Numerical simulation and experimental validation on fabrication of nickel-based superalloy Kagome lattice sandwich structures

Nickel-based superalloy lattice sandwich structures present higher stiffness,higher strength and higher temperature resistance in comparison with other metals.In this study,the Kagome unit was adopted to design the lattice sandwich structure and ProCAST software was used to simulate the filling and solidification processes of the nickel-based superalloy.Grain morphology and sizes of the nickel-based superalloy lattice sandwich structures were simulated by using of cellular automaton coupled with finite element model(CAFE),and indirect additive manufacture combining with investment casting were carried out to fabricate the nickel-based superalloy lattice sandwich structures.The calculated grain morphology and sizes are in good agreement with the experimental results.The grains are mainly equiaxed with an average size of about 500µm.The simulated results also show that the superheat of melting and the mold preheated temperature have significant influence on the grain size of the Kagome lattice sandwich structures,lower superheat of melting and mold preheated temperatures are encouraged to obtain the fine grains while assuring the integrity of the Kagome lattice sandwich structures for industrial application.

The Preparation of Ultra-fine Calcium Carbonate and Its properties Study

This article adopts the double decomposition method, select the appropriate experimental conditions and operation process, respectively add appropriate amount of sodium carboxymethyl cellulose （CMC） as crystal control agent to study the influence of crystalline of ultrafine calcium carbonate. The experimental results show that the different concentrations of CMC as crystal control agent on the morphology and crystal structure of calcium carbonate have obvious effect, which emerge morphology change from square to spherical, crystalline transition from calcite to aragonite. Thus, the results provide experimental data and theoretical basis for the use of different additives, and provide experimental basis and feasible solution for this kind of reaction.

Monodisperse silver microspheres: A facile BSA template method

The spherical silver mirco/nano-particles with narrow size distributions were obtained by chemical reduction of silver ammonia solution with ascorbic acid as reducing agent and bovine serum albumin (BSA) as bio-template. The effects of the concentration of Ag+ ions, BSA and ammonia, reactive temperature on the silver morphology and particle sizes were investigated. SEM, TEM and XRD were employed to characterize the morphology and structures of the prepared silver mirco/nano-particles. The results show that the spherical silver particle with smooth surface and narrow size distributions can be obtained by controlling the concentration of Ag+ ions, BSA, reaction temperature, etc. By controlling the above parameters, the silver spherical mirco/nano-particles with particle sizes ranging from 0.2 to 2.3 m can be well prepared, which is expected to be used in manufacturing high performance electronic pastes.