In order to improve the pyrotechnical reagent with potassium perchlorate,composite catalyst of active carbon supporting transition metal oxides （TMO）,Fe2O3 and CuO,were prepared and added into pyrotechnical reagent ...In order to improve the pyrotechnical reagent with potassium perchlorate,composite catalyst of active carbon supporting transition metal oxides （TMO）,Fe2O3 and CuO,were prepared and added into pyrotechnical reagent with potassium perchlorate.Accelerating rate calorimeter （ARC） was used to study the catalysis of pyrotechnical reagent which is consisted of potassium perchlorate and composite catalyst.Composite catalyst of both Fe2O3 and CuO supported by active carbon can catalyze pyrotechnical reagent with potassium perchlorate.Furthermore,it can lower the apparent activation energy and accelerate the reaction with a smaller quantity than that with Fe2O3 and CuO.The maximal reaction rate of pyrotechnical reagent with potassium perchlorate mixed with Fe2O3/active carbon and CuO/active carbon is 8.31 min-1 and 9.13 min-1,which is 1.74 times and 1.91 times of pyrotechnical reagent mixed with no catalyst;time to maximal rate was 18.99 min and 1.96 min respectively,which is lower than pyrotechnical reagent mixed with no catalyst by 86.46% and 98.67% ;the apparent activation energy is 368.10 kJ·mol-1 and 325.29 kJ·mol-1,which is lower than pyrotechnical reagent mixed with no catalyst by 31.89% and 39.81% respectively.展开更多
The residual metal impurities in cisplatin, carboplatin and oxaliplatin were determined by ICP-AES. The samples were ignited and dissolved with HCl:HNO 3 (3:1). The method is simple and accurate. By the determination ...The residual metal impurities in cisplatin, carboplatin and oxaliplatin were determined by ICP-AES. The samples were ignited and dissolved with HCl:HNO 3 (3:1). The method is simple and accurate. By the determination of the metal residues in the samples, the calculated actual daily exposure and concentration of the metal Pd, Ir, Rh, Ru, Mo, Ni, Cr, V, Cu, Mn, Fe and Zn that were less than the permitted daily exposures (PDE) and the limited concentration permitted in the EMEA guideline on the specification limits for residues of metal catalysts or metal reagents [1] . The metal residues can de adequately removed from the active pharmaceutical ingredients and the corresponding drugs. The trace metal residues will not affect human health and lead to the safety hazard by the intravenous injection.展开更多
NF3 decomposition over transition metal oxides coated MgO reagents in the absence of water is investigated. The results show that NF3 can be decomposed completely over pure MgO but the time of NF3 steady full conversi...NF3 decomposition over transition metal oxides coated MgO reagents in the absence of water is investigated. The results show that NF3 can be decomposed completely over pure MgO but the time of NF3 steady full conversion kept as short as 80 min, while the reactivities of coated MgO reagents were remarkably enhanced by transition metal oxides, for example the time of NF3 complete conversion over 12%Fe/MgO extended to 380 min. It is suggested that not only an increase in surface area but also a significant enhancement in the fluorination of MgO substrate caused by the surface transition metal oxides result in an improved reactivity of coated MgO reagents for NF3 decomposition.展开更多
基金Sponsored by the National Natural Science Foundation of China(50874017)
文摘In order to improve the pyrotechnical reagent with potassium perchlorate,composite catalyst of active carbon supporting transition metal oxides （TMO）,Fe2O3 and CuO,were prepared and added into pyrotechnical reagent with potassium perchlorate.Accelerating rate calorimeter （ARC） was used to study the catalysis of pyrotechnical reagent which is consisted of potassium perchlorate and composite catalyst.Composite catalyst of both Fe2O3 and CuO supported by active carbon can catalyze pyrotechnical reagent with potassium perchlorate.Furthermore,it can lower the apparent activation energy and accelerate the reaction with a smaller quantity than that with Fe2O3 and CuO.The maximal reaction rate of pyrotechnical reagent with potassium perchlorate mixed with Fe2O3/active carbon and CuO/active carbon is 8.31 min-1 and 9.13 min-1,which is 1.74 times and 1.91 times of pyrotechnical reagent mixed with no catalyst;time to maximal rate was 18.99 min and 1.96 min respectively,which is lower than pyrotechnical reagent mixed with no catalyst by 86.46% and 98.67% ;the apparent activation energy is 368.10 kJ·mol-1 and 325.29 kJ·mol-1,which is lower than pyrotechnical reagent mixed with no catalyst by 31.89% and 39.81% respectively.
基金The national SME technology innovation fund(11C26215305898)Kunming SME technology innovation fund(CJ2011040)
文摘The residual metal impurities in cisplatin, carboplatin and oxaliplatin were determined by ICP-AES. The samples were ignited and dissolved with HCl:HNO 3 (3:1). The method is simple and accurate. By the determination of the metal residues in the samples, the calculated actual daily exposure and concentration of the metal Pd, Ir, Rh, Ru, Mo, Ni, Cr, V, Cu, Mn, Fe and Zn that were less than the permitted daily exposures (PDE) and the limited concentration permitted in the EMEA guideline on the specification limits for residues of metal catalysts or metal reagents [1] . The metal residues can de adequately removed from the active pharmaceutical ingredients and the corresponding drugs. The trace metal residues will not affect human health and lead to the safety hazard by the intravenous injection.
基金financially supported by the National Natural Science Foundation of China(No.20976149)
文摘NF3 decomposition over transition metal oxides coated MgO reagents in the absence of water is investigated. The results show that NF3 can be decomposed completely over pure MgO but the time of NF3 steady full conversion kept as short as 80 min, while the reactivities of coated MgO reagents were remarkably enhanced by transition metal oxides, for example the time of NF3 complete conversion over 12%Fe/MgO extended to 380 min. It is suggested that not only an increase in surface area but also a significant enhancement in the fluorination of MgO substrate caused by the surface transition metal oxides result in an improved reactivity of coated MgO reagents for NF3 decomposition.