The α-SiC in 0.5μm size powders were coated with Al_2O_3 and Y_2O_3 by a coprecipitation coating (CPC) method forfabrication of SiC/YAG composites. The same powder preparation was carried out by conventional mechani...The α-SiC in 0.5μm size powders were coated with Al_2O_3 and Y_2O_3 by a coprecipitation coating (CPC) method forfabrication of SiC/YAG composites. The same powder preparation was carried out by conventional mechanical mixing(MM) method for comparison. Two kinds of SiC/YAG composites were manufactured by pressureless sintering usingthe different powders, named CPC composite and MM composite thereafter respectively. It is shown that the CPCcomposite has the advantages of homogeneous distribution of YAG phase and of being sintered to high density ata low temperature, 100℃ lower than that of MM composite. The strength (573 MPa) and hardness (23.3 GPa) ofthe CPC composite are significantly higher than those (323 MPa and 13.5 GPa) of the MM composite, respectively.展开更多
基金This work was supported by the National Natural Science Foundation of China(No.50372041)National“863”Plan(No.2003AA305620).
文摘The α-SiC in 0.5μm size powders were coated with Al_2O_3 and Y_2O_3 by a coprecipitation coating (CPC) method forfabrication of SiC/YAG composites. The same powder preparation was carried out by conventional mechanical mixing(MM) method for comparison. Two kinds of SiC/YAG composites were manufactured by pressureless sintering usingthe different powders, named CPC composite and MM composite thereafter respectively. It is shown that the CPCcomposite has the advantages of homogeneous distribution of YAG phase and of being sintered to high density ata low temperature, 100℃ lower than that of MM composite. The strength (573 MPa) and hardness (23.3 GPa) ofthe CPC composite are significantly higher than those (323 MPa and 13.5 GPa) of the MM composite, respectively.