Aiming at the problem of available water conservation in desertification ecological restoration, we prepared the water retention materials with montmorillonite(MMT) modified by Castor Oil Polyoxyethylene Ether(10)...Aiming at the problem of available water conservation in desertification ecological restoration, we prepared the water retention materials with montmorillonite(MMT) modified by Castor Oil Polyoxyethylene Ether(10)(EL-10) emulsifying vegetable waxes. The water retention property was studied in simulated desertification climate, and the materials were analyzed and characterized by UV-Vis, SEM, FTIR and XRD measurements. Moreover, a UV carbon arc lamp was used to test the resistance to aging. The experimental results show that the emulsion has good dispersity. Both the water retention property and the aging resistance performance of the modified clay were excellent. The lamellar structure and chemical composition of MMT had no obvious changes before and after modification. The surfaces of clay particles were coated uniformly with modified MMT, so the loose clay particles were cemented together by vegetable waxes. Meanwhile, the original big hydrophilic pores between the clay particles turned into capillary hydrophobic pores. So the clay particles formed a bonding layer which could inhibit water evaporation. Grass-planting experiment showed that reasonable mass ratio of vegetable waxes and EL-10 was 1:18. The materials not only had great water retention property but also maintained sound air permeability so that the germination rate of grass seed significantly increased from 8% to 52%.展开更多
In order to investigate the influening factors of organic modification procedure and find out connections between organic modification and the properties of bentonite greases, organic montmorillonite(OMMT) thickeners ...In order to investigate the influening factors of organic modification procedure and find out connections between organic modification and the properties of bentonite greases, organic montmorillonite(OMMT) thickeners with different surfactant dosages and constituents were synthesized through intercalation reaction between sodium montmorillonite(NaM MT) and quaternary ammonium surfactants in aqueous solvents. The lubricating greases were prepared with the resulting organoclays, while the penetration and oil separation of lubricating greases were evaluated, respectively. The surface modification process of montmorillonite(MMT) was analyzed and the thickening mechanism of OMMT was discussed in this study. The experimental results showed that, with an increasing amount of surfactant, the basal spacing between the clay platelets was increasing and the structure of modifier molecules layer in the interlayer was changing from lateral bilayer to paraffin-type bilayer. The optimal properties of lubricating greases were achieved, when the structure of surfactant molecules loaded in the interlayer was the paraffin-type monolayer, which meant that the dosage of modifier was equal to 120—140 mmol/(100g). Meanwhile, it was found that the thickening performance, colloid stability, anti-wear and friction-reducing performance of lubricating greases were improved, when the surfactants were mixed with octadecyl trimethyl ammonium chloride(OTAC) and hexadecyl trimethyl ammonium chloride(HTAC). And the optimum mole ratio of two surfactants is was 1:1.展开更多
基金Funded by the National High-tech Research and Development Program of China(863 Program)(No.2001AA322100)the National Natural Science Foundation of China(No.50772131)+1 种基金the Main Project of Ministry of Education of China(No.106086)the Fundamental Research Funds for the Central Universities of China University of Mining and Technology(Beijing)(No.2012YJ05)
文摘Aiming at the problem of available water conservation in desertification ecological restoration, we prepared the water retention materials with montmorillonite(MMT) modified by Castor Oil Polyoxyethylene Ether(10)(EL-10) emulsifying vegetable waxes. The water retention property was studied in simulated desertification climate, and the materials were analyzed and characterized by UV-Vis, SEM, FTIR and XRD measurements. Moreover, a UV carbon arc lamp was used to test the resistance to aging. The experimental results show that the emulsion has good dispersity. Both the water retention property and the aging resistance performance of the modified clay were excellent. The lamellar structure and chemical composition of MMT had no obvious changes before and after modification. The surfaces of clay particles were coated uniformly with modified MMT, so the loose clay particles were cemented together by vegetable waxes. Meanwhile, the original big hydrophilic pores between the clay particles turned into capillary hydrophobic pores. So the clay particles formed a bonding layer which could inhibit water evaporation. Grass-planting experiment showed that reasonable mass ratio of vegetable waxes and EL-10 was 1:18. The materials not only had great water retention property but also maintained sound air permeability so that the germination rate of grass seed significantly increased from 8% to 52%.
基金financially supported by the Chongqing Construction Project of Innovation Teams in Colleges and Universities-Petroleum Products Application Engineering and Technology(Project No.KJTD201342)the Chongqing Project of Innovation Research by Postgraduates(Project No.CYB16130)
文摘In order to investigate the influening factors of organic modification procedure and find out connections between organic modification and the properties of bentonite greases, organic montmorillonite(OMMT) thickeners with different surfactant dosages and constituents were synthesized through intercalation reaction between sodium montmorillonite(NaM MT) and quaternary ammonium surfactants in aqueous solvents. The lubricating greases were prepared with the resulting organoclays, while the penetration and oil separation of lubricating greases were evaluated, respectively. The surface modification process of montmorillonite(MMT) was analyzed and the thickening mechanism of OMMT was discussed in this study. The experimental results showed that, with an increasing amount of surfactant, the basal spacing between the clay platelets was increasing and the structure of modifier molecules layer in the interlayer was changing from lateral bilayer to paraffin-type bilayer. The optimal properties of lubricating greases were achieved, when the structure of surfactant molecules loaded in the interlayer was the paraffin-type monolayer, which meant that the dosage of modifier was equal to 120—140 mmol/(100g). Meanwhile, it was found that the thickening performance, colloid stability, anti-wear and friction-reducing performance of lubricating greases were improved, when the surfactants were mixed with octadecyl trimethyl ammonium chloride(OTAC) and hexadecyl trimethyl ammonium chloride(HTAC). And the optimum mole ratio of two surfactants is was 1:1.