Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality （MIFQ） is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study,...Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality （MIFQ） is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study, a new durability analysis method is presented. In this method, S-N curve is used to determine crack growth rate under constant amplitude loading and evaluate the effects of different factors on durability and then the structural durability is analyzed. The tests and analyses indicate that this method has lower dependence on testing, and higher accuracy, reliability and generality and is convenient for application.展开更多
Based on the evolution of fatigue cracks in welded structures,the fatigue life of welded structures was defined as the sum of the crack initiation life Ni and the crack propagation life Np.Correspondingly,a fatigue-li...Based on the evolution of fatigue cracks in welded structures,the fatigue life of welded structures was defined as the sum of the crack initiation life Ni and the crack propagation life Np.Correspondingly,a fatigue-life analysis method combining S-N curves and fracture mechanics theory was proposed.The equivalent structural stress method and the lower 99%boundary of the master S-N curve were used to evaluate Ni,and cracks at the end of the initiation stage were considered as semi-elliptical surface cracks.Moreover,Paris equation and the stress intensity factor range of the cracks were used to evaluate Np.Furthermore,the fatigue test results obtained from the running girder of cranes were used as a reference for comparison and verification of the results.The results revealed that the equivalent structural stress is a good indicator for the crack initiation behavior of complex welded structures.In addition,the predicted fatigue life corresponded closely to the testing life.展开更多
When the historic probabilistic S-N curves are given under special survival probability and confidence levels and there is no possible to re-test, fatigue reliability analysis at other levels can not be done except fo...When the historic probabilistic S-N curves are given under special survival probability and confidence levels and there is no possible to re-test, fatigue reliability analysis at other levels can not be done except for the special levels. Therefore, the wide applied curves are expected. Monte Carlo reconstruction methods of the test data and the curves are investigated under fatigue life following lognormal distribution. To overcome the non-conservative assessment of existent man-made enlarging the sample size up to thousands, a simulation policy is employed to address the true production where the sample size is controlled less than 20 for material specimens, 10 for structural component specimens and the errors matching the statistical parameters are less than 5 percent. Availability and feasibility of the present methods have been indicated by the reconstruction practice of the test data and curves for 60Si2Mn high strength spring steel of railway industry.展开更多
ΔF-N curves are usually used to predict the fatigue life of spot welding in engineering,but they are time-consuming and laborious and not universal.For the purpose of predicting the fatigue life of spot welding accur...ΔF-N curves are usually used to predict the fatigue life of spot welding in engineering,but they are time-consuming and laborious and not universal.For the purpose of predicting the fatigue life of spot welding accurately and efficiently,tensile-shear fatigue tests were conducted to obtain the fatigue life of spot-welded specimens with different sheet thicknesses combinations.These specimens were simulated by using the finite element method,and the structural stress was theoretically calculated.In the double logarithmic coordinate system,the structural stress-fatigue life(S-N)curve of spot welding was fitted by the least-squares method,based on the quasi-Newton method.The square of the correlation coefficient of the S-N curve was taken as the optimization objective,with the correction coefficients of force,bending moment,spot welding diameter,and sheet thickness as the variables.During the optimization process,three different ways were utilized to get three optimized spot welding S-N curves,which are suitable for different situations.The results show that the fitting effect of the S-N curve is improved,the data points are more compact,and the optimization effect is significant.These S-N curves can be used to predict the fatigue life,which provide the basis for practical engineering application.展开更多
With the popularization of friction stir welding(FSW),5083-H321 and 6061-T6 aluminum alloy materials are widely used during the FSW process.In this study,the fatigue life of friction stir welding with two materials,i....With the popularization of friction stir welding(FSW),5083-H321 and 6061-T6 aluminum alloy materials are widely used during the FSW process.In this study,the fatigue life of friction stir welding with two materials,i.e.,5083-H321 and 6061-T6 aluminum alloy,are studied.Fatigue tests were carried out on the base metal of these two materials as well as on the butt joints and overlapping FSW samples.The principle of the equivalent structural stress method is used to analyze the FSW test data of these two materials.The fatigue resistances of these two materials were com-pared and a unified principal S-N curve equation was fitted.Two key parameters of the unified principal S-N curve obtained by fitting,Cd is 4222.5,and h is 0.2693.A new method for an FSW fatigue life assessment was developed in this study and can be used to calculate the fatigue life of different welding forms with a single S-N curve.Two main fatigue tests of bending and tension were used to verify the unified principal S-N curve equation.The results show that the fatigue life calculated by the unified mean 50%master S-N curve parameters are the closest to the fatigue test results.The reliability,practicability,and generality of the master S-N curve fitting parameters were verified using the test data.The unified principal S-N curve acquired in this study can not only be used in aluminum alloy materials but can also be applied to other materials.展开更多
基金National Natural Science Foundation of China (60472118) High-tech Research Project of Jiangsu Province (BG2004008)
文摘Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality （MIFQ） is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study, a new durability analysis method is presented. In this method, S-N curve is used to determine crack growth rate under constant amplitude loading and evaluate the effects of different factors on durability and then the structural durability is analyzed. The tests and analyses indicate that this method has lower dependence on testing, and higher accuracy, reliability and generality and is convenient for application.
基金Project was supported by the National Nature Science Foundation of China(51575408).
文摘Based on the evolution of fatigue cracks in welded structures,the fatigue life of welded structures was defined as the sum of the crack initiation life Ni and the crack propagation life Np.Correspondingly,a fatigue-life analysis method combining S-N curves and fracture mechanics theory was proposed.The equivalent structural stress method and the lower 99%boundary of the master S-N curve were used to evaluate Ni,and cracks at the end of the initiation stage were considered as semi-elliptical surface cracks.Moreover,Paris equation and the stress intensity factor range of the cracks were used to evaluate Np.Furthermore,the fatigue test results obtained from the running girder of cranes were used as a reference for comparison and verification of the results.The results revealed that the equivalent structural stress is a good indicator for the crack initiation behavior of complex welded structures.In addition,the predicted fatigue life corresponded closely to the testing life.
基金Project supported by the National High Technology Research and Development Program of China(863 Program) (No.2006AA04Z406)the National Natural Science Foundation of China (Nos.50375130, 50323003 and 50575189)+1 种基金the Special Foundation for the Authors of National Excellent Doctoral Dissertations (No.200234)the Program for New Century Excellent Talents in University(No.NCET040890)
文摘When the historic probabilistic S-N curves are given under special survival probability and confidence levels and there is no possible to re-test, fatigue reliability analysis at other levels can not be done except for the special levels. Therefore, the wide applied curves are expected. Monte Carlo reconstruction methods of the test data and the curves are investigated under fatigue life following lognormal distribution. To overcome the non-conservative assessment of existent man-made enlarging the sample size up to thousands, a simulation policy is employed to address the true production where the sample size is controlled less than 20 for material specimens, 10 for structural component specimens and the errors matching the statistical parameters are less than 5 percent. Availability and feasibility of the present methods have been indicated by the reconstruction practice of the test data and curves for 60Si2Mn high strength spring steel of railway industry.
基金Supported by National Natural Science Foundation of China(Grant Nos.U1534209,51675446)Independent Subject of State Key Laboratory of Traction Power(Grant No.2019TPL-T13).
文摘ΔF-N curves are usually used to predict the fatigue life of spot welding in engineering,but they are time-consuming and laborious and not universal.For the purpose of predicting the fatigue life of spot welding accurately and efficiently,tensile-shear fatigue tests were conducted to obtain the fatigue life of spot-welded specimens with different sheet thicknesses combinations.These specimens were simulated by using the finite element method,and the structural stress was theoretically calculated.In the double logarithmic coordinate system,the structural stress-fatigue life(S-N)curve of spot welding was fitted by the least-squares method,based on the quasi-Newton method.The square of the correlation coefficient of the S-N curve was taken as the optimization objective,with the correction coefficients of force,bending moment,spot welding diameter,and sheet thickness as the variables.During the optimization process,three different ways were utilized to get three optimized spot welding S-N curves,which are suitable for different situations.The results show that the fitting effect of the S-N curve is improved,the data points are more compact,and the optimization effect is significant.These S-N curves can be used to predict the fatigue life,which provide the basis for practical engineering application.
基金Supported by Department of Education of Liaoning Province(Grant No.JDL2020019)Dalian High Level Talents Project(Grant No.2017RQ132).
文摘With the popularization of friction stir welding(FSW),5083-H321 and 6061-T6 aluminum alloy materials are widely used during the FSW process.In this study,the fatigue life of friction stir welding with two materials,i.e.,5083-H321 and 6061-T6 aluminum alloy,are studied.Fatigue tests were carried out on the base metal of these two materials as well as on the butt joints and overlapping FSW samples.The principle of the equivalent structural stress method is used to analyze the FSW test data of these two materials.The fatigue resistances of these two materials were com-pared and a unified principal S-N curve equation was fitted.Two key parameters of the unified principal S-N curve obtained by fitting,Cd is 4222.5,and h is 0.2693.A new method for an FSW fatigue life assessment was developed in this study and can be used to calculate the fatigue life of different welding forms with a single S-N curve.Two main fatigue tests of bending and tension were used to verify the unified principal S-N curve equation.The results show that the fatigue life calculated by the unified mean 50%master S-N curve parameters are the closest to the fatigue test results.The reliability,practicability,and generality of the master S-N curve fitting parameters were verified using the test data.The unified principal S-N curve acquired in this study can not only be used in aluminum alloy materials but can also be applied to other materials.