Heterogeneous catalyst aluminium oxide(acidic) is found to be an effective catalyst for the solvent-free condensation reaction of indole with aldehydes in microwave irradiation with shorter reaction time and higher yi...Heterogeneous catalyst aluminium oxide(acidic) is found to be an effective catalyst for the solvent-free condensation reaction of indole with aldehydes in microwave irradiation with shorter reaction time and higher yields.展开更多
Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile me...Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile memories,neuromorphic computation and data encryption.However,the deposition of memristive films often requires expensive equipment,strict vacuum conditions,high energy consumption,and extended processing times.In contrast,electrochemical anodizing can produce metal oxide films quickly(e.g.10 s) under ambient conditions.By means of the anodizing technique,oxide films,oxide nanotubes,nanowires and nanodots can be fabricated to prepare memristors.Oxide film thickness,nanostructures,defect concentrations,etc,can be varied to regulate device performances by adjusting oxidation parameters such as voltage,current and time.Thus memristors fabricated by the anodic oxidation technique can achieve high device consistency,low variation,and ultrahigh yield rate.This article provides a comprehensive review of the research progress in the field of anodic oxidation assisted fabrication of memristors.Firstly,the principle of anodic oxidation is introduced;then,different types of memristors produced by anodic oxidation and their applications are presented;finally,features and challenges of anodic oxidation for memristor production are elaborated.展开更多
Aluminium oxide coatings were formed on aluminium substrates in oxalic acid-sulphuric acid bath. Abrasion tests of the obtained anodic layers were carried out on a pin-on-disc machine in accordance with the ISO/DP 825...Aluminium oxide coatings were formed on aluminium substrates in oxalic acid-sulphuric acid bath. Abrasion tests of the obtained anodic layers were carried out on a pin-on-disc machine in accordance with the ISO/DP 825 specifications. The rickets microhardness, D (HV0.2), and the abrasion weight loss, Wa (mg) were measured. Influence of oxalic acid concentration (Cox), bath temperature (T) and anodic current density (J) on D and Wa has been examined, and the sulphuric acid concentration (Csul) was maintained at 100 g.L-1. It was found that high microhardness and abrasive wear resistance of oxide layers were produced under low temperatures and high current densities with the addition of oxalic acid. The morphology and the composition of the anodic oxide layer were examined by scanning electron microscopy (SEM), atomic force microscopy (AFM), optical microscopy and glow-discharge optical emission spectroscopy (GDOES). It was found that the chemistry of the anodizing electrolyte, temperature, and current density are the controlling factors of the mechanical properties of the anodic oxide layer.展开更多
The structure and properties of coatings based on WC-Co alloys containing additives of 1% - 5% aluminium oxide and 2.5% - 4.5% carbon were investigated. The coatings had a nanocrystalline structure. Depending on the d...The structure and properties of coatings based on WC-Co alloys containing additives of 1% - 5% aluminium oxide and 2.5% - 4.5% carbon were investigated. The coatings had a nanocrystalline structure. Depending on the duration and frequency of the discharge pulses, the ratio between WC and W2C in the coatings was different. The additives in the hard alloy allowed us increase the microhardness and wear resistance of the coatings by a factor of 2 - 3 in comparison to coatings created using a conventional WC-10%Co alloy.展开更多
The composition,structure and micro-morphology of magnesium- iron- aluminum composite oxides were investigated using various methods such as XRF,SEM,EDS,XRD and KMn O4-titration. Compared to hercynite,the composite ox...The composition,structure and micro-morphology of magnesium- iron- aluminum composite oxides were investigated using various methods such as XRF,SEM,EDS,XRD and KMn O4-titration. Compared to hercynite,the composite oxides have completely different phases including solid solution( Mg O)0. 77( Fe O)0. 23,composite spinel Mg Fe0. 2Al1. 8O4 and a small amount of Mg Fe2O4. The composite oxides exhibit excellent corrosion resistance to cement clinker and potassium salts.The products produced by magnesite and the composite oxides show better performance than magnesia- hercynite bricks,especially the corrosion resistance and thermal shock resistance.展开更多
Micro-arc oxidation(MAO) technique is capable of producing dense oxide films on the aluminium alloy surface. This oxide film protects the aluminium alloy from the corrosion attack for longer duration.Empirical relatio...Micro-arc oxidation(MAO) technique is capable of producing dense oxide films on the aluminium alloy surface. This oxide film protects the aluminium alloy from the corrosion attack for longer duration.Empirical relationships were derived to evaluate the MAO coating properties(porosity and hardness) by incorporating very important MAO parameters(current density, inter-electrode distance and oxidation time). MAO parameters were also optimized to achieve coatings with minimum porosity and maximum hardness. Further, the effect of MAO parameters on coating characteristics was analysed. From the results, it is found that the current density has greater influence on the responses than the other two parameters.展开更多
Thick and hard ceramic coatings were prepared on the Al-Cu-Mg alloy by microarc oxidation in alkali-silicate electrolytic solution. The thickness and microhardness of the oxide coatings were measured. The influence of...Thick and hard ceramic coatings were prepared on the Al-Cu-Mg alloy by microarc oxidation in alkali-silicate electrolytic solution. The thickness and microhardness of the oxide coatings were measured. The influence of current density on the growth rate of the coating was examined. The microstructure and phase composition of the coatings were investigated by means of scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction. Moreover, the tensile strength of the Al alloy before and after microarc oxidation treatment were tested, and the fractography and morphology of the oxide coatings were observed using scanning electron microscope. It is found that the current density considerably influences the growth rate of the microarc oxidation coatings. The oxide coating is mainly composed of α-Al2O3 and γ-Al2O3, while high content of Si is observed in the superficial layer of the coating. The cross-section microhardness of 120 μm thick coating reaches the maximum at distance of 35 μm from the substrate/coating interface. The tensile strength and elongation of the coated Al alloy significantly decrease with increasing coating thickness. The microarc oxidation coatings greatly improve the wear resistance of Al alloy, but have high friction coefficient which changes in the range of 0.70.8. Under grease lubricating, friction coefficient is only 0.15 and wear loss is less than 1/10 of the loss under dry friction.展开更多
Interest in energy harvesters has grown rapidly over the last decade. The cantilever shaped piezoelectric energy harvesting beam is one of the most employed designs, due to its simplicity and flexibility for further p...Interest in energy harvesters has grown rapidly over the last decade. The cantilever shaped piezoelectric energy harvesting beam is one of the most employed designs, due to its simplicity and flexibility for further performance enhancement. The research effort in the MEMS Piezoelectric vibration energy harvester designed using three types of cantilever materials, Lithium Niobate (LiNbO3), Aluminum Nitride (AlN) and Zinc Oxide (ZnO) with different substrate materials: aluminum, steel and silicon using COMSOL Multiphysics package were designed and analyzed. Voltage, mechanical power and electrical power versus frequency for different cantilever materials and substrates were modeled and simulated using Finite element method (FEM). The resonant frequencies of the LiNbO3/Al, AlN/Al and ZnO/Al systems were found to be 187.5 Hz, 279.5 Hz and 173.5 Hz, respectively. We found that ZnO/Al system yields optimum voltage and electrical power values of 8.2 V and 2.8 mW, respectively. For ZnO cantilever on aluminum, steel and silicon substrates, we found the resonant frequencies to be 173.5 Hz, 170 Hz and 175 Hz, respectively. Interestingly, ZnO/steel yields optimal voltage and electrical power values of 9.83 V and 4.02 mW, respectively. Furthermore, all systems were studied at different differentiate frequencies. We found that voltage and electrical power have increased as the acceleration has increased.展开更多
Surface-enhanced Raman scattering(SERS)platform,which enables trace analyte detection,has important application prospects.By structuring/modifying the surface of the SERSsubstrate,analyte in highly diluted solutions c...Surface-enhanced Raman scattering(SERS)platform,which enables trace analyte detection,has important application prospects.By structuring/modifying the surface of the SERSsubstrate,analyte in highly diluted solutions can be concentrated into localized active areas for highly sensitive detection.However,subject to the difficulty of the fabrication process,itremains challenging to balance hot-spot construction and the concentration capacity of analyte simultaneously.Therefore,preparing SERS substrates with densely ordered hot spots andefficient concentration capacity is of great significance for highly sensitive detection.Herein,we propose an Ag and fluoroalkyl-modified hierarchical armour substrate(Ag/F-HA),which has a double-layer stacking design to combine analyte concentration with hotspot construction.The microarmour structure is fabricated by femtosecond-laser processing to serve as asuperhydrophobic and low-adhesive surface to concentrate analyte,while the anodic aluminium oxide(AAO)template creates a nanopillar array serving as dense and ordered hot spots.Under the synergistic action of hot spots and analyte concentration,Ag/F-HA achieves a detectionlimit down to 10^(-7)M doxorubicin(DOX)molecules with a RSD of 7.69%.Additionally,Ag/F-HA exhibits excellent robustness to resist external disturbances such as liquid splash or abrasion.Based on our strategy,SERS substrates with directional analyte concentrations are further explored by patterning microcone arrays with defects.This work opens a way to the realistic implementation of SERS in diverse scenarios.展开更多
文摘Heterogeneous catalyst aluminium oxide(acidic) is found to be an effective catalyst for the solvent-free condensation reaction of indole with aldehydes in microwave irradiation with shorter reaction time and higher yields.
基金supported by the National Key Research and Development Program of China (Grant No.2018YFE0203802)Natural Science Foundation of Hubei Province, China (Grant No.2022CFA031)Dongguan Innovative Research Team Program (2020607101007)。
文摘Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile memories,neuromorphic computation and data encryption.However,the deposition of memristive films often requires expensive equipment,strict vacuum conditions,high energy consumption,and extended processing times.In contrast,electrochemical anodizing can produce metal oxide films quickly(e.g.10 s) under ambient conditions.By means of the anodizing technique,oxide films,oxide nanotubes,nanowires and nanodots can be fabricated to prepare memristors.Oxide film thickness,nanostructures,defect concentrations,etc,can be varied to regulate device performances by adjusting oxidation parameters such as voltage,current and time.Thus memristors fabricated by the anodic oxidation technique can achieve high device consistency,low variation,and ultrahigh yield rate.This article provides a comprehensive review of the research progress in the field of anodic oxidation assisted fabrication of memristors.Firstly,the principle of anodic oxidation is introduced;then,different types of memristors produced by anodic oxidation and their applications are presented;finally,features and challenges of anodic oxidation for memristor production are elaborated.
文摘Aluminium oxide coatings were formed on aluminium substrates in oxalic acid-sulphuric acid bath. Abrasion tests of the obtained anodic layers were carried out on a pin-on-disc machine in accordance with the ISO/DP 825 specifications. The rickets microhardness, D (HV0.2), and the abrasion weight loss, Wa (mg) were measured. Influence of oxalic acid concentration (Cox), bath temperature (T) and anodic current density (J) on D and Wa has been examined, and the sulphuric acid concentration (Csul) was maintained at 100 g.L-1. It was found that high microhardness and abrasive wear resistance of oxide layers were produced under low temperatures and high current densities with the addition of oxalic acid. The morphology and the composition of the anodic oxide layer were examined by scanning electron microscopy (SEM), atomic force microscopy (AFM), optical microscopy and glow-discharge optical emission spectroscopy (GDOES). It was found that the chemistry of the anodizing electrolyte, temperature, and current density are the controlling factors of the mechanical properties of the anodic oxide layer.
文摘The structure and properties of coatings based on WC-Co alloys containing additives of 1% - 5% aluminium oxide and 2.5% - 4.5% carbon were investigated. The coatings had a nanocrystalline structure. Depending on the duration and frequency of the discharge pulses, the ratio between WC and W2C in the coatings was different. The additives in the hard alloy allowed us increase the microhardness and wear resistance of the coatings by a factor of 2 - 3 in comparison to coatings created using a conventional WC-10%Co alloy.
文摘The composition,structure and micro-morphology of magnesium- iron- aluminum composite oxides were investigated using various methods such as XRF,SEM,EDS,XRD and KMn O4-titration. Compared to hercynite,the composite oxides have completely different phases including solid solution( Mg O)0. 77( Fe O)0. 23,composite spinel Mg Fe0. 2Al1. 8O4 and a small amount of Mg Fe2O4. The composite oxides exhibit excellent corrosion resistance to cement clinker and potassium salts.The products produced by magnesite and the composite oxides show better performance than magnesia- hercynite bricks,especially the corrosion resistance and thermal shock resistance.
基金Council of Scientific and Industrial Research (G8/19901/2013), New Delhi for the financial support provided to conduct this investigation through sponsored project No. 22(0615)/13/EMR-II dated 26.02.2013
文摘Micro-arc oxidation(MAO) technique is capable of producing dense oxide films on the aluminium alloy surface. This oxide film protects the aluminium alloy from the corrosion attack for longer duration.Empirical relationships were derived to evaluate the MAO coating properties(porosity and hardness) by incorporating very important MAO parameters(current density, inter-electrode distance and oxidation time). MAO parameters were also optimized to achieve coatings with minimum porosity and maximum hardness. Further, the effect of MAO parameters on coating characteristics was analysed. From the results, it is found that the current density has greater influence on the responses than the other two parameters.
文摘Thick and hard ceramic coatings were prepared on the Al-Cu-Mg alloy by microarc oxidation in alkali-silicate electrolytic solution. The thickness and microhardness of the oxide coatings were measured. The influence of current density on the growth rate of the coating was examined. The microstructure and phase composition of the coatings were investigated by means of scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction. Moreover, the tensile strength of the Al alloy before and after microarc oxidation treatment were tested, and the fractography and morphology of the oxide coatings were observed using scanning electron microscope. It is found that the current density considerably influences the growth rate of the microarc oxidation coatings. The oxide coating is mainly composed of α-Al2O3 and γ-Al2O3, while high content of Si is observed in the superficial layer of the coating. The cross-section microhardness of 120 μm thick coating reaches the maximum at distance of 35 μm from the substrate/coating interface. The tensile strength and elongation of the coated Al alloy significantly decrease with increasing coating thickness. The microarc oxidation coatings greatly improve the wear resistance of Al alloy, but have high friction coefficient which changes in the range of 0.70.8. Under grease lubricating, friction coefficient is only 0.15 and wear loss is less than 1/10 of the loss under dry friction.
文摘Interest in energy harvesters has grown rapidly over the last decade. The cantilever shaped piezoelectric energy harvesting beam is one of the most employed designs, due to its simplicity and flexibility for further performance enhancement. The research effort in the MEMS Piezoelectric vibration energy harvester designed using three types of cantilever materials, Lithium Niobate (LiNbO3), Aluminum Nitride (AlN) and Zinc Oxide (ZnO) with different substrate materials: aluminum, steel and silicon using COMSOL Multiphysics package were designed and analyzed. Voltage, mechanical power and electrical power versus frequency for different cantilever materials and substrates were modeled and simulated using Finite element method (FEM). The resonant frequencies of the LiNbO3/Al, AlN/Al and ZnO/Al systems were found to be 187.5 Hz, 279.5 Hz and 173.5 Hz, respectively. We found that ZnO/Al system yields optimum voltage and electrical power values of 8.2 V and 2.8 mW, respectively. For ZnO cantilever on aluminum, steel and silicon substrates, we found the resonant frequencies to be 173.5 Hz, 170 Hz and 175 Hz, respectively. Interestingly, ZnO/steel yields optimal voltage and electrical power values of 9.83 V and 4.02 mW, respectively. Furthermore, all systems were studied at different differentiate frequencies. We found that voltage and electrical power have increased as the acceleration has increased.
基金National Natural Science Foundation of China(Nos.92050203,52122511,52305319,52375582)Shenzhen Fundamental Research Program(Nos.JCYJ20200109105606426,JCYJ20190808164007485)。
文摘Surface-enhanced Raman scattering(SERS)platform,which enables trace analyte detection,has important application prospects.By structuring/modifying the surface of the SERSsubstrate,analyte in highly diluted solutions can be concentrated into localized active areas for highly sensitive detection.However,subject to the difficulty of the fabrication process,itremains challenging to balance hot-spot construction and the concentration capacity of analyte simultaneously.Therefore,preparing SERS substrates with densely ordered hot spots andefficient concentration capacity is of great significance for highly sensitive detection.Herein,we propose an Ag and fluoroalkyl-modified hierarchical armour substrate(Ag/F-HA),which has a double-layer stacking design to combine analyte concentration with hotspot construction.The microarmour structure is fabricated by femtosecond-laser processing to serve as asuperhydrophobic and low-adhesive surface to concentrate analyte,while the anodic aluminium oxide(AAO)template creates a nanopillar array serving as dense and ordered hot spots.Under the synergistic action of hot spots and analyte concentration,Ag/F-HA achieves a detectionlimit down to 10^(-7)M doxorubicin(DOX)molecules with a RSD of 7.69%.Additionally,Ag/F-HA exhibits excellent robustness to resist external disturbances such as liquid splash or abrasion.Based on our strategy,SERS substrates with directional analyte concentrations are further explored by patterning microcone arrays with defects.This work opens a way to the realistic implementation of SERS in diverse scenarios.