The density of liquid binary Ni-Mo alloys with molybdenum concentration from 0 to 20% (mass fraction) wasmeasured by a modified sessile drop method. It has been found that the density of the liquid Ni-Mo alloys decrea...The density of liquid binary Ni-Mo alloys with molybdenum concentration from 0 to 20% (mass fraction) wasmeasured by a modified sessile drop method. It has been found that the density of the liquid Ni-Mo alloys decreaseswith increasing temperature, but increases with the increase of molybdenum concentration in the alloys. The molarvolume of liquid Ni-Mo binary alloys increases with the increase of temperature and molybdenum concentration. Thepartial molar volume of molybdenum in Ni-Mo binary alloy has been approximately calculated as [13.18-2.65×10^(-3)T+(-47.94+3.10×10^(-2)T)×10^(-2)X_(Mo)]×10^(-6)m^3·mol^(-1). The molar volume of Ni-Mo alloy determined inthe present work shows a negative deviation from the ideal linear mixing molar volume.展开更多
The density of liquid Ni-Ta alloys was measured by using a modified sessile drop method. It is found that the density of the liquid Ni-Ta alloys decreases with the increasing temperature, but increases with the increa...The density of liquid Ni-Ta alloys was measured by using a modified sessile drop method. It is found that the density of the liquid Ni-Ta alloys decreases with the increasing temperature, but increases with the increase of tantalum concentration in the alloys. The molar volume of liquid Ni-Ta binary alloys increases with the increase of temperature and tantalum concentration.展开更多
The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume ...The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume of liquidNi-Cr alloy increases with increasing the Cr concentration in the alloy. The molar volume of Ni-Cr alloy determinedin the present work shows a positive deviation from the linear molar volume.展开更多
The density of three kinds of liquid steel was measured by a modified sessile drop method over the temperature range of 1803-1 873 K.It is found that the density of liquid steels decreases with increasing temperature ...The density of three kinds of liquid steel was measured by a modified sessile drop method over the temperature range of 1803-1 873 K.It is found that the density of liquid steels decreases with increasing temperature and carbon content in steel.Both of the density and its absolute temperature coefficient of studied steels are smaller than the literature values of pure iron.The molar volume of the steels increases with increasing temperature.展开更多
The density of Ni-Cr alloy in the mushy state has been measured using the modified sessile drop method. The density of Ni-Cr alloy in the mushy state was found to decrease with increasing temperature and Cr concentrat...The density of Ni-Cr alloy in the mushy state has been measured using the modified sessile drop method. The density of Ni-Cr alloy in the mushy state was found to decrease with increasing temperature and Cr concentration in alloy. The molar volume of Ni-Cr alloy in the mushy state therefore increases with increasing the Cr concentration in alloy. The ratio of the difference of density divided by the temperature difference between liquidus and solidus temperatures decreases with increasing Cr concentration. The density of the alloy increased with the precipitation of a solid phase in alloy during the solidification process. The temperature dependence of the density of alloy in the mushy state was not linear but biquadratic.展开更多
文摘The density of liquid binary Ni-Mo alloys with molybdenum concentration from 0 to 20% (mass fraction) wasmeasured by a modified sessile drop method. It has been found that the density of the liquid Ni-Mo alloys decreaseswith increasing temperature, but increases with the increase of molybdenum concentration in the alloys. The molarvolume of liquid Ni-Mo binary alloys increases with the increase of temperature and molybdenum concentration. Thepartial molar volume of molybdenum in Ni-Mo binary alloy has been approximately calculated as [13.18-2.65×10^(-3)T+(-47.94+3.10×10^(-2)T)×10^(-2)X_(Mo)]×10^(-6)m^3·mol^(-1). The molar volume of Ni-Mo alloy determined inthe present work shows a negative deviation from the ideal linear mixing molar volume.
文摘The density of liquid Ni-Ta alloys was measured by using a modified sessile drop method. It is found that the density of the liquid Ni-Ta alloys decreases with the increasing temperature, but increases with the increase of tantalum concentration in the alloys. The molar volume of liquid Ni-Ta binary alloys increases with the increase of temperature and tantalum concentration.
文摘The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume of liquidNi-Cr alloy increases with increasing the Cr concentration in the alloy. The molar volume of Ni-Cr alloy determinedin the present work shows a positive deviation from the linear molar volume.
文摘The density of three kinds of liquid steel was measured by a modified sessile drop method over the temperature range of 1803-1 873 K.It is found that the density of liquid steels decreases with increasing temperature and carbon content in steel.Both of the density and its absolute temperature coefficient of studied steels are smaller than the literature values of pure iron.The molar volume of the steels increases with increasing temperature.
文摘The density of Ni-Cr alloy in the mushy state has been measured using the modified sessile drop method. The density of Ni-Cr alloy in the mushy state was found to decrease with increasing temperature and Cr concentration in alloy. The molar volume of Ni-Cr alloy in the mushy state therefore increases with increasing the Cr concentration in alloy. The ratio of the difference of density divided by the temperature difference between liquidus and solidus temperatures decreases with increasing Cr concentration. The density of the alloy increased with the precipitation of a solid phase in alloy during the solidification process. The temperature dependence of the density of alloy in the mushy state was not linear but biquadratic.