The effect of complex melt-refining treatment （melt flux incorporating with rotating gas bubble stirring） on microstructure and mechanical behavior of the sand-cast Mg-10Gd-3Y-0.5Zr alloy was investigated. In additi...The effect of complex melt-refining treatment （melt flux incorporating with rotating gas bubble stirring） on microstructure and mechanical behavior of the sand-cast Mg-10Gd-3Y-0.5Zr alloy was investigated. In addition, the melt purifying mechanism of the complex melt-refining treatment for the sand-cast alloy was discussed systematically. The results show that the new melt-refining method can significantly improve melt quality and mechanical behavior of the tested alloy, i.e., compared to the reference unpttdfied alloy, the volume fraction of inclusions decreased from 0.47% to 0.28%, the ultimate tensile strength and elongation for T6-treated alloy increased from 245 MPa and 0.7% to 312 MPa and 4.5%, respectively. Especially, combining 1% flux with rotating gas bubble stirring can get even better purifying effectiveness than conventional sole 2% flux purification; the use of melt flux decreased by 50% and significantly reduced environmental pollution.展开更多
基金Project(USCAST2012-15) supported by the SAST-SJTU Joint Research Centre of Advanced Aerospace TechnologyProject(B type,14QB1403200) supported by the Shanghai Rising-Star Program,China+1 种基金Projects(20120073120011,20130073110052) supported by the Research Fund for the Doctoral Program of Higher Education of ChinaProject(IPP9084) supported by IPP program in SJTU,China
文摘The effect of complex melt-refining treatment （melt flux incorporating with rotating gas bubble stirring） on microstructure and mechanical behavior of the sand-cast Mg-10Gd-3Y-0.5Zr alloy was investigated. In addition, the melt purifying mechanism of the complex melt-refining treatment for the sand-cast alloy was discussed systematically. The results show that the new melt-refining method can significantly improve melt quality and mechanical behavior of the tested alloy, i.e., compared to the reference unpttdfied alloy, the volume fraction of inclusions decreased from 0.47% to 0.28%, the ultimate tensile strength and elongation for T6-treated alloy increased from 245 MPa and 0.7% to 312 MPa and 4.5%, respectively. Especially, combining 1% flux with rotating gas bubble stirring can get even better purifying effectiveness than conventional sole 2% flux purification; the use of melt flux decreased by 50% and significantly reduced environmental pollution.