A new kind of method, co sedimentation method, was used to fabricate functional gradient material(FGM) in order to eliminate the interfaces in gradient materials. The deposit bodies obtained from the sedimentation of ...A new kind of method, co sedimentation method, was used to fabricate functional gradient material(FGM) in order to eliminate the interfaces in gradient materials. The deposit bodies obtained from the sedimentation of Ti and Mo particles were densified at 1 673 K under a pressure of 20 MPa in flowing argon for 1 h. Finally, Ti Mo system FGM with continuous change of composition was successfully prepared. The results reveal that the sedimentation method is an effective way to manufacture FGM with continuous change of composition. Moreover, the results also show that the compositional gradient of FGM can be adjusted in a wide range through both particle size distribution and the ratio of powders. [展开更多
文摘A new kind of method, co sedimentation method, was used to fabricate functional gradient material(FGM) in order to eliminate the interfaces in gradient materials. The deposit bodies obtained from the sedimentation of Ti and Mo particles were densified at 1 673 K under a pressure of 20 MPa in flowing argon for 1 h. Finally, Ti Mo system FGM with continuous change of composition was successfully prepared. The results reveal that the sedimentation method is an effective way to manufacture FGM with continuous change of composition. Moreover, the results also show that the compositional gradient of FGM can be adjusted in a wide range through both particle size distribution and the ratio of powders. [