Three-dimensionally ordered mesoporous Fe2O3（meso-Fe2O3） and its supported Au, Pd,and Au-Pd alloy（xA uP dy/meso-Fe2O3; x = 0.08–0.72 wt.%; Pd/Au molar ratio（y） = 1.48–1.85）photocatalysts have been prepared via...Three-dimensionally ordered mesoporous Fe2O3（meso-Fe2O3） and its supported Au, Pd,and Au-Pd alloy（xA uP dy/meso-Fe2O3; x = 0.08–0.72 wt.%; Pd/Au molar ratio（y） = 1.48–1.85）photocatalysts have been prepared via the KIT-6-templating and polyvinyl alcohol-protected reduction routes, respectively. Physical properties of the samples were characterized, and their photocatalytic activities were evaluated for the photocatalytic oxidation of acetone in the presence of a small amount of H2O2 under visible-light illumination. It was found that the meso-Fe2O3 was rhombohedral in crystal structure. The as-obtained samples displayed a high surface area of 111.0–140.8 m^2/g and a bandgap energy of 1.98–2.12 eV. The Au, Pd and/or Au–Pd alloy nanoparticles（NPs） with a size of 3–4 nm were uniformly dispersed on the surface of the meso-Fe2O3 support. The 0.72 wt.% AuP d1.48/meso-Fe2O3 sample performed the best in the presence of 0.06 mol/L H2O2 aqueous solution, showing a 100% acetone conversion within4 hr of visible-light illumination. It was concluded that the good performance of 0.72 wt.%AuPd（1.48）/meso-Fe2O3 for photocatalytic acetone oxidation was associated with its ordered mesoporous structure, high adsorbed oxygen species concentration, plasmonic resonance effect between AuPd（1.48） NPs and meso-Fe2O3, and effective separation of the photogenerated charge carriers. In addition, the introduction of H2O2 and the involvement of the photo-Fenton process also played important roles in enhancing the photocatalytic activity of 0.72 wt.%AuPd（1.48）/meso-Fe2O3.展开更多
基金supported by the National Natural Science Foundation of China (No. 21377008)the National High Technology Research and Development Program of China ("863"Program)(No. 2015AA034603)the Foundation of the Creative Research Team Construction Promotion Project of Beijing Municipal Institutions
文摘Three-dimensionally ordered mesoporous Fe2O3（meso-Fe2O3） and its supported Au, Pd,and Au-Pd alloy（xA uP dy/meso-Fe2O3; x = 0.08–0.72 wt.%; Pd/Au molar ratio（y） = 1.48–1.85）photocatalysts have been prepared via the KIT-6-templating and polyvinyl alcohol-protected reduction routes, respectively. Physical properties of the samples were characterized, and their photocatalytic activities were evaluated for the photocatalytic oxidation of acetone in the presence of a small amount of H2O2 under visible-light illumination. It was found that the meso-Fe2O3 was rhombohedral in crystal structure. The as-obtained samples displayed a high surface area of 111.0–140.8 m^2/g and a bandgap energy of 1.98–2.12 eV. The Au, Pd and/or Au–Pd alloy nanoparticles（NPs） with a size of 3–4 nm were uniformly dispersed on the surface of the meso-Fe2O3 support. The 0.72 wt.% AuP d1.48/meso-Fe2O3 sample performed the best in the presence of 0.06 mol/L H2O2 aqueous solution, showing a 100% acetone conversion within4 hr of visible-light illumination. It was concluded that the good performance of 0.72 wt.%AuPd（1.48）/meso-Fe2O3 for photocatalytic acetone oxidation was associated with its ordered mesoporous structure, high adsorbed oxygen species concentration, plasmonic resonance effect between AuPd（1.48） NPs and meso-Fe2O3, and effective separation of the photogenerated charge carriers. In addition, the introduction of H2O2 and the involvement of the photo-Fenton process also played important roles in enhancing the photocatalytic activity of 0.72 wt.%AuPd（1.48）/meso-Fe2O3.
