Improvement of Mechanical,Dynamic-Mechanical and Thermal Properties for Noil Ramie Fiber Reinforced Polyethylene Composites

Noil discarded fibers from fiber production for textile industry have short length and are always considered less valuable.Here,noil ramie fibers/HDPE composite is prepared using twin-screw extruder and the dynamic mechanical and thermal properties are studied.The influence of ramie fiber and maleic anhydride-grafted polyolefin(MA-g-PO)on mechanical,dynamic mechanical and thermal properties is investigated.It is observed that the tensile,flexural and impact properties of the composites treated with MA-g-PO are all improved in comparison to the untreated composites.Dynamic mechanical properties of the composite with MA-g-PO show an increase in the storage modulus with a higherαrelaxation peak,together with the micromorphology analysis,indicating an improved interfacial bonding between fiber and matrix by the MA-g-PO addition.Furthermore,the change in TGA thermograms of composite caused by MA-g-PO exhibits that the addition of MA-g-PO is also helpful to increase the thermal stability of noil ramie fiber/HDPE composites.

Influence of FeCrAl fiber on microstructure and mechanical properties of FeCrAl(f)/HA composites

FeCrAl fiber-reinforced hydroxyapatite（HA） biocomposites（FeCrAl（f）/HA） were fabricated by the hot pressing technique.The metallographic microscopy,X-ray diffractometry,scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS） were used to observe and analyze the microstructure and composition of FeCrAl（f）/HA composites,respectively.The mechanical properties of FeCrAl（f）/HA composites were measured by the three-point-bending test.The results show that the composite can be reinforced by FeCrAl fiber and enhanced gradually,and then declined with the increase of the content of FeCrAl fiber（0-11%,volume fraction） in the whole range of experiments.Both the HA matrix and FeCrAl fiber integrate very tightly and bit into each other very deeply and counter-diffusion takes place to some extent at two-phase interface.The optimum parameters of FeCrAl（f）/HA composite are diameter of 22 μm,length of 1-2 mm and of volume faction of about 7% for FeCrAl fibers.

Rheological and mechanical properties of wood fiber-PP/PE blend composites

For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the interfacial adhesion between wood fiber and matrix. WPCs were prepared from wood fiber up to 60 wt.% and modified PP/PE was blended by extrusion. The rheological properties were studied by using dynamic measurement. According to the strain sweep test, the linear viscoelastic region of composites in the melt was determined. The result showed that the storage modulus was independent of the strain at low strain region （〈0.1%）. The frequency sweep resuits indicated that all composites exhibited shear thinning behavior, and both the storage modulus and complex viscosity of MAH modified composites were decreased comparing to those unmodified. Flexural properties and impact strength of the prepared WPCs were measured according to the relevant standard specifications. The flexural and impact strength of the manufactured composites significantly increased and reached a maximum when MAH dosage was 1.0 wt%, whereas the flexural modulus after an initial decreased, also increased with MAH dosage. The increase in mechanical properties indicated that the presence of anhydride groups enhanced the interracial adhesion between wood fiber and PP/PE blends.

Mechanical properties of polyvinyl alcohol-basalt hybrid fiber engineered cementitious composites with impact of elevated temperatures

In the present study,the mechanical properties of polyvinyl alcohol(PVA)-basalt hybrid fiber reinforced engineered cementitious composites(ECC)after exposure to elevated temperatures were experimentally investigated.Five temperatures of 20,50,100,200 and 400℃ were set to evaluate the residual compressive,tensile and flexural behaviors of hybrid and mono fiber ECC.It was shown that partial replacement of PVA fibers with basalt fibers endowed ECC with improved residual compressive toughness,compared to brittle failure of mono fiber ECC heated to 400℃.The tension tests indicated that the presence of basalt fibers benefited the tensile strength up to 200℃,and delayed the sharp reduction of strength to 400℃.Under flexural load,the peak deflections corresponding to flexural strengths of hybrid fiber ECC were found to be less vulnerable ranging from 20 to 100℃.Further,the scanning electron microscopy(SEM)results uncovered that the rupture of basalt fiber at moderate temperature and its pullout mechanism at high temperature was responsible for the mechanical evolution of hybrid fiber ECC.This work develops a better understanding of elevated temperature and basalt fiber impact on the residual mechanical properties and further provides guideline for tailoring ECC for improved fire resistance.

Effect of Hybridization on the Mechanical Properties of Pineapple Leaf Fiber/Kenaf Phenolic Hybrid Composites

In this study,pineapple leaf fiber(PALF),kenaf fiber(KF)and PALF/KF/phenolic(PF)composites were fabricated and their mechanical properties were investigated.The mechanical properties(tensile,flexural and impact)of the PALF/KF/PF hybrid composites were investigated and compared with PALF/KF composites.The 3P7K exhibited enhanced tensile strength(46.96 MPa)and modulus(6.84 GPa),flexural strength(84.21 MPa)and modulus(5.81 GPa),and impact strength(5.39 kJ/m2)when compared with the PALF/PF and KF/PF composites.Scanning electron microscopy(SEM)was used to observe the fracture surfaces of the tensile testing samples.The microstructure of the 7P3K hybrid composite showed good interfacial bonding and the addition of KF improved the interfacial strength.It has been concluded that the 3P7K ratio allowed obtaining materials with better mechanical properties(tensile,flexural and impact strengths)than PALF/PF and KF/PF composites.The results obtained in this study will be used for further comparative study of untreated hybrid composites with treated hybrid composites.

Mechanical properties and failure behavior of 3D printed thermoplastic composites using continuous basalt fiber under high-volume fraction

Continuous basalt fiber(CBF)is an outstanding inorganic fiber produced from nature,which has a wide range of applications in the field of armor protection of national defense military.However,the mechanical response and failure mechanism of 3D printed CBF reinforced components are still not well understood.Here,the 3D printing thermoplastic composites with high volume fraction CBF have been successfully prepared by fused deposition modelling(FDM)method.The effects of fiber printing direction and polymer matrix type on the tensile and flexural properties of the 3D printed composites have been explored,and the detailed failure morphology has been characterized using scanning electron microscopy and optical microscopy.It was found that under high fiber volume fraction,3D printed CBF reinforced polyamides(PA)composites have the best ability to maintain material integrity of the composites,followed by acrylonitrile butadiene styrene(ABS)and high impact polystyrene(HIPS).Besides,the results from rule of mixtures can accurately predict the longitudinal Young’s modulus of the 3D printed specimens,but there exists a large discrepancy for the prediction of the tensile strength.The microstructure analysis shows that the failure modes of 3D printed composites mainly include fiber debonding,fiber pull-out,stress whitening and matrix cracking.

Mechanical and Thermal Properties of Apocynum and Ramie Fiber Mat Reinforced Polylactic Acid Composites

With the increasing awareness of environmental protection and rational utilization of resources,natural fiber reinforced composites have shown broad development prospects.Apocynum fiber,known as the“king of wild fiber”,not only has moisture absorption,air permeability,and good mechanical properties but also has many health-related advantages such as antibacterial properties.In this study,four types of needle-punched Apocynum fiber and ramie fiber mat reinforced polylactic acid(PLA)composites were fabricated.Mechanical and thermal properties of the composites were tested and analyzed.The results showed that compared with those of the ramie fiber finish needle-punched mat reinforced composites,the tensile strength and the tensile modulus of Apocynum fiber finish needle-punched mat reinforced composites had increased by 15.3%and 60.1%,respectively.In comparison,the bending strength and the bending modulus were decreased by 21.8%and 7.6%,respectively.Moreover,compared with the Apocynum fiber finish needled-punched mat reinforced composites and the ramie fiber finish needle-punched mat reinforced composites,the Apocynum 50/ramie 50 finish needle-punched mat reinforced composites had the best tensile and bending properties.The after-fracture morphology was detected by a scanning electron microscope(SEM).The thermal properties of the composites were also characterized.It was found that the thermal properties of the four types of composites showed very similar behaviors.

Improved wettability and mechanical properties of metal coated carbon fiber-reinforced aluminum matrix composites by squeeze melt infiltration technique

In order to improve the wettability and bonding performance of the interface between carbon fiber and aluminum matrix,nickel-and copper-coated carbon fiber-reinforced aluminum matrix composites were fabricated by the squeeze melt infiltration technique.The interface wettability,microstructure and mechanical properties of the composites were compared and investigated.Compared with the uncoated fiber-reinforced aluminum matrix composite,the microstructure analysis indicated that the coatings significantly improved the wettability and effectively inhibited the interface reaction between carbon fiber and aluminum matrix during the process.Under the same processing condition,aluminum melt was easy to infiltrate into the copper-coated fiber bundles.Furthermore,the inhibited interface reaction was more conducive to maintain the original strength of fiber and improve the fiber−matrix interface bonding performance.The mechanical properties were evaluated by uniaxial tensile test.The yield strength,ultimate tensile strength and elastic modulus of the copper-coated carbon fiber-reinforced aluminum matrix composite were about 124 MPa,140 MPa and 82 GPa,respectively.In the case of nickel-coated carbon fiber-reinforced aluminum matrix composite,the yield strength,ultimate tensile strength and elastic modulus were about 60 MPa,70 MPa and 79 GPa,respectively.The excellent mechanical properties for copper-coated fiber-reinforced composites are attributed to better compactness of the matrix and better fiber−matrix interface bonding,which favor the load transfer ability from aluminam matrix to carbon fiber under the loading state,giving full play to the bearing role of carbon fiber.

Influences of Mo Fibers on Mechanical Properties of Resin Mineral Composites

The influences of new,scrap,and five modified Mo fibers on interface bonding strength of fiber-matrix and mechanical strength of RMC were studied.Typical specimens with different fibers and mass ratio of resin and hardener were prepared to verify the above assumptions.Theoretical analysis and experimental results prove that,compared with ordinary new Mo fibers,scrap Mo fibers can perform better in improving interface bonding strength and mechanical properties of RMC because many discharge pits randomly distribute on the surface of scrap fibers.For five modified Mo fibers,interface bonding strength and the reinforcing effect on RMC have been improved obviously.Wherein,comprehensive mechanical properties of RMC are optimal with the addition of M6 fibers which have undergone combined surface treatment including acidification,gas-phase oxidation and coupling treatment.And interface bonding strength between M6 fiber and matrix is the maximum.

Effects of Fiber Surface Pretreatment and Composite Posttreatment on Mechanical Properties of 2D⁃Cf/Phosphate Geopolymer Matrix Composites

Geopolymers are an important class of materials with potential applications because of their heat resistance,flame resistance,environmental friendliness,and possibilities of being transformed into ceramic matrix composites at low cost.However,the low mechanical properties as well as the intrinsic brittleness limit their technological implementations,and it is necessary to enhance the mechanical properties of geopolymers by adopting various kinds of reinforcements.In this work,therefore,two⁃dimensional continuous carbon fiber(Cf)reinforced phosphate⁃based geopolymer composites(Cf/geopolymer)were prepared through ultrasonic⁃assisted impregnation method.Effects of acetone treatment and high⁃temperature treatment on the properties of Cf/geopolymer composites were studied by X⁃ray photoelectron spectroscopy(XPS),X⁃ray diffraction(XRD),and scanning electron microscopy(SEM).Results of the study proved that acetone treatment plays a key role in ameliorating the interfacial interaction between Cf and phosphate matrix,which can thus enhance the mechanical properties of Cf/geopolymer composites.The Cf/geopolymer composites prepared by acetone⁃treated Cf had a flexural strength of 156.1 MPa and an elastic modulus of 39.7 GPa in Y direction.Moreover,an additional Sol⁃SiO2 re⁃impregnation treatment could further enhance the mechanical properties of the acetone⁃treated Cf/geopolymer composites by repairing the cracks and filling the pores.The results in this paper not only provide insights into the surface modification of Cf,but also report a facile and low⁃cost preparation route for Cf/geopolymer composites with potential applications in aerospace and defense technology.

Effect of Cold Plasma Treatment on the Mechanical Properties of RTM Composites

Cold plasma technology was used to treat the surface of carbon fibers braided by PET in this paper and SEM was used to analyze the fracture microstructure of composite interlaminar shear stress (ILSS). The result shows that the surface polarity of carbon fibers was modified by cold plasma treatment, which increases the impregnation of PET braided carbon fibers during the process of resin flowing, improves the interfacial properties of RTM composites, and therefore enhances the mechanical properties of the KTM composites.

Effect of electropolymer sizing of carbon fiber on mechanical properties of phenolic resin composites

Carbon fiber/phenolic resin composites were reinforced by the carbon fiber sized with the polymer films of phenol, m-phenylenediamine or acrylic acid, which was electropolymerized by cyclic voltammetry or chronopotentiometry. The contact angles of the sized carbon fibers with deionized water and diiodomethane were measured by the wicking method based on the modified Washburn equation, to show the effects of the different electropolymer film on the surface free energy of the carbon fiber after sizing by the electropolymerization. Compared with the unsized carbon fiber, which has 85.6°of contact angle of water, 52.2°of contact angle of diiodomethane, and 33.1 mJ/m2 of surface free energy with 29.3 mJ/m2 of dispersive components (γL) and 3.8 mJ/m2 of polar components (γsp), respectively. It is found that the electropolymer sized carbon fiber tends to reduce the surface energy due to the decrease of dispersiveγL with the increase of the polymer film on the surface of the carbon fiber that plays an important role in improving the mechanical properties of carbon/phenolic resin composites. Compared with the phenolic resin composites reinforced by the unsized carbon fiber, the impact, flexural and interlaminar shear strength of the phenolic resin composites were improved by 44 %, 68% and 87% when reinforced with the carbon fiber sized by the electropolymer of m-phenylenediamine, 66%, 100%, and 112% by the electropolymer of phenol, and 20%, 80 %, 100% by the electropolymer of acrylic acid. The results indicate the skills of electropolymerization may provide a feasible method for the sizing of carbon fiber in a composite system, so as to improve the interfacial performance between the reinforce materials and the matrix and to increase the mechanical properties of the composites.

Preparation of Polyimide Fiber/Thermoplastic Resin Composites with Improved Mechanical Properties

As a high-performance material for preparing composite materials, polyimide fibers suffer from many potential drawbacks, including poor bonding with other substrates, which results in composite materials with poor mechanical properties. Therefore, this study proposed a simple and rapid technique for obtaining loose, porous polyimide fiber papers by implementing a wet method using equal amounts of polyimide fiber and polyimide fiber paper as reinforcements, respectively. The polyimide resin-based composite materials were prepared by hand lay-up and hot pressing. The results showed that the paper-based reinforcement exhibited high porosity and the fibers were arranged with a uniform pore size distribution. The tensile properties, bending performance, and interlaminar shear performance of the paper-based composite improved by 130%, 108%, and 34.5%, respectively, compared to those of the fiberbased counterpart. The factors affecting the mechanical properties of the composites were analyzed based on the fiber length, fiber beating or lack thereof, and the basis weight of the paper. The increased uniformity of the polyimide fiber paper changed the ordering of the fibers and resolved drawbacks such as difficult dispersion, uneven pore size distribution, and poor mechanical properties related to single fibers in the resin-based composite material.

Preparation and Properties of Unmodified Ramie Fiber Reinforced Polypropylene Composites

Ramie fiber （RF） was used to reinforce the polypropylene （PP）. The composites were prepared with a melting hybrid technology. Tests had been performed on PP and composites with different RF contents （10 wt%, 20 wt%, and 30 wt%）. By using SEM, DSC, TGA, electronic universal testing machine, HDT-VICAT tester and coefficient of linear expansion tester, the effects of the RF loading were assessed on the basis of morphologies, mechanical and thermal properties as well as vicat softening temperature and CTE of the resulting composites. The results show that the thermal degradation temperature of the PP/RF composites becomes lower with higher fiber content. The crystallization rate of the PP matrix is accelerated by the unmodified RF. Because of the inferior interfacial bonding strength between RF and PP, the tensile strength of composites decreases by the presence of RF. And the RF used is relatively long compared with the diameter, the impact strength of the composites is improved by the unmodified RF. The vicat softening temperature of composites can be increased by about 5℃ in the presence of RF compared with PP. The CTE is reduced significantly in the presence of RF. Generally speaking, impact strength, crystallization rate, vicat softening temperature and CTE of PP/RF composites could be improved in the presence of RF. The tensile strength is decreased and thermal degradation temperature of composites becomes lower, but these should not affect most subsequent normal uses of the composites. As the unmodified RF is used directly, no hazardous waste is produced during the fabrication process, combined with the low price, so, a facile and economic preparation pathway is given by using unmodified natural fiber to reinforce polymer and composites with good performance obtained.

Mechanical Properties of Phenolic-Resin Composites Reinforced with CF/BF Interlayer Hybrid Fibers

Phenolic-resin composites reinforced with carbon fiber（CF） and basalt fiber（BF） interlayer hybrid fibers plain fabric were fabricated.The tensile strength,compressive strength and interlaminar shear strength of the prepared composites were studied.The results indicated that hybrid fibers reinforced composites possessed the advantages of both CF and BF.When resin content was 35% by volume fraction,the comprehensive mechanical performance of BF/CF reinforced phenolic resin composites reached the optimal values with the warp and weft direction tensile strength,compressive strength and interlayer shear strength being 252 MPa and 487 MPa,105 MPa and 129 MPa,21 MPa and 20 MPa,respectively.The scanning electron microscope（SEM） observations showed that the BF/CF hybrid fibers reinforced composites had better interfacial adhesion.

Comparative study on the interface and mechanical properties of T700/Al and M40/Al composites

T700/Al and M40/Al composites were fabricated by squeeze casting technology, and their interface and mechanical properties were investigated comparatively. The results showed that both of the composites were dense, and the fibers were distributed uniformly in aluminum matrix. Aluminum carbide （Al4C3） was observed on the interface of the two carbon fiber-reinforced aluminum （Cf/Al） composites. There was little Al4C3 with a length of 300-500 nm and a width of 30-60 nm in the M40/Al composite, whereas there was a great deal of Al4C3 with a length of 200-400 nm and a width of 100-200 nm in the T700/Al composite, due to a higher graphitization of M40Cf than T700Cf. The M40/Al composite showed a much higher tensile strength than the TT00/Al composite, and it was related to interracial bonding between carbon fibers and aluminum matrices.

Mechanical and Thermal Properties of Sugar Palm Fiber Reinforced Thermoplastic Polyurethane Composites:Effect of Silane Treatment and Fiber Loading

The aim of the present study was to develop sugar palm fiber(SPF)reinforced thermoplastic polyurethane(TPU)composites and to investigate the effects of fiber surface modification by 2%silane treatment and fiber loading(0,10,20,30,40 and 50 wt%)on the mechanical and thermal properties of the obtained composites.Surface treatment was employed to improve the fiber-matrix interface,which was expected to boost the mechanical strength of the composites,in terms of tensile,flexural and impact properties.Thermal properties were also investigated by thermal gravimetric analysis(TGA)and dynamic mechanical analysis(DMA)to assess the thermal stability of the developed composites.Furthermore,scanning electron microscopy(SEM)was used to study the tensile fracture samples of composites with a view towards evaluating the effects of fiber surface treatments on the fiber/matrix interfacial bonding.The findings of this study reveal that the silane treatment has determined good bonding and linkage of the cellulose fiber to the TPU matrix,hence contributing to enhanced mechanical and thermal properties of the composites.The composite formulation with 40 wt%sugar palm fiber loading showed optimum values such as 17.22 MPa for tensile,13.96 MPa for flexural,and 15.47 kJ/m^2 for impact strength.Moreover,the formulations with higher fiber content exhibited satisfactory values of storage modulus and thermal degradation,while their good interfacial adhesion was evidenced by SEM images.

Microstructure and Mechanical Properties of as Cast Aluminium Alloy 7075/Basalt Dispersed Metal Matrix Composites

This paper aims to study the effects of short basalt fiber reinforcement on the mechanical properties of cast aluminium alloy 7075 composites containing short basalt fiber of content ranging from 2.5 to 10 percent by weight in steps of 2.5 percent and fabricated using compo-casting technique. The objective is to investigate the process feasibility and resulting material properties such as young’s modulus, ductility, hardness & compression strength. The properties obtained are compared with those of as-cast that were manufactured under the same fabrication conditions. The results of this study revealed that, as the short basalt fiber content was increased, there were significant increases in the ultimate tensile strength, hardness, compressive strength and Young’s modulus, accompanied by a reduction in its ductility. Furthermore, the microstructure & facture studies were carried out using Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) in order to establish relationships between the quality of the fiber/aluminium interface bond and hence to link with mechanical properties of the composites.

The Effect of Curative Concentration on Thermal and Mechanical Properties of Flexible Epoxy Coated Jute Fabric Reinforced Polyamide 6 Composites

Many researchers have shown interest in the reinforcement of commodity thermoplastic with natural fibers. However, the drawback of natural fibers is their low thermal processing temperatures, that border around 200℃. In this investigation, we tried to improve the thermal stability of natural fibers with the use of flexible epoxy surface coating that could facilitate processing with engineering thermoplastics. Jute fabric and Polyamide 6 (PA6) composites were prepared by compression molding. The thermal decomposition characteristics of the jute fabric were evaluated by using thermo gravimetric analysis (TGA). Mechanical analysis was conducted to evaluate tensile test and three point bending test of composite. It was found that thermal degradation resistance of jute fabric was improved by coating with flexible epoxy resin. Moreover, the flexural modulus improved with increasing curative concentration. The interfacial interaction between the epoxy and PA6 was clearly indicated by the photo micrographs of the polished cross sections of the coated and uncoated jute fabric/PA6 composites.

Mechanical properties of C_f/Si-O-C composites prepared by hot-pressing assisted pyrolysis of polysiloxane

Silicon oxycarbide composites reinforced by three-dimensional braided carbon fiber （3D-B Cf/Si-O-C） were fabricated via precursor infiltration and pyrolysis of polysiloxane, and the effects of processing variables on mechanical properties and microstructures of 3D-B Cf/Si-O-C composites were investigated. It is found that the mechanical properties and densities of 3D-B Cf/Si-O-C composites can be increased if the first pyrolysis cycle is assisted by hot-pressing. Pyrolysis temperature has great effects on mechanical properties and microstructures of 3D-B Cf/Si-O-C composites. The composite, which is hot-pressed at 1 600 ℃ for 5 min with pressure of 10 MPa in the first pyrolysis cycle, exhibits high mechanical properties: bending strength 502 MPa and fracture toughness 23.7 MPa·m1/2. The high mechanical properties are mainly attributed to desirable interfacial structure and high density.