The main results obtained from the experimental and engineering investigation on the heat evolution and cracking risk of a furnace concrete block were presented. The heat evolution of experimental mortars containing m...The main results obtained from the experimental and engineering investigation on the heat evolution and cracking risk of a furnace concrete block were presented. The heat evolution of experimental mortars containing micro-slag under different environmental temperatures was instrumented in order to investigate the self-catalyzed effect, which was discovered in engineering. More-over,the thermal stress of the furnace concrete due to heat temperature rise was calculated to evaluate the cracking risk of mass concrete containing micro-slag due to self-catalyzed effect. The experimental results illustrate that with the development of hydration and initial temperature of mixture, the hydra-tion can be also accelerated and temperature of concrete will be continued to rise, which was the self-catalyzed effect. And the thermal stress due to self-catalyzed effect could not result in the cracking of furnace concrete.展开更多
Hydration characteristics of Portland cement paste with phosphorus slag powder incorporated and hydration kinetics was investigated with SEM, X-ray diffraction, DTA-TG and calorimeter Ⅱ80. Results showed that phospho...Hydration characteristics of Portland cement paste with phosphorus slag powder incorporated and hydration kinetics was investigated with SEM, X-ray diffraction, DTA-TG and calorimeter Ⅱ80. Results showed that phosphorus slag powder could reduce total amount of hydration products yet had little influence on the type of hydration products. The total amount of heat of hydration was decreased by 49.11% and the final setting was postponed by 2.28 h when phosphorus slag powder substituted 35% Portland cement by mass. The accelerating stage of this composite paste was controlled by catalysis, decreasing stage controlled by both catalysis and diffusion while stabilizing stage by diffusion alone. Hydration resistance and activation energy were reduced and hydration speed was accelerated.展开更多
基金Funded by the Key Technologies R&D Program from Department of Science and Technology Hubei Province(200410G0121) "973" Pro-gram(001CB610704-3) from Ministry of Science and Technology of China
文摘The main results obtained from the experimental and engineering investigation on the heat evolution and cracking risk of a furnace concrete block were presented. The heat evolution of experimental mortars containing micro-slag under different environmental temperatures was instrumented in order to investigate the self-catalyzed effect, which was discovered in engineering. More-over,the thermal stress of the furnace concrete due to heat temperature rise was calculated to evaluate the cracking risk of mass concrete containing micro-slag due to self-catalyzed effect. The experimental results illustrate that with the development of hydration and initial temperature of mixture, the hydra-tion can be also accelerated and temperature of concrete will be continued to rise, which was the self-catalyzed effect. And the thermal stress due to self-catalyzed effect could not result in the cracking of furnace concrete.
基金Funded by the National Natural Science Foundation of China (No. 50539010)China Central Special Non-profit Research Funds for Institutes (Nos.200901066 and YWF090)
文摘Hydration characteristics of Portland cement paste with phosphorus slag powder incorporated and hydration kinetics was investigated with SEM, X-ray diffraction, DTA-TG and calorimeter Ⅱ80. Results showed that phosphorus slag powder could reduce total amount of hydration products yet had little influence on the type of hydration products. The total amount of heat of hydration was decreased by 49.11% and the final setting was postponed by 2.28 h when phosphorus slag powder substituted 35% Portland cement by mass. The accelerating stage of this composite paste was controlled by catalysis, decreasing stage controlled by both catalysis and diffusion while stabilizing stage by diffusion alone. Hydration resistance and activation energy were reduced and hydration speed was accelerated.