This paper reports that the transient laser-induced voltages have been observed in La2/3Ca1/3MnO3 thin films on MgO （001） in the absence of an applied current. A peak voltage of - 0.15 V was detected in response to ...This paper reports that the transient laser-induced voltages have been observed in La2/3Ca1/3MnO3 thin films on MgO （001） in the absence of an applied current. A peak voltage of - 0.15 V was detected in response to 0.015J pulse of 308 nm laser. It is demonstrated that the signal polarity is reversed when the films are irradiated through the substrate rather than at the air/film interface. Off-diagonal thermoelectricity may support the inversion of the signal when the irradiation direction is reversed.展开更多
The La2/3Cal/3Mn03_σ film has been deposited on the （001） SrTiO3 substrate and its temper- ature-dependent photoconductive properties have been investigated from 80 to 300 K. The La2/3Cal/3MnO3-σ film has a novel ...The La2/3Cal/3Mn03_σ film has been deposited on the （001） SrTiO3 substrate and its temper- ature-dependent photoconductive properties have been investigated from 80 to 300 K. The La2/3Cal/3MnO3-σ film has a novel photoelectric property due to its oxygen-deficient structure. We observed laser-induced giant negative photoresistance of the sample in a wide temperature range. The change rate of negative photoresistance was nearly 100% at the low temperature when the sample was irradiated by 532 nm laser. In addition, this effect was sensitive to the power of laser irradiation. The oxygen-deficiency of La2/3Cal/3Mn03-σ film seems to have an impact on the laser-induced resistance variation. The experimental results made the La2/3Cal/3MnO3_σ film a promising application as a photoswitch device.展开更多
基金Project supported by the National Natural Science Foundation of China （Grant Nos 60576015 and 50672132）.
文摘This paper reports that the transient laser-induced voltages have been observed in La2/3Ca1/3MnO3 thin films on MgO （001） in the absence of an applied current. A peak voltage of - 0.15 V was detected in response to 0.015J pulse of 308 nm laser. It is demonstrated that the signal polarity is reversed when the films are irradiated through the substrate rather than at the air/film interface. Off-diagonal thermoelectricity may support the inversion of the signal when the irradiation direction is reversed.
基金supported by National Basic Research Program of China(973 Program)(Grant No.2014CB7443-02)Specially Founded Program on National Key Scientific Instruments and Equipment Development(Grant No.2012YQ140005)
文摘The La2/3Cal/3Mn03_σ film has been deposited on the （001） SrTiO3 substrate and its temper- ature-dependent photoconductive properties have been investigated from 80 to 300 K. The La2/3Cal/3MnO3-σ film has a novel photoelectric property due to its oxygen-deficient structure. We observed laser-induced giant negative photoresistance of the sample in a wide temperature range. The change rate of negative photoresistance was nearly 100% at the low temperature when the sample was irradiated by 532 nm laser. In addition, this effect was sensitive to the power of laser irradiation. The oxygen-deficiency of La2/3Cal/3Mn03-σ film seems to have an impact on the laser-induced resistance variation. The experimental results made the La2/3Cal/3MnO3_σ film a promising application as a photoswitch device.