Evolution of Joint Formation in Resistance Microwelding of Crossed Pt-10%Ir and 316 LVM Stainless Steel Wires 被引量:2
1
作者 黄永德 肖林 +1 位作者 Andie PEQUEGNAT ZHOU Yunhong 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2015年第6期1286-1290,共5页
The surface morphology, cross-sections, and joint break force(JBF) of joints welded under different electrode forces were studied. The defects, such as electrode sticking, notch, and excessive expulsions, were obser... The surface morphology, cross-sections, and joint break force(JBF) of joints welded under different electrode forces were studied. The defects, such as electrode sticking, notch, and excessive expulsions, were observed in the joints. No desirable joints were achieved with the consideration of weld geometries and joint performances. From the cross-sectional morphology, the joint evolution during the RMW of Pt alloy and 316 LVM SS wires was developed, which involved cold collapse and heat promoted set-down of Pt alloy wire, unbalanced heating at interface, molten phase squeezed out, and defect formation. Finally, the defect formation was also discussed. 展开更多
关键词 Pt-10%Ir 316 LVM SS resistance microwelding evolution of joint formation notch defects
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部