How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion stre...How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion strengthened iron alloy with high strength and appreciable ductility was fabricated by solution combustion route and subsequent spark plasma sintering, and the influences of yttrium oxide content and sintering temperature on microstructures and mechanical properties were investigated. The results show at the same sintering temperature,with the increase of yttrium oxide content, the relative density of the sintered alloy decreases and the strength increases. For Fe–2wt%Y_(2)O_(3)alloy, as the sintering temperature increases gradually, the compressive strength decreases, while the strain-to-failure increases. The Fe–2wt%Y_(2)O_(3)alloy with 15.5 nm Y_(2)O_(3)particles uniformly distributed into the 147.5 nm iron grain interior sintered at 650℃ presents a high ultimate compressive strength of 1.86 GPa and large strain-to-failure of 29%. The grain boundary strengthening and intragranular second-phase particle dispersion strengthening are the main dominant mechanisms to enhance the mechanical properties of the alloy.展开更多
The mechanical and tribological properties of Cu-based powder metallurgy （P/M） friction composites containing 10wt%-50wt% oxide-dispersion-strengthened （ODS） Cu reinforced with nano-Al2O3 were investigated. Additi...The mechanical and tribological properties of Cu-based powder metallurgy （P/M） friction composites containing 10wt%-50wt% oxide-dispersion-strengthened （ODS） Cu reinforced with nano-Al2O3 were investigated. Additionally, the friction and wear behaviors as well as the wear mechanism of the Cu-based composites were characterized by scanning electron microscopy （SEM） in conjunction with energy-dispersive X-ray spectroscopy （EDS） elemental mapping. The results indicated that the Cu-based friction composite containing 30wt% ODS Cu exhibited the highest hardness and shear strength. The average and instantaneous friction coefficient curves of this sample, when operated in a high-speed train at a speed of 300 km/h, were similar to those of a commercial disc brake pad produced by Knorr-Bremse AG （Germany）. Additionally, the lowest linear wear loss of the obtained samples was （0.008 ± 0.001） mm per time per face, which is much lower than that of the Knorr-Bremse pad （（0.01 ± 0.001） mm）. The excellent performance of the developed pad is a consequence of the formation of a dense oxide composite layer and its close combination with the pad body.展开更多
A discrete dislocation plasticity analysis of dispersion strengthening in oxide dispersion strengthened(ODS) steels was described. Parametric dislocation dynamics(PDD) simulation of the interaction between an edge dis...A discrete dislocation plasticity analysis of dispersion strengthening in oxide dispersion strengthened(ODS) steels was described. Parametric dislocation dynamics(PDD) simulation of the interaction between an edge dislocation and randomly distributed spherical dispersoids(Y2O3) in bcc iron was performed for measuring the influence of the dispersoid distribution on the critical resolved shear stress(CRSS). The dispersoid distribution was made using a method mimicking the Ostwald growth mechanism. Then, an edge dislocation was introduced, and was moved under a constant shear stress condition. The CRSS was extracted from the result of dislocation velocity under constant shear stress using the mobility(linear) relationship between the shear stress and the dislocation velocity. The results suggest that the dispersoid distribution gives a significant influence to the CRSS, and the influence of dislocation dipole, which forms just before finishing up the Orowan looping mechanism, is substantial in determining the CRSS, especially for the interaction with small dispersoids. Therefore, the well-known Orowan equation for determining the CRSS cannot give an accurate estimation, because the influence of the dislocation dipole in the process of the Orowan looping mechanism is not accounted for in the equation.展开更多
Dispersoid formation and microstructural evolution in an oxide dispersion-strengthened CoCrFeMnNi high-entropy alloy(HEA)using a newly designed multistep sintering process are investigated.The proposed multistep sinte...Dispersoid formation and microstructural evolution in an oxide dispersion-strengthened CoCrFeMnNi high-entropy alloy(HEA)using a newly designed multistep sintering process are investigated.The proposed multistep sintering consists of a dispersoid preforming heat treatment of as-milled 0.1 wt%Y_(2)O_(3)-CoCrFeMnNi high-entropy alloy powders at 800℃,followed by sintering at 800–1000℃ under uniaxial pressure.In the conventional single-step sintered bulk,the coarsened BCC Y_(2)O_(3)dispersoids mainly form with an incoherent interface with the HEA matrix.In contrast,finer FCC Y_(2)O_(3)dispersoids,an atypical form of Y_(2)O_(3),are formed in the matrix region after multistep sintering.Nucleation of FCC Y_(2)O_(3)disper-soids is initiated on the favorable facet,the{111}plane of the austenitic matrix,with the formation of a semi-coherent interface with the matrix during the dispersoid preforming heat treatment and it maintains its refined size even after sintering.It is found that dispersoid preforming prior to sintering appears promising to control the finer dispersoid formation and refined grain structure.展开更多
The relationship of the yttrium compounds with its alloying method has been studied, the alloying methods studied including MA and CA (Mechanical Alloying and Chemical Alloying). The results show that the compound in ...The relationship of the yttrium compounds with its alloying method has been studied, the alloying methods studied including MA and CA (Mechanical Alloying and Chemical Alloying). The results show that the compound in CA steel is Y2Ti2O7 but that in MA steel is Y2O3. The statistical analysis confirms that the titanium contents in the two compounds are different apparently. However, the yttrium content maintains constant.展开更多
Development of the technological process for brazing of heat-resistant copper alloy strengthened with Al2O3 oxide particles is an important task of fabrication of high-temperature application structures. As mechanical...Development of the technological process for brazing of heat-resistant copper alloy strengthened with Al2O3 oxide particles is an important task of fabrication of high-temperature application structures. As mechanical properties of the brazed joints directly depend on the structural factor and morphological peculiarities of the brazed seams, the latter are of technological interest in terms of making of permanent joints. This study gives results of X-ray spectral microanalysis of the brazed joints on dispersion-strengthened copper alloy （ Gridcop Al-25 ） produced by using the Ti-Cu system adhesion-active brazing filler alloy, different heat sources and temperature-time parameters of the brazing process. Shown are differences in formation of structure of the seams made by vacuum brazing using radiation and high-frequency heating. Vacuum brazing with radiation heating provides the homogeneous seams with crystallisation of the phases based on the CuTi and CuTi2 compounds in the form of discrete faceted particles 2 - 9μm in size against the background of the copper matrix. Based on investigation of structural peculiarities of the brazed seams, the temperature-time conditions of vacuum brazing with radiation heating were selected for manufacture of specimens for mechanical tests. Analysis of the results of strength tests of the butt brazed specimens proved the expediency of preliminary heat treatment of the base material, providing strength of the joints at a level of about 92% of that of the base material.展开更多
Oxide-dispersion-strengthened （ODS） ferritic steels are promising candidates for structural applications in the future nuclear reactors. The higher chromium contents of ODS ferritic steels, the better the corrosion ...Oxide-dispersion-strengthened （ODS） ferritic steels are promising candidates for structural applications in the future nuclear reactors. The higher chromium contents of ODS ferritic steels, the better the corrosion resistance, which can meet the harsh corrosion environment of the advanced reactors. However, increasing the Cr content may also lead to the brittleness of the ODS steels when serving at high temperatures. The ODS ferritic steels with different Cr contents （12, 16 and 18 wt% Cr, respectively） were fabricated by mechanical alloying, hot isostatic pressing and forging. Mechanical properties and microstructure evolution of the ODS ferritic steels after aging at 753 K for 2000 h were investigated. It is found that both Vickers hardness and yield strength of 18%Cr ODS ferritic steel were strongly increased and the impact energy was decreased after aging at 753 K. In order to explore the reasons for changes in the mechanical properties, the fracture surfaces were characterized by scanning electron microscopy, and microstructures after aging were observed by transmission electron microscopy. The impact fracture of 18%Cr ODS ferritic steel belongs to quasi-cleavage facture, which is consistent with its very low impact energy. The grain size and dispersed oxide particles of different ODS steels are very stable. M23C6 carbide and M2C carbide were found in 12%Cr ODS steel and 16%Cr ODS steels, respectively.展开更多
基金financially supported by the Guangdong Basic and Applied Basic Research Foundation,China (No.2021A1515110202)the Natural Science Foundation Program of Beijing,China (Nos.2224104,2202031,2174079+6 种基金2162027)the National Natural Science Foundation Program of China (Nos.52131307,52130407,52071013,52104359,51774035,and 52174344)the Scientific and Technological Innovation Foundation of Foshan,China (No.BK21BE007)the National Key Research and Development Program of China (Nos.2021YFB3701900,2022YFB3705400,and 2022YFB3708800)the Beijing Municipal Science & Technology Commission,Administrative Commission of Zhongguancun Science Park,China (No.Z221100005822001)the S&T Program of Hebei,China(No.20311001D)the Fundamental Research Funds for the Central Universities (Nos.FRF-IDRY-20-022,FRF-TP-20-032A2,FRF-TP-20-100A1Z,and FRF-IDRY-22-030)。
文摘How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion strengthened iron alloy with high strength and appreciable ductility was fabricated by solution combustion route and subsequent spark plasma sintering, and the influences of yttrium oxide content and sintering temperature on microstructures and mechanical properties were investigated. The results show at the same sintering temperature,with the increase of yttrium oxide content, the relative density of the sintered alloy decreases and the strength increases. For Fe–2wt%Y_(2)O_(3)alloy, as the sintering temperature increases gradually, the compressive strength decreases, while the strain-to-failure increases. The Fe–2wt%Y_(2)O_(3)alloy with 15.5 nm Y_(2)O_(3)particles uniformly distributed into the 147.5 nm iron grain interior sintered at 650℃ presents a high ultimate compressive strength of 1.86 GPa and large strain-to-failure of 29%. The grain boundary strengthening and intragranular second-phase particle dispersion strengthening are the main dominant mechanisms to enhance the mechanical properties of the alloy.
基金financially supported by the National High Technology Research and Development Program of China (No. 2013AA031104)
文摘The mechanical and tribological properties of Cu-based powder metallurgy （P/M） friction composites containing 10wt%-50wt% oxide-dispersion-strengthened （ODS） Cu reinforced with nano-Al2O3 were investigated. Additionally, the friction and wear behaviors as well as the wear mechanism of the Cu-based composites were characterized by scanning electron microscopy （SEM） in conjunction with energy-dispersive X-ray spectroscopy （EDS） elemental mapping. The results indicated that the Cu-based friction composite containing 30wt% ODS Cu exhibited the highest hardness and shear strength. The average and instantaneous friction coefficient curves of this sample, when operated in a high-speed train at a speed of 300 km/h, were similar to those of a commercial disc brake pad produced by Knorr-Bremse AG （Germany）. Additionally, the lowest linear wear loss of the obtained samples was （0.008 ± 0.001） mm per time per face, which is much lower than that of the Knorr-Bremse pad （（0.01 ± 0.001） mm）. The excellent performance of the developed pad is a consequence of the formation of a dense oxide composite layer and its close combination with the pad body.
文摘A discrete dislocation plasticity analysis of dispersion strengthening in oxide dispersion strengthened(ODS) steels was described. Parametric dislocation dynamics(PDD) simulation of the interaction between an edge dislocation and randomly distributed spherical dispersoids(Y2O3) in bcc iron was performed for measuring the influence of the dispersoid distribution on the critical resolved shear stress(CRSS). The dispersoid distribution was made using a method mimicking the Ostwald growth mechanism. Then, an edge dislocation was introduced, and was moved under a constant shear stress condition. The CRSS was extracted from the result of dislocation velocity under constant shear stress using the mobility(linear) relationship between the shear stress and the dislocation velocity. The results suggest that the dispersoid distribution gives a significant influence to the CRSS, and the influence of dislocation dipole, which forms just before finishing up the Orowan looping mechanism, is substantial in determining the CRSS, especially for the interaction with small dispersoids. Therefore, the well-known Orowan equation for determining the CRSS cannot give an accurate estimation, because the influence of the dislocation dipole in the process of the Orowan looping mechanism is not accounted for in the equation.
基金supported by the National Research Foundation of the Ministry of Science and ICT(MSIT)of the Republic of Korea(Nos.2021R1A2C2014025,2020R1A5A6017701,and 2022M3H4A1A02076759)。
文摘Dispersoid formation and microstructural evolution in an oxide dispersion-strengthened CoCrFeMnNi high-entropy alloy(HEA)using a newly designed multistep sintering process are investigated.The proposed multistep sintering consists of a dispersoid preforming heat treatment of as-milled 0.1 wt%Y_(2)O_(3)-CoCrFeMnNi high-entropy alloy powders at 800℃,followed by sintering at 800–1000℃ under uniaxial pressure.In the conventional single-step sintered bulk,the coarsened BCC Y_(2)O_(3)dispersoids mainly form with an incoherent interface with the HEA matrix.In contrast,finer FCC Y_(2)O_(3)dispersoids,an atypical form of Y_(2)O_(3),are formed in the matrix region after multistep sintering.Nucleation of FCC Y_(2)O_(3)disper-soids is initiated on the favorable facet,the{111}plane of the austenitic matrix,with the formation of a semi-coherent interface with the matrix during the dispersoid preforming heat treatment and it maintains its refined size even after sintering.It is found that dispersoid preforming prior to sintering appears promising to control the finer dispersoid formation and refined grain structure.
基金supported by the Major State Basic Research Development Program of China (973 Program) (No. 2008cb7178020)the State Key Laboratory for Advanced Metals and Materials of the University of Science and Technology Beijing
文摘The relationship of the yttrium compounds with its alloying method has been studied, the alloying methods studied including MA and CA (Mechanical Alloying and Chemical Alloying). The results show that the compound in CA steel is Y2Ti2O7 but that in MA steel is Y2O3. The statistical analysis confirms that the titanium contents in the two compounds are different apparently. However, the yttrium content maintains constant.
文摘Development of the technological process for brazing of heat-resistant copper alloy strengthened with Al2O3 oxide particles is an important task of fabrication of high-temperature application structures. As mechanical properties of the brazed joints directly depend on the structural factor and morphological peculiarities of the brazed seams, the latter are of technological interest in terms of making of permanent joints. This study gives results of X-ray spectral microanalysis of the brazed joints on dispersion-strengthened copper alloy （ Gridcop Al-25 ） produced by using the Ti-Cu system adhesion-active brazing filler alloy, different heat sources and temperature-time parameters of the brazing process. Shown are differences in formation of structure of the seams made by vacuum brazing using radiation and high-frequency heating. Vacuum brazing with radiation heating provides the homogeneous seams with crystallisation of the phases based on the CuTi and CuTi2 compounds in the form of discrete faceted particles 2 - 9μm in size against the background of the copper matrix. Based on investigation of structural peculiarities of the brazed seams, the temperature-time conditions of vacuum brazing with radiation heating were selected for manufacture of specimens for mechanical tests. Analysis of the results of strength tests of the butt brazed specimens proved the expediency of preliminary heat treatment of the base material, providing strength of the joints at a level of about 92% of that of the base material.
文摘Oxide-dispersion-strengthened （ODS） ferritic steels are promising candidates for structural applications in the future nuclear reactors. The higher chromium contents of ODS ferritic steels, the better the corrosion resistance, which can meet the harsh corrosion environment of the advanced reactors. However, increasing the Cr content may also lead to the brittleness of the ODS steels when serving at high temperatures. The ODS ferritic steels with different Cr contents （12, 16 and 18 wt% Cr, respectively） were fabricated by mechanical alloying, hot isostatic pressing and forging. Mechanical properties and microstructure evolution of the ODS ferritic steels after aging at 753 K for 2000 h were investigated. It is found that both Vickers hardness and yield strength of 18%Cr ODS ferritic steel were strongly increased and the impact energy was decreased after aging at 753 K. In order to explore the reasons for changes in the mechanical properties, the fracture surfaces were characterized by scanning electron microscopy, and microstructures after aging were observed by transmission electron microscopy. The impact fracture of 18%Cr ODS ferritic steel belongs to quasi-cleavage facture, which is consistent with its very low impact energy. The grain size and dispersed oxide particles of different ODS steels are very stable. M23C6 carbide and M2C carbide were found in 12%Cr ODS steel and 16%Cr ODS steels, respectively.