Chemical, mechanical, and thermal expansion properties of a carbon nanotube-reinforced aluminum nanocomposite

In the present study,the chemical and mechanical properties and the thermal expansion of a carbon nanotube（CNT）-based crystalline nano-aluminum（nano Al） composite were reported.The properties of nanocomposites were tailored by incorporating CNTs into the nano Al matrix using a physical mixing method.The elastic moduli and the coefficient of thermal expansion（CTE） of the nanocomposites were also estimated to understand the effects of CNT reinforcement in the Al matrix.Microstructural characterization of the nanocomposite reveals that the CNTs are dispersed and embedded in the Al matrix.The experimental results indicate that the incorporation of CNTs into the nano Al matrix results in the increase in hardness and elastic modulus along with a concomitant decrease in the coefficient of thermal expansion The hardness and elastic modulus of the nanocomposite increase by 21%and 20%,respectively,upon CNT addition.The CTE of CNT/A1 nanocomposite decreases to 70%compared with that of nano Al.

Mechanical, electrical, and thermal expansion properties of carbon nanotube-based silver and silver–palladium alloy composites

The mechanical, electrical, and thermal expansion properties of carbon nanotube（CNT）-based silver and silver–palladium（10：1, w/w） alloy nanocomposites are reported. To tailor the properties of silver, CNTs were incorporated into a silver matrix by a modified molecular level-mixing process. CNTs interact weakly with silver because of their non-reactive nature and lack of mutual solubility. Therefore, palladium was utilized as an alloying element to improve interfacial adhesion. Comparative microstructural characterizations and property evaluations of the nanocomposites were performed. The structural characterizations revealed that decorated type-CNTs were dispersed, embedded, and anchored into the silver matrix. The experimental results indicated that the modification of the silver and silver–palladium nanocomposite with CNT resulted in increases in the hardness and Young＇s modulus along with concomitant decreases in the electrical conductivity and the coefficient of thermal expansion（CTE）. The hardness and Young＇s modulus of the nanocomposites were increased by 30%？40% whereas the CTE was decreased to 50%-60% of the CTE of silver. The significantly improved CTE and the mechanical properties of the CNT-reinforced silver and silver–palladium nanocomposites are correlated with the intriguing properties of CNTs and with good interfacial adhesion between the CNTs and silver as a result of the fabrication process and the contact action of palladium as an alloying element.

Effects of B addition on glass forming ability and thermal behavior of FePC-based bulk metallic glasses

The FePC-based bulk metallic glasses（BMGs）have been demonstrated to possess high plasticity and good soft magnetic properties.However,the relatively poor glass forming ability（GFA）and thermal stabilities limited their application in industries.The effects of microalloying with B in FePC-based BMGs on the GFA and thermal behaviors were systematically investigated.It was found that a small amount of B addition can dramatically enhance the GFA of FePC-based BMGs,which in turn leads to the critical maximum diameter up to 2 mm for full glass formation even using low cost raw materials.The underlying mechanism of the enhancement of GFA from the competing crystalline phase with amorphous phase,the average thermal expansion coefficient and dynamic viscosity were discussed in detail.

Thermal properties of diamond/Al composites by pressure infiltration:comparison between methods of coating Ti onto diamond surfaces and adding Si into Al matrix

This study was pertained to the effects of Ti coating on diamond surfaces and Si addition into Al matrix on the thermal conductivity（TC） and the coefficient of thermal expansion（CTE） of diamond/Al composites by pressure infiltration.The fracture surfaces,interface microstructures by metal electro-etching and interfacial thermal conductance of the composites prepared by two methods were compared.The results reveal that Ti coating on diamond surfaces and only12.2 wt% Si addition into Al matrix could both improve the interfacial bonding and increase the TCs of the composites.But the Ti coating layer introduces more interfacial thermal barrier at the diamond/Al interface compared to adding 12.2 wt% Si into Al matrix.The diamond/Al composite with 12.2 wt% Si addition exhibits maximum TC of 534 W·m^-1·K^-1and a very low CTE of 8.9×10^-6K^-1,while the coating Ti-diamond/Al composite has a TC of 514 W·m^-1·K^-1 and a CTE of 11.0×10^-6K^-1.