In order to reduce the cost and to improve the low temperature bonding strength of phenol formaldehyde resin（ PF）,the lignin modified phenol formaldehyde resin（ LPF） was synthesized using calcium lignosulfonate as...In order to reduce the cost and to improve the low temperature bonding strength of phenol formaldehyde resin（ PF）,the lignin modified phenol formaldehyde resin（ LPF） was synthesized using calcium lignosulfonate as a partial replacement of phenol,and sodium hydroxide as catalyzer. Then the magnesia carbon bricks were prepared using the LPF as binder. Different process conditions of LPFs such as calcium lignosulfonate additions（ 10%,20%,30%,40% and 50%,in mass,the same hereinafter）,catalyzer additions（ extra added,1%,2%,3%,4% and 5%） and reaction times（ 1,1. 5,2,2. 5 and 3 h） were investigated. Effects of prepared LPFs on properties of magnesia carbon bricks（ baked at 200 ℃ for 24 h） were researched in order to modify the synthesizing conditions of LPFs. Cold physical properties and hot modulus of rupture of magnesia carbon bricks bonded by LPF and by traditional PF after baked at 200 ℃ for 24 h and fired at 1 200 ℃ for 3 h were compared,respectively. The results show that the optimal synthesizing conditions of LPF for preparing magnesia carbon bricks are 30% calcium lignosulfonate,1% catalyzer,and 2 h reaction time. The magnesia carbon bricks bonded by the optimal LPF achieve：（ 1） the bulk densities 2. 84 g · cm- 3and 2. 82g·cm- 3,apparent porosities 9. 6% and 14. 6%,moduli of rupture 17. 8 MPa and 6. 4 MPa,crushing strengths72. 3 MPa and 48. 7 MPa,after baked at 200 ℃ and1 200 ℃,respectively;（ 2） the hot modulus of rupture7. 3 MPa after fired at 1 400 ℃. The above properties are better than those of the magnesia carbon brick bonded by PF.展开更多
基金New Century Excellent Talents Program of Ministry of Education ( NCET - 09 - 0137 )The open foundation of the State Key Laboratory of Refractories and Metallurgy ( 2014QN17 )
文摘In order to reduce the cost and to improve the low temperature bonding strength of phenol formaldehyde resin（ PF）,the lignin modified phenol formaldehyde resin（ LPF） was synthesized using calcium lignosulfonate as a partial replacement of phenol,and sodium hydroxide as catalyzer. Then the magnesia carbon bricks were prepared using the LPF as binder. Different process conditions of LPFs such as calcium lignosulfonate additions（ 10%,20%,30%,40% and 50%,in mass,the same hereinafter）,catalyzer additions（ extra added,1%,2%,3%,4% and 5%） and reaction times（ 1,1. 5,2,2. 5 and 3 h） were investigated. Effects of prepared LPFs on properties of magnesia carbon bricks（ baked at 200 ℃ for 24 h） were researched in order to modify the synthesizing conditions of LPFs. Cold physical properties and hot modulus of rupture of magnesia carbon bricks bonded by LPF and by traditional PF after baked at 200 ℃ for 24 h and fired at 1 200 ℃ for 3 h were compared,respectively. The results show that the optimal synthesizing conditions of LPF for preparing magnesia carbon bricks are 30% calcium lignosulfonate,1% catalyzer,and 2 h reaction time. The magnesia carbon bricks bonded by the optimal LPF achieve：（ 1） the bulk densities 2. 84 g · cm- 3and 2. 82g·cm- 3,apparent porosities 9. 6% and 14. 6%,moduli of rupture 17. 8 MPa and 6. 4 MPa,crushing strengths72. 3 MPa and 48. 7 MPa,after baked at 200 ℃ and1 200 ℃,respectively;（ 2） the hot modulus of rupture7. 3 MPa after fired at 1 400 ℃. The above properties are better than those of the magnesia carbon brick bonded by PF.
