The diffusion property of sulfur on the soda-lime-silicate float glass surface was studied by using secondary ion mass spectroscopy(SIMS).According to the Fick's Second Law,two models of diffusion of sulfur on the ...The diffusion property of sulfur on the soda-lime-silicate float glass surface was studied by using secondary ion mass spectroscopy(SIMS).According to the Fick's Second Law,two models of diffusion of sulfur on the glass surface were built.When the diffusion of sulfate(S^6+) is considered uniquely,the concentration-depth profile of sulfur can not be fitted very well,especially on the top surfaces of the air side and tin side of float glass.So the diffusion of sulfide(S^2-) on the profile of sulfur can not be ignored.The concentration-depth profile of sulfur on both sides of glass can be fitted more exactly when both S^6+ and S^2- are considerd.Based on the above-mentioned fitting results,it is concluded that the diffusion coefficents of S^6+ and S^2- of tin side are larger than those of the air side.Moreover,the diffusion coefficents are related to the contacted medium.展开更多
基金Funded by National Natural Science Foundation of China(NSFC)(No.50972136)National Science and Technology S upporting P rogram(No.2015BAA02B00)+1 种基金National Key Technologies R&D Program(No.2016YFB0303900)the Fundamental Research Funds of State Key Laboratory for Advanced Technology of Float Glass
文摘The diffusion property of sulfur on the soda-lime-silicate float glass surface was studied by using secondary ion mass spectroscopy(SIMS).According to the Fick's Second Law,two models of diffusion of sulfur on the glass surface were built.When the diffusion of sulfate(S^6+) is considered uniquely,the concentration-depth profile of sulfur can not be fitted very well,especially on the top surfaces of the air side and tin side of float glass.So the diffusion of sulfide(S^2-) on the profile of sulfur can not be ignored.The concentration-depth profile of sulfur on both sides of glass can be fitted more exactly when both S^6+ and S^2- are considerd.Based on the above-mentioned fitting results,it is concluded that the diffusion coefficents of S^6+ and S^2- of tin side are larger than those of the air side.Moreover,the diffusion coefficents are related to the contacted medium.