A reaction interface between the aluminum and K_2ZrF_6 during molten salt reaction process was frozen by quenching the mold in water, and the interface structure was analyzed to determine the formation process of Al_3...A reaction interface between the aluminum and K_2ZrF_6 during molten salt reaction process was frozen by quenching the mold in water, and the interface structure was analyzed to determine the formation process of Al_3Zr. Results show that a clear conical interface existed between the K_2ZrF_6 and aluminum. A zirconium accumulation layer with the thickness of about 2–3 lm was formed at the aluminum side of the interface. Many initially formed Al_3Zr particles（with the size of 0.4–16 lm） distributed in this layer, most of which located at the interface. The morphology of Al_3Zr particles is closely related with their size. For the size of 0.4–1 lm, the Al_3Zr appeared as globular and ellipsoid shapes. When it grew to the size of 1–2 and 2–16 lm, it exhibited the rule cube shape, and rule cuboids shape, respectively.展开更多
基金Supported by the National Natural Science Foundation of China(Nos.51204053,51374067&51674078)Central University Basic R&D Operating Expenses(Nos.N130409005,N130709001&N130209001)
文摘A reaction interface between the aluminum and K_2ZrF_6 during molten salt reaction process was frozen by quenching the mold in water, and the interface structure was analyzed to determine the formation process of Al_3Zr. Results show that a clear conical interface existed between the K_2ZrF_6 and aluminum. A zirconium accumulation layer with the thickness of about 2–3 lm was formed at the aluminum side of the interface. Many initially formed Al_3Zr particles（with the size of 0.4–16 lm） distributed in this layer, most of which located at the interface. The morphology of Al_3Zr particles is closely related with their size. For the size of 0.4–1 lm, the Al_3Zr appeared as globular and ellipsoid shapes. When it grew to the size of 1–2 and 2–16 lm, it exhibited the rule cube shape, and rule cuboids shape, respectively.