Sol-gel technology was employed to synthesize nanosized precursors of La-Mg hydrogen storage alloy at different pH values (0.5, 1.5, 8.0 and 9.0) of reaction solution. The effect of pH value on microstructure of the n...Sol-gel technology was employed to synthesize nanosized precursors of La-Mg hydrogen storage alloy at different pH values (0.5, 1.5, 8.0 and 9.0) of reaction solution. The effect of pH value on microstructure of the nano precursors of La-Mg hydrogen storage alloy was studied by infrared radiation (IR), thermo-gravimetric and differential thermal analysis (TG/DTA), X-ray diffraction analyzer (XRD) and transmission electron microscopy (TEM). IR results indicate that the chelating agent, citric acid, is not fully ionized, and carboxyl groups are not entirely used to complex metal ions in acidic solutions. The efficiency of complexing metal ions is enhanced in basic solutions. TG/DTA results show that the combustion may take place with low rate of the flame propagation that causes the longer combustion time when pH<1.5. On the contrary, the dry gel synthesized in basic solution combusts at low ignition temperature and combustion reaction is violent; it is easy to form fine particles. XRD and TEM results reveal that the precursor powders are mainly two-phase mixture of La 2 O 3 and MgO. The morphology of the particles is almost flake with the size of ~30 nm when pH is 8.0.展开更多
Metal–organic gel(MOG)derived composites are promising multi-functional materials due to their alterable composition,identifiable chemical homogeneity,tunable shape,and porous structure.Herein,stable metal–organic h...Metal–organic gel(MOG)derived composites are promising multi-functional materials due to their alterable composition,identifiable chemical homogeneity,tunable shape,and porous structure.Herein,stable metal–organic hydrogels are prepared by regulating the complexation effect,solution polarity and curing speed.Meanwhile,collagen peptide is used to facilitate the fabrication of a porous aerogel with excellent physical properties as well as the homogeneous dispersion of magnetic particles during calcination.Subsequently,two kinds of heterometallic magnetic coupling systems are obtained through the application of Kirkendall effect.FeCo/nitrogen-doped carbon(NC)aerogel demonstrates an ultra-strong microwave absorption of−85 dB at an ultra-low loading of 5%.After reducing the time taken by atom shifting,a FeCo/Fe3O4/NC aerogel containing virus-shaped particles is obtained,which achieves an ultra-broad absorption of 7.44 GHz at an ultra-thin thickness of 1.59 mm due to the coupling effect offered by dual-soft-magnetic particles.Furthermore,both aerogels show excellent thermal insulation property,and their outstanding radar stealth performances in J-20 aircraft are confirmed by computer simulation technology.The formation mechanism of MOG is also discussed along with the thermal insulation and electromagnetic wave absorption mechanism of the aerogels,which will enable the development and application of novel and lightweight stealth coatings.展开更多
Capillary column preparation using perpentylated (2,3,6-tri-O-pentyl)-β-cyclodextrin asstationary phase by sol-gel technology with simplicity and rapidity is described. Multiplepreparation steps in conventional colum...Capillary column preparation using perpentylated (2,3,6-tri-O-pentyl)-β-cyclodextrin asstationary phase by sol-gel technology with simplicity and rapidity is described. Multiplepreparation steps in conventional column technology were avoided. The prepared columns exhibitsatisfactory chromatographic performances and pronounced selectivity for a wide range of testsolutes, and have been successfully used for the separation of nitrotoluene, dimethoxybenzene,alcohols, alkanes, dimethylphenol and cresol isomers.展开更多
The sol-gel technology is applied for the preparation of solid-phase microextraction (SPME) fiber. The fiber demonstrates high thermal stability, efficient extraction rate and the selectivity for non-polar or low-pol...The sol-gel technology is applied for the preparation of solid-phase microextraction (SPME) fiber. The fiber demonstrates high thermal stability, efficient extraction rate and the selectivity for non-polar or low-polar analytes. Efficient SPME-GC-FID analyses of benzene- toluene-ethylbenzene-xylenes (BTEXs) and low-polar halocarbon were achieved by the sol-gel coated DSDA-DDBT-TiO2 fiber. Some parameters of the SPME fiber for the determination of halocarbon in aqueous sample were investigated.展开更多
Heptakis(2, 3, 6-tri-O-octyl)-β-cyclodextrin was coated onto the fused silica capillary by sol-gel technology. Column efficiency and column selectivity were studied. The results indicated that high ability of separat...Heptakis(2, 3, 6-tri-O-octyl)-β-cyclodextrin was coated onto the fused silica capillary by sol-gel technology. Column efficiency and column selectivity were studied. The results indicated that high ability of separation was acquired . Positional isomers of aromatic compounds were well separated.展开更多
The importance of foundry coating in improving the surface quality of castings cannot be over emphasized. The application of mould and core washes creates a high thermal integrity barrier between the metal and the mou...The importance of foundry coating in improving the surface quality of castings cannot be over emphasized. The application of mould and core washes creates a high thermal integrity barrier between the metal and the mould resulting in the reduction of the thermal shock experienced by the sand system. These thermal shock leads to series of surface defects such as veining/finning, metal penetration, burn-on/in, scab, rat tail, erosion etc. The use of coatings reduces the tendency of occurrence of these defects. However, the understanding of the coating, its components, characteristics and mechanism of action is important. In this review, a detailed description of these topics and examples are provided where necessary. A potential area of research in foundry coating development, using sol-gel process is suggested. The application of sol-gel technology in the development of foundry coatings is a novel approach.展开更多
基金supported by the Open Foundation of Key Laboratory of the Ministry of Educationof Nonferrous Metal Alloys and Processes(No.EKL09002)The Ph.D.Fund Project of Lanzhou University of Science and Technology(No.BS01200904)
文摘Sol-gel technology was employed to synthesize nanosized precursors of La-Mg hydrogen storage alloy at different pH values (0.5, 1.5, 8.0 and 9.0) of reaction solution. The effect of pH value on microstructure of the nano precursors of La-Mg hydrogen storage alloy was studied by infrared radiation (IR), thermo-gravimetric and differential thermal analysis (TG/DTA), X-ray diffraction analyzer (XRD) and transmission electron microscopy (TEM). IR results indicate that the chelating agent, citric acid, is not fully ionized, and carboxyl groups are not entirely used to complex metal ions in acidic solutions. The efficiency of complexing metal ions is enhanced in basic solutions. TG/DTA results show that the combustion may take place with low rate of the flame propagation that causes the longer combustion time when pH<1.5. On the contrary, the dry gel synthesized in basic solution combusts at low ignition temperature and combustion reaction is violent; it is easy to form fine particles. XRD and TEM results reveal that the precursor powders are mainly two-phase mixture of La 2 O 3 and MgO. The morphology of the particles is almost flake with the size of ~30 nm when pH is 8.0.
基金the National Natural Science Foundation of China(22265021)the Aeronautical Science Foundation of China(2020Z056056003).
文摘Metal–organic gel(MOG)derived composites are promising multi-functional materials due to their alterable composition,identifiable chemical homogeneity,tunable shape,and porous structure.Herein,stable metal–organic hydrogels are prepared by regulating the complexation effect,solution polarity and curing speed.Meanwhile,collagen peptide is used to facilitate the fabrication of a porous aerogel with excellent physical properties as well as the homogeneous dispersion of magnetic particles during calcination.Subsequently,two kinds of heterometallic magnetic coupling systems are obtained through the application of Kirkendall effect.FeCo/nitrogen-doped carbon(NC)aerogel demonstrates an ultra-strong microwave absorption of−85 dB at an ultra-low loading of 5%.After reducing the time taken by atom shifting,a FeCo/Fe3O4/NC aerogel containing virus-shaped particles is obtained,which achieves an ultra-broad absorption of 7.44 GHz at an ultra-thin thickness of 1.59 mm due to the coupling effect offered by dual-soft-magnetic particles.Furthermore,both aerogels show excellent thermal insulation property,and their outstanding radar stealth performances in J-20 aircraft are confirmed by computer simulation technology.The formation mechanism of MOG is also discussed along with the thermal insulation and electromagnetic wave absorption mechanism of the aerogels,which will enable the development and application of novel and lightweight stealth coatings.
文摘Capillary column preparation using perpentylated (2,3,6-tri-O-pentyl)-β-cyclodextrin asstationary phase by sol-gel technology with simplicity and rapidity is described. Multiplepreparation steps in conventional column technology were avoided. The prepared columns exhibitsatisfactory chromatographic performances and pronounced selectivity for a wide range of testsolutes, and have been successfully used for the separation of nitrotoluene, dimethoxybenzene,alcohols, alkanes, dimethylphenol and cresol isomers.
文摘The sol-gel technology is applied for the preparation of solid-phase microextraction (SPME) fiber. The fiber demonstrates high thermal stability, efficient extraction rate and the selectivity for non-polar or low-polar analytes. Efficient SPME-GC-FID analyses of benzene- toluene-ethylbenzene-xylenes (BTEXs) and low-polar halocarbon were achieved by the sol-gel coated DSDA-DDBT-TiO2 fiber. Some parameters of the SPME fiber for the determination of halocarbon in aqueous sample were investigated.
文摘Heptakis(2, 3, 6-tri-O-octyl)-β-cyclodextrin was coated onto the fused silica capillary by sol-gel technology. Column efficiency and column selectivity were studied. The results indicated that high ability of separation was acquired . Positional isomers of aromatic compounds were well separated.
文摘The importance of foundry coating in improving the surface quality of castings cannot be over emphasized. The application of mould and core washes creates a high thermal integrity barrier between the metal and the mould resulting in the reduction of the thermal shock experienced by the sand system. These thermal shock leads to series of surface defects such as veining/finning, metal penetration, burn-on/in, scab, rat tail, erosion etc. The use of coatings reduces the tendency of occurrence of these defects. However, the understanding of the coating, its components, characteristics and mechanism of action is important. In this review, a detailed description of these topics and examples are provided where necessary. A potential area of research in foundry coating development, using sol-gel process is suggested. The application of sol-gel technology in the development of foundry coatings is a novel approach.