To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor （SMBR） for wastewater treatment, polypropylene hollow fiber microporous membrane （PPHFMM） was surface-modified by the...To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor （SMBR） for wastewater treatment, polypropylene hollow fiber microporous membrane （PPHFMM） was surface-modified by the plasma-induced immobilization of poly （N-vinyl-2-pyrrolidone） （PVP） and the plasma treatment with different gases respectively. Attenuated total reflection-Fourier transform infrared spectroscopy （FT-IR/ATR）, X-ray photoelectron spectroscopy （XPS） and field emission scanning electron microscope （FE-SEM） were used to characterize the structural and morphological changes on the membrane surface. Water contact angle was measured by the sessile drop method. It was found that the water contact angle was 128.8, 72.3, 62.7, 74.4, 79.1, 86.3, and 71.3° for the nascent, PVP-immobilized, air, 02, Ar, CO2 and H2O plasma treated PPHFMM, respectively. The SMBR was operated at fixed transmembrane pressure to determine the limiting flux for the PPHFMM before and after surface modification. Results showed that the limiting flux appeared to be 103, 159, 117, 133, 136, 121 and 152 L/（m^2· h） for the nascent, PVP-immobilized, air, O2, At, CO2 and H2O plasma treated PPHFMM, respectively. After continuous operation for about 50 h in the SMBR, the antifouling characteristics were improved to some extent.展开更多
基金The Hi-Tech Research and Development Program (863) of China (No. 2002AA601230)
文摘To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor （SMBR） for wastewater treatment, polypropylene hollow fiber microporous membrane （PPHFMM） was surface-modified by the plasma-induced immobilization of poly （N-vinyl-2-pyrrolidone） （PVP） and the plasma treatment with different gases respectively. Attenuated total reflection-Fourier transform infrared spectroscopy （FT-IR/ATR）, X-ray photoelectron spectroscopy （XPS） and field emission scanning electron microscope （FE-SEM） were used to characterize the structural and morphological changes on the membrane surface. Water contact angle was measured by the sessile drop method. It was found that the water contact angle was 128.8, 72.3, 62.7, 74.4, 79.1, 86.3, and 71.3° for the nascent, PVP-immobilized, air, 02, Ar, CO2 and H2O plasma treated PPHFMM, respectively. The SMBR was operated at fixed transmembrane pressure to determine the limiting flux for the PPHFMM before and after surface modification. Results showed that the limiting flux appeared to be 103, 159, 117, 133, 136, 121 and 152 L/（m^2· h） for the nascent, PVP-immobilized, air, O2, At, CO2 and H2O plasma treated PPHFMM, respectively. After continuous operation for about 50 h in the SMBR, the antifouling characteristics were improved to some extent.