Double main phase process is applied to fabricate [(Pr, Nd)1 – xMMx]13.8FebalM1.5B5.9 (x = 0.5 and 0.7;M = Cu, Al, Co, and Nb) sintered magnets with high misch metal (MM) content. In comparison to the magnets by sing...Double main phase process is applied to fabricate [(Pr, Nd)1 – xMMx]13.8FebalM1.5B5.9 (x = 0.5 and 0.7;M = Cu, Al, Co, and Nb) sintered magnets with high misch metal (MM) content. In comparison to the magnets by single main phase process, the enhanced magnetic properties have been achieved. For magnets of x = 0.7, Hcj increases to 371.9 kA/m by 60.5%, and (BH)max is significantly enhanced to 253.3 kJ/m3 by 56.9%, compared with those of the single main phase magnets of the same nominal composition. In combination with minor loops and magnetic recoil curves, the property improvement of magnets with double main phase method is well explained. As a result, it is demonstrated that double main phase technology is an effective approach to improve the permanent magnetic properties of MM based sintered magnets.展开更多
基金Project supported by the National Natural Foundation of China(Grant Nos.51590880,11564030,and 51571126)the National Key Research Program of China(Grant No.2016YFB0700903)+3 种基金Fujian Institute of Innovation,Chinese Academy of Sciences(Grant No.FJCXY18040302)the Key Program of the Chinese Academy of Sciences(Grant No.KJZD-EW-M05-1)the Inner Mongolia Science and Technology Major Project of 2016,Chinathe Natural Science Foundation of Inner Mongolia,China(Grant Nos.2018LH05006 and 2018LH05011)。
文摘Double main phase process is applied to fabricate [(Pr, Nd)1 – xMMx]13.8FebalM1.5B5.9 (x = 0.5 and 0.7;M = Cu, Al, Co, and Nb) sintered magnets with high misch metal (MM) content. In comparison to the magnets by single main phase process, the enhanced magnetic properties have been achieved. For magnets of x = 0.7, Hcj increases to 371.9 kA/m by 60.5%, and (BH)max is significantly enhanced to 253.3 kJ/m3 by 56.9%, compared with those of the single main phase magnets of the same nominal composition. In combination with minor loops and magnetic recoil curves, the property improvement of magnets with double main phase method is well explained. As a result, it is demonstrated that double main phase technology is an effective approach to improve the permanent magnetic properties of MM based sintered magnets.