The vascular graft with 4 mm diameter was prepared by casting one layer of polyurethane (PU) film onto the knitting tubular fabric as the reinforced support. The effects of different PU content and wall thickness on t...The vascular graft with 4 mm diameter was prepared by casting one layer of polyurethane (PU) film onto the knitting tubular fabric as the reinforced support. The effects of different PU content and wall thickness on the longitudinal mechanical properties of vascular graft were investigated. The breaking elongation, breaking force, initial modulus and breaking work were studied. The results showed that the longitudinal mechanical properties of vascular graft were enhanced as the content of polyurethane increased, which resulted from the combination of PU excellent elasticity and fabric preferable strength.展开更多
In this paper,a kind of composite microtube,which is made from superfine silk powder and polyurethane,reinforced by polyster and spandex tubular fabrics,was examined.The cross-section of composite microtubes were micr...In this paper,a kind of composite microtube,which is made from superfine silk powder and polyurethane,reinforced by polyster and spandex tubular fabrics,was examined.The cross-section of composite microtubes were microporous,and micropores were uniform distributed,the inner surface was relatively smooth.The results showed that the wall thickness of composite microtubes increased,which led to the strength,the breaking work and the initial modulus incresead;that the spandex content increased brought about the initial modulus and the breaking work decreased,but the breaking extension and the breaking load were firstly increased and then decreased;and all the mechanical properties decreased as the SFSP content increased.展开更多
In order to avoid the delamination of traditional laminated tubular composites,on an ordinary loom,the 3D woven special⁃shaped square tubular fabrics were woven with environment⁃friendly basalt filament yarns,and then...In order to avoid the delamination of traditional laminated tubular composites,on an ordinary loom,the 3D woven special⁃shaped square tubular fabrics were woven with environment⁃friendly basalt filament yarns,and then the 3D woven special⁃shaped square tubular composites were prepared with epoxy resin by a vacuum⁃assisted resin transfer molding(VARTM)process.Through experiments and software fitting,the axial compression properties of composites were analyzed.The polynomial fitting formulas of load⁃displacement curve and energy⁃displacement curve were obtained by using least square methods.The results showed that the 3D woven special⁃shaped square tubular composites had good axial compression performance,and with the increase of the composite thickness,compressive strength and energy absorption increased significantly.The failure mode was analyzed in the paper,thus revealing the failure stress propagation,local stress concentration,and failure morphology.It provides an effective reference for the design and application of the 3D woven special⁃shaped square tubular composite.展开更多
基金Supported by Education Depart ment of Hubei Province,China (No. Z200717001)
文摘The vascular graft with 4 mm diameter was prepared by casting one layer of polyurethane (PU) film onto the knitting tubular fabric as the reinforced support. The effects of different PU content and wall thickness on the longitudinal mechanical properties of vascular graft were investigated. The breaking elongation, breaking force, initial modulus and breaking work were studied. The results showed that the longitudinal mechanical properties of vascular graft were enhanced as the content of polyurethane increased, which resulted from the combination of PU excellent elasticity and fabric preferable strength.
基金State Natural Sciences Fundgrant number:50873079+1 种基金National Major Foudamental Research Program of Chinagrant number:2009CB526402
文摘In this paper,a kind of composite microtube,which is made from superfine silk powder and polyurethane,reinforced by polyster and spandex tubular fabrics,was examined.The cross-section of composite microtubes were microporous,and micropores were uniform distributed,the inner surface was relatively smooth.The results showed that the wall thickness of composite microtubes increased,which led to the strength,the breaking work and the initial modulus incresead;that the spandex content increased brought about the initial modulus and the breaking work decreased,but the breaking extension and the breaking load were firstly increased and then decreased;and all the mechanical properties decreased as the SFSP content increased.
基金Natural Science Foundation of Liaoning Province,China(No.2019⁃MS⁃017)。
文摘In order to avoid the delamination of traditional laminated tubular composites,on an ordinary loom,the 3D woven special⁃shaped square tubular fabrics were woven with environment⁃friendly basalt filament yarns,and then the 3D woven special⁃shaped square tubular composites were prepared with epoxy resin by a vacuum⁃assisted resin transfer molding(VARTM)process.Through experiments and software fitting,the axial compression properties of composites were analyzed.The polynomial fitting formulas of load⁃displacement curve and energy⁃displacement curve were obtained by using least square methods.The results showed that the 3D woven special⁃shaped square tubular composites had good axial compression performance,and with the increase of the composite thickness,compressive strength and energy absorption increased significantly.The failure mode was analyzed in the paper,thus revealing the failure stress propagation,local stress concentration,and failure morphology.It provides an effective reference for the design and application of the 3D woven special⁃shaped square tubular composite.