Interfacial heat transfer behavior at metal/die in finger-plated casting during high pressure die casting process

Heat transfer at the metal-die interface has a great influence on the solidification process and casting structure. As thin-wall components are extensively produced by high pressure die casting process(HPDC), the B390 alloy finger-plate casting was cast against an H13 steel die on a cold-chamber HPDC machine. The interfacial heat transfer behavior at different positions of the die was carefully studied using an inverse approach based on the temperature measurements inside the die. Furthermore, the filling process and the solidification rate in different finger-plates were also given to explain the distribution of interfacial heat flux(q) and interfacial heat transfer coefficient(h). Measurement results at the side of sprue indicates that qmax and hmax could reach 9.2 MW·m^(-2) and 64.3 kW ·m^(-2)·K^(-1), respectively. The simulation of melt flow in the die reveals that the thinnest(T_1) finger plate could accelerate the melt flow from 50 m·s^(-1) to 110 m·s^(-1). Due to this high velocity, the interfacial heat flux at the end of T_1 could firstly reach a highest value 7.92 MW·m^(-2) among the ends of T_n(n=2,3,4,5). In addition, the q_(max) and h_(max) values of T_2, T_4 and T_5 finger-plates increase with the increasing thickness of the finger plate. Finally, at the rapid decreasing stage of interfacial heat transfer coefficient(h), the decreasing rate of h has an exponential relationship with the increasing rate of solid fraction(f).

A study of metal/die interfacial heat transfer behavior of vacuum die cast pure copper

High pressure die casting copper is used to produce rotors for induction motors to improve efficiency.Experiments were carried out for a special"step-shape"casting with different step thicknesses.Based on the measured temperature inside the die,the interfacial heat transfer coefficient(IHTC)at the metal/die interface during vacuum die casting was evaluated by solving the inverse problem.The IHTC peak value was 4.5×10^3-11×10^3 W·m^-2·K^-1 under the basic operation condition.The influences of casting pressure,fast shot speed,pouring temperature and initial die surface temperature on the IHTC peak values were investigated.Results show that a greater casting pressure and faster shot speed could only increase the IHTC peak values at the location close to the ingate.An increase of pouring temperature and/or initial die surface temperature significantly increases the IHTC peak values.

Design of relief-cavity in closed-precision forging of gears

To reduce the difficulty of material filling into the top region of tooth in hot precision forging of gears using the alternative die designs, relief-cavity designs in different sizes were performed on the top of die tooth. The influences of the conventional process and relief-cavity designs on corner filling, workpiece stress, die stress, forming load and material utilization were examined. Finite element simulation for tooth forming, die stress and forming load using the four designs was performed. The material utilization was further considered, and the optimal design was determined. The tooth form and forming load in forging trials ensured the validity of FE simulation. Tooth accuracy was inspected by video measuring machine(VMM), which shows the hot forged accuracy achieves the level of rough machining of gear teeth. The effects of friction on mode of metal flow and strain distribution were also discussed.