored by National High-tech Research and Development Project of China(2012AA062302)Major Program of National Natural Science Foundation of China(51090384)Fundamental Research Funds for the Central Universities of China(N130602003)
文摘To achieve the high-efficiency utilization of vanadium-titanium magnetite( VTM),reduction experiments were conducted to determine the carbothermic reduction mechanism of VTM. Effects of volatile matter,temperature,time,and carbon ratio( molar ratio of fixed carbon in coal to oxygen in iron oxides of VTM) on reduction degree were investigated.Results show that reduction degree increases with increasing volatile matter in coal,temperature,time,and carbon ratio.Phase transformation,microstructure,and reduction path were analyzed by X-ray diffraction,scanning electron microscopy,energy-dispersive X-ray spectroscopy,and Fact Sage 6. 0. The thermoravimetry-differential scanning calorimetry-quadrupole mass spectrometer method was used for kinetic analysis of the main reduction process. Results indicate that the kinetic mechanism follows the principle of random nucleation and growth( n = 4),and the activation energy values at 600-900 and 900-1 350 ℃ are 88. 7 and 295. 5 kJ / mol,respectively.