Effect of arc-ultrasound on microstructures and mechanical properties of plasma arc welded joints of SiC_p/Al MMCs

The effect of arc-ultrasound on microstructures and mechanical properties of SiCp/6061A1 MMCs joints produced by arc-ultrasound plasma arc ＂in-situ＂ alloy-welding with different excitation frequencies was investigated, in which argon-nitrogen mixture was used as plasma gas, Ti wire as filler and the arc-ultrasound was produced by modulating the plasma arc with high frequency. The results show that arc-ultrasound could refine the new reinforced composites such as TiC, TiN significantly, and improve their distribution greatly. And new phase A13Ti becomes finer and less. The test results of mechanical properties indicate that the maximum tensile strength of welded joints is gained when the excitation frequency is 50 kHz, and the maximum is 225 MPa, raising by about 7% comoared with conventional nlasma arc welding （PAW） （20q MPa）.

Influence of SiO_2 nano-particles on microstructures and properties of Ni-W-P/CeO_2-SiO_2 composites prepared by pulse electrodeposition

Ni-W-P base composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by pulse co-deposition of Ni,W,P,CeO2 and SiO2 nano-particles.The influence of SiO2 concentrations in bath on microstructures and properties of Ni-W-P/CeO2-SiO2 composites was studied,and the characteristics were assessed by chemical compositions,element distribution,surface morphologies,deposition rate and microhardness.The results indicate that when SiO2 concentration in bath is controlled at 20 g/L,the composites possess the fastest deposition rate,the highest microhardness,compact microstructures,smaller crystallite sizes and uniform distribution of W,P,Ce and Si within Ni-W-P matrix metal.Increasing SiO2 concentration in bath from 10 to 20 g/L leads to the refinement in grain size and the inhomogeneity of microstructures.While when SiO2 concentration is increased to 30 g/L,the crystallite sizes increase again and some bosses with nodulation shape appear on the surface of composites.

Production,Properties and Microstructures of Mg-RE-Zn-Zr(RE=MM,Nd) Alloy

The Mg-MM and Mg-Nd master alloys were prepared through the ingot metallurgy method under the protection of a special flux. The thermodynamic behaviors of different rare earth elements in the molten Mg alloys were investigated. Two experimental alloys, Mg-3.0 wt pct MM-0.7 wt pct Zn-0.7 wt pct Zr and Mg-2.8 wt pct Nd-0.7 wt pct Zn-0.7 wt pct Zr, were prepared. The hardness and tensile properties of experimental alloys were measured and the microstructures were observed. The results showed that the rare earth elements could react greatly with the Mg chloride in the flux. The Mg-Nd-Zn-Zr alloy displayed a good aging hardening effect. The dispersed metastable phase ? (Mg3Nd) is an important strengthening phase to improve the tensile properties of this alloy. So the Mg-Nd-Zn-Zr alloy has better tensile properties and elongation than those of the Mg-MM-Zn-Zr alloy, and the ductile fracture character could be observed. The microvoid coalescence is the dominant fracture mechanism in this alloy.

Microstructures and Properties of 550 MPa Grade High Strength Thin-walled H-beam Steel

The microstructures and mechanical properties of 550 MPa grade lightweight high strength thin-walled H-beam steel were experimentally studied. The experimental results show that the microstructure of the air-cooled H-beam steel sample is consisted of ferrite, pearlite and a small amount of granular bainites as well as fine and dispersive V（C,N） precipitates. The microstructure of the water-cooled steel sample is consisted of ferrite and bainite as well as a small amount of fine pearlites. The microstructure of the water-cooled sample is finer than that of the air-cooled sample with the average intercept size of the surface grains reaching to 3.5 gna. The finish rolling temperature of the thin-walled high strength H-beam steel is in the range of 750 ~C-850 ~C. The lower the finish rolling temperature and the faster the cooling rate, the finer the ferrite grains, the volume fraction of bainite is increased through water cooling process. Grain refinement strengthening and precipitation strengthening are used as major strengthening means to develop 550 MPa grade lightweight high strength thin- walled H-beam steel. Vanadium partially soluted in the matrix and contributes to the solution strengthening. The 550 MPa grade high-strength thin-walled H-beam steel could be developed by direct air cooling after hot rolling to fully meet the requirements of the target properties.

Properties,Microstructures and Precipitate Morphology of Hot-rolled Interstital-Free(IF)Steel Sheets

In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or region. In this paper, properties, microstructures and precipitate morphology of hot-rolled iF steel sheets are described..

Semisolid die forging process,microstructures and properties of AZ31 magnesium alloy mobile telephone shells

A semisolid slurry of AZ31 magnesium alloy was prepared by vibrating wavelike sloping plate process,and the semisolid die forging process,microstructures,and properties of the magnesium alloy mobile telephone shell were investigated.The semisolid forging process was performed on a YA32-315 four-column universal hydraulic press.The microstructures were observed by optical microscopy,the hardness was analyzed with a model 450SVD Vickers hardometer,the mechanical properties was measured with a CMT5105 tensile test machine,and the fractograph of elongated specimens was observed by scanning electron microscopy （SEM）.The results reveal that with the increase of die forging force,the microstructures of the product become fine and dense.A lower preheating temperature and a longer dwell time are favorable to the formation of fine and dense microstructures.The optimum process conditions of preparing mobile telephone shells with excellent surface quality and microstructures are a die forging force of 2000 kN,a die preheating temperature of 250℃,and a dwell time of 240 s.After solution treatment at 430℃ and aging at 220℃ for 8 h,the Vickers hardness is 61.7 and the ultimate tensile strength of the product is 193MPa.Tensile fractographs show the mixing mechanisms of quasi-cleavage fracture and ductile fracture.

Microstructures and Electrochemical Properties of Cobalt-Free LaNi_(4.0)Al_(0.2)Fe_(0.4)Cu_(0.4-x)Sn_x (x=0～0.4) Electrode Alloys Prepared by Casting

The microstructure, hydriding performance, and electrochemical properties of LaNi4.0Ai0.2Fe0.4Cu0.4-x Snx（x = 0- 0.4） hydrogen storage alloys prepared by casting were investigated using XRD, SEM, pressure-composition isotherms, and electrochemical measurements. Substitution of Sn for Cu leads to the precipitation of LaNiSn phase. With increasing amount of tin substitution, cell volume, plateau pressures, and discharge capacities of the alloys decrease, whereas the cycle life of the alloys improves.

The effect of annealing treatment on the microstructures and mechanical properties of cold-sprayed nickel coating

The effect of annealing treatment on the microstructures and mechanical properties of cold-sprayed Ni coating was investigated by conducting micro-hardness and tensile tests and using a normal optical microscope （OM） ,a scanning electron microscope （ SEM）, a transmission electron microscope （TEM） and an electron probe X-ray microanalyzer （EPMA）. The results show that following the increase of the annealing temperature ,the micro-hardness of cold-sprayed Ni coating decreases and the elongation after fracture increases, while the tensile strength increases before decreasing. The tensile deformation and fracture behavior change from a typical brittle fracture to a hybrid brittle and ductile fracture, then to a typical ductile failure. It is found that when annealed at an elevated temperature （ e. g. 900℃ ） ,the grains tend to grow abnormally with the oxides spheroidizing and the defects agglomerating at the interfaces, causing the tensile strength reduction of the cold-sprayed nickel coating. It is also pointed out that the tensile strength of the cold-sprayed Ni coating can be significantly improved by the appropriate annealing procedures, but the elongation after fracture cannot be clearly increased because it is difficult to eliminate the main defects in the coating by the following heat treatments.

Effect of aging temperature on the microstructures and mechanical properties of ZG12Cr9Mo1Co1NiVNbNB ferritic heat-resistant steel

The effect of aging on the mechanical properties and microstructures of a new ZG12Cr9 MolColNiVNbNB ferritic heat resistant steel was investigated in this work to satisfy the high steam parameters of the ultra-supercritical power plant.The results show that the main precipitates during aging are Fe（Cr,Mo）23C6,V（Nb）C,and（Fe2Mo） Laves in the steel.The amounts of the precipitated phases increase during aging,and correspondingly,the morphologies of phases are similar to be round.Fe（Cr,Mo）23C6 appears along boundaries and grows with increasing temperature.In addition,it is revealed that the martensitic laths are coarsened and eventually happen to be polygonization.The hardness and strength decrease gradually,whereas the plasticity of the steel increases.What＇s more,the hardness of this steel after creep is similar to that of other 9%-12%Cr ferritic steels.Thus,ZG12Cr9 MolColNiVNbNB can be used in the project.

Influences of oxide content and sintering temperature on microstructures and mechanical properties of intragranular-oxide strengthened iron alloys prepared by spark plasma sintering

How to increase strength without sacrificing ductility has been developed as a key goal in the manufacture of high-performance metals or alloys. Herein, the double-nanophase intragranular yttrium oxide dispersion strengthened iron alloy with high strength and appreciable ductility was fabricated by solution combustion route and subsequent spark plasma sintering, and the influences of yttrium oxide content and sintering temperature on microstructures and mechanical properties were investigated. The results show at the same sintering temperature,with the increase of yttrium oxide content, the relative density of the sintered alloy decreases and the strength increases. For Fe–2wt%Y_(2)O_(3)alloy, as the sintering temperature increases gradually, the compressive strength decreases, while the strain-to-failure increases. The Fe–2wt%Y_(2)O_(3)alloy with 15.5 nm Y_(2)O_(3)particles uniformly distributed into the 147.5 nm iron grain interior sintered at 650℃ presents a high ultimate compressive strength of 1.86 GPa and large strain-to-failure of 29%. The grain boundary strengthening and intragranular second-phase particle dispersion strengthening are the main dominant mechanisms to enhance the mechanical properties of the alloy.

Microstructure and Properties of AlCoCrFeNiTi High-Entropy Alloy Coatings Prepared by Laser Cladding

21-4N(5Cr21Mn9Ni4N)is extensively employed in the production of engine valves,operating under severe conditions.Apart from withstanding high-temperature gas corrosion,it must also endure the impact of cylinder explosion pressure.The predominant failure mode of 21-4N valves is abrasive wear.Surface coatings serve as an effective approach to prevent such failures.In this investigation,Laser cladding technology was utilized to fabricate AlCoCrFeNiTi high entropy alloy coatings onto the surfaces of 21-4N valves.According to the findings,the cladding zone has a normal dendritic microstructure,a good substrate-to-cladding layer interaction,and no obvious flaws.In terms of hardness,the cladding demonstrates an average hardness of 620 HV.The hardness has increased by 140%compared to the substrate.The average hardness of the cladding remains at approximately 520 HV even at elevated temperatures.Regarding frictional wear performance,between 400℃and 800℃,the cladding layer exhibits an average friction coefficient of 0.4,with the primary wear mechanisms being abrasive wear,adhesive wear,and a minor degree of plastic deformation.

Effect of induction heating and tempering on properties and microstructures of quenched and tempered pipes

In this study,a C-Mn quenched steel tube was quickly tempered by induction heating,and the influence of the tempering temperature on its performance was studied and compared with that by traditional tempering. The results show that the yield strength of both is quite strong with regular changes in the tempering temperature,but that the tensile strength of the tube tempered by induction heating is higher than that tempered by traditional tempering by about 25 MPa,and the elongation after induction tempering is significantly higher than that after traditional tempering. The differences in the microstructures of tubes after induction and traditional tempering were compared by metallographic microscope,scanning electron microscopy,and transmission electron microscopy.Theoretical analysis was also performed. Compared with traditional tempering,a fine dispersion of precipitated carbides occurs after induction tempering,which is the main reason for the performance differences.

Microstructure characterization and mechanical properties of TC4-DT titanium alloy after thermomechanical treatment

Influence of thermomechanical treatments （mill annealing, duplex annealing, solution treatment plus aging and triple annealing） on microstructures and mechanical properties of TC4-DT titanium alloy was investigated. Results showed that thermomechanical treatments had a significant influence on the microstructure parameters and higher annealing and aging temperature and lower cooling rate led to the decrease of the volume fraction of primaryαand the size of prior-βand the increase of the width of grain boundary αand secondary α. The highest strength was obtained by solution treatment and aging due to a large amount of transformedβand finer grain boundaryαand secondaryαat the expense of slight decrease of elongation and the ultimate strength, yield strength, elongation, reduction of area were 1100 MPa, 1030 MPa, 13%and 53%separately. A good combination of strength and ductility has been obtained by duplex annealing with the above values 940 MPa, 887.5 MPa, 15%and 51%respectively. Analysis between microstructure parameters and tensile properties showed that with the volume fraction of transformedβphase and the prior-βgrain size increasing, the ultimate strength, yield strength and reduction of area increased, but the elongation decreased. While the width of grain boundary α and secondary α showed a contrary effect on the tensile properties. Elimination of grain boundaryαas well as small prior-βgrain size can also improve ductility.

Mechanism of Effects of Rare Earths on Microstructure and Properties at Elevated Temperatures of AZ91 Magnesium Alloy

By using real-space recursion method,the energetics of the undoped and Al and/or RE atoms doped 7（1450）〈0001〉 symmetric tilt grain boundaries（GBs）in AZ91 alloys were investigated.Similar calculations were performed on undoped and doped bulk α Mg for comparison.The results showed that Al atoms segregated at GBs in AZ91 alloys.When RE atoms were added,they also segregated at GBs,and their segregation is stronger than Al atoms＇.Therefore,RE atoms retard the segregation of Al atoms.Calculations of interaction energy indicated that Al atoms repelled each other,and could form ordered phase with host Mg atoms.On the contrary to the case of Al,RE atoms attracted each other,they could not form ordered phase with Mg,but could form clusters.Between RE and Al,there existed attractive interaction,and this attractive interaction was the origin of Al11RE3 precipitation.Precipitation of Al11RE3 particles with high melting point and high thermal stability along GB improves high temperature properties of AZ91 alloys.

Effects of calcium addition on as-cast microstructure and mechanical properties of Mg-5Zn-5Sn alloy

The effects of Ca addition on the as-cast microstructure and mechanical properties of the Mg-5Zn-5Sn (mass fraction,%) alloy were investigated.The results indicate that an addition of 0.5%-1.5% (mass fraction) Ca to the Mg-5Zn-5Sn alloy not only refines the as-cast microstructure of the alloy but also causes the formation of the primary and/or eutectic CaMgSn phases with high thermal stability;an increase in Ca amount from 0.5% to 1.5% (mass fraction) increases the amount and size of the CaMgSn phase.In addition,Ca addition to the Mg-5Zn-5Sn alloy improves not only the tensile properties at room temperature and 150 ℃ but also the creep properties.Among the Ca-containing Mg-5Zn-5Sn alloys,the one added 0.5% (mass fraction) Ca obtains the optimum ultimate tensile strength and elongation at room temperature and 150 ℃,however,the alloy added 1.5% (mass fraction) Ca exhibits the optimum yield strength and creep properties.

Effect of austempering parameters on microstructure and mechanical properties of horizontal continuous casting ductile iron dense bars

In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters （i.e. austenitizing temperature and time, and austempering temperature and time） on microstructure and mechanical properties of LZQT500-7 ductile iron dense bars with 172 mm in diameter which were produced by horizontal continuous casting （HCC）. The results show that the major factors influencing the hardness of austempered ductile iron （ADI） are austenitizing temperature and austempering temperature. The fraction of retained austenite increases as the austenitizing and austempering temperatures increase. When austenitizing temperature is low, acicular ferrite and retained austenite can be efifciently obtained by appropriately extending the austenitizing time. The proper austmepering time could ensure enough stability of retained austenite and prevent high carbon austenite decomposition. The optimal mechanical properties of ADI can be achieved with the fol owing process parameters： austenitizing temperature and time are 866 ＆#176;C and 135 min, and austempering temperature and time are 279 ＆#176;C and 135 min, respectively. The microstructure of ADI under the optimal austempering process consists of ifne acicular ferrite and a smal amount of retained austenite, and the hardness, tensile strength, yield strength, elongation and impact toughness of the bars are HBW 476, 1670 MPa, 1428 MPa, 2.93%and 25.7 J, respectively.

Effect of V and Nb additions on microstructure,properties,and deformability of Ti-45Al-9 (V,Nb,Y) alloy

Ti-45Al-9(V, Nb, Y) alloys with four different x=V/Nb (atomic ratio x = 1, 1.5, 2 and 3.5) have been prepared, and the microstructures, properties and hot deformation behaviors were investigated. SEM, XRD and TEM results showed that Ti-45Al-9(V, Nb, Y) alloys were mainly composed of γ, α 2 , and β phase, and the volume fraction of β phase increased with the increase of the atomic ratio of V/Nb. The alloys were featured with lamellar microstructure with β and γ phases locating at the colony boundaries, and some β precipitates appearing at γ/γ interfaces. It was found that the colony size decreased with the increase of x. The alloys exhibited moderate mechanical properties at room temperature, with a yield strength of over 600 MPa, and fractures showed mainly translamellar character. The alloy with x=3.5 exhibited the best deformability at elevated temperature and that with x=1 had superior oxidation resistance at 800 ℃.

Effect of extrusion on the microstructure and mechanical properties of a low-alloyed Mg-2Zn-0.8Sr-0.2Ca matrix composite reinforced by TiC nano-particles

A low-alloyed Mg-2Zn-0.8Sr-0.2Ca matrix composite reinforced by TiC nano-particles was successfully prepared by semi-solid stirring under the assistance of ultrasonic,and then the as-cast composite was hot extruded.The results indicated that the volume fraction of dynamical recrystallization and the recrystallized grain size have a certain decline at lower extrusion temperature or rate.The finest grain size of~0.30μm is obtained in the sample extruded at 200℃ and 0.1 mm/s.The as-extruded sample displays a strong basal texture intensity,and the basal texture intensity increases to 5.937 mud while the extrusion temperature increases from 200 to 240℃.The ultra-high mechanical properties(ultimate tensile strength of 480.2 MPa,yield strength of 462 MPa)are obtained after extrusion at 200℃ with a rate of 0.1 mm/s.Among all strengthening mechanisms for the present composite,the grain refinement contributes the most to the increase in strength.A mixture of cleavage facets and dimples were observed in the fracture surfaces of three as-extruded nanocomposites,which explain a mix of brittle-ductile fracture way of the samples.

Mechanical Properties and Microstructure of Portland Cement Concrete Prepared with Coral Reef Sand

The feasibility of using coral reef sand（CRS） in Portland cement concrete is investigated by testing the mechanical property and microstructure of concrete. The composition, structure and properties of the CRS are analyzed. Mechanical properties and microstructure of concrete with CRS are studied and compared to concrete with natural river sand. The relationship between the microstructure and performance of CRS concrete is established. The CRS has a porous surface with high water intake capacity, which contributes to the mechanical properties of concrete. The interfacial transition zone between the cement paste and CRS is densified compared to normal concrete with river sand. Hydration products form in the pore space of CRS and interlock with the matrix of cement paste, which increases the strength. The total porosity of concrete prepared with CRS is higher than that with natural sand. The main difference in pore size distribution is the fraction of fine pores in the range of 100 nm.

Effects of Dysprosium Oxide Doping on Microstructure and Properties of Barium Titanate Ceramic

Different amounts of dysprosium oxide were incorporated into barium titanate powders synthesized by hydrothermal method. Relations of substitution behaviors and lattice parameters with solid-solubility were studied. Furthermore, the influences of dysprosium oxide doping fraction on grain size and dielectric properties of barium titanate ceramic, including dielectric constant and breakdown electric field strength , were investigated via scanning electron microscope, X-ray diffraction and electric property tester. The results show that dysprosium oxide can restrain abnormal grain growth during sintering and that fine-grained and high density of barium titanate ceramic can result in excellent dielectric properties. As mass fraction of dysprosium oxide is 0.6%, the lattice parameters of grain increase to the maximum because of the lowest vacancy concentration. The electric property parameters are cited as following： dielectric constant （25 ℃ ） reaches 4100, the change in relative dielectric constant with temperature is - 10% to 10% within the range of - 15 - 100 ℃, breakdown electric field strength （alternating current） achieves 3.2 kV·mm^-1, which can be used in manufacturing high voltage ceramic capacitors