Self consistent Field discrete variational Xα( SCF Xα DV) method was used to study the wettabilitybetween TiB2 Ceramic and Metals. The Metals were Ni, Mo, Ni+ Mo, and etc. microstructureof TiB2/ Fe, TiB2/ Niand TiB2...Self consistent Field discrete variational Xα( SCF Xα DV) method was used to study the wettabilitybetween TiB2 Ceramic and Metals. The Metals were Ni, Mo, Ni+ Mo, and etc. microstructureof TiB2/ Fe, TiB2/ Niand TiB2/ NiMoinvestigatedby TEM werechosen toidentify the calculation model. The result shows the wetting in the above systems were chemicalreactive wetting ,and can becalculated by SCF Xα DV . Theeffectof active ele ment( Mo) to TiB2/ Ni wettability wasstudied too.展开更多
Al2O3-metal composite coatings with different reactants and diluents were fabricated on mild steel plate with nonpressure combustion synthesis process. The coat-ings were characterized by means of X-ray diffraction, s...Al2O3-metal composite coatings with different reactants and diluents were fabricated on mild steel plate with nonpressure combustion synthesis process. The coat-ings were characterized by means of X-ray diffraction, scanning electron microscopy, and energy-dispersive spec-trometry, respectively. Thermal shock tests were carried out to determine the bond strength of the coating with the steel substrate. The results indicate that the coating is composed of α-A1203, α-（Fe-Cr） and Al2SiO5 as the main phases. It is found that the coating with the diluents of Al2O3-SiO2 and transition layer of Al2O3-Cr presents the hi.ghest hardness of 2270 HV0.2 and the lowest porosity of 3.93 %. Owing to a metallurgical bond of the coating-to-substrate, the coating exhibits a good thermal shock resistance.展开更多
文摘Self consistent Field discrete variational Xα( SCF Xα DV) method was used to study the wettabilitybetween TiB2 Ceramic and Metals. The Metals were Ni, Mo, Ni+ Mo, and etc. microstructureof TiB2/ Fe, TiB2/ Niand TiB2/ NiMoinvestigatedby TEM werechosen toidentify the calculation model. The result shows the wetting in the above systems were chemicalreactive wetting ,and can becalculated by SCF Xα DV . Theeffectof active ele ment( Mo) to TiB2/ Ni wettability wasstudied too.
基金financially supported by the Ministry of Education of China(No.625010312)
文摘Al2O3-metal composite coatings with different reactants and diluents were fabricated on mild steel plate with nonpressure combustion synthesis process. The coat-ings were characterized by means of X-ray diffraction, scanning electron microscopy, and energy-dispersive spec-trometry, respectively. Thermal shock tests were carried out to determine the bond strength of the coating with the steel substrate. The results indicate that the coating is composed of α-A1203, α-（Fe-Cr） and Al2SiO5 as the main phases. It is found that the coating with the diluents of Al2O3-SiO2 and transition layer of Al2O3-Cr presents the hi.ghest hardness of 2270 HV0.2 and the lowest porosity of 3.93 %. Owing to a metallurgical bond of the coating-to-substrate, the coating exhibits a good thermal shock resistance.